Dentin sealing and antibacterial effects of silver-doped bioactive glass/mesoporous silica nanocomposite: an in vitro study
- 188 Downloads
To synthesize a silver-doped bioactive glass/mesoporous silica nanoparticle (Ag-BGN@MSN), as well as to investigate its effects on dentinal tubule occlusion, microtensile bond strength (MTBS), and antibacterial activity.
Materials and methods
Ag-BGN@MSN was synthesized using a modified “quick alkali-mediated sol-gel” method. Demineralized tooth disc models were made and divided into four groups; the following treatments were then applied: group 1—no treatment, group 2—bioglass, group 3—MSN, group 4—Ag-BGN@MSN. Next, four discs were selected from each group and soaked into 6 wt% citric acid to test acid-resistant stability. Dentinal tubule occlusion, as well as the occlusion ratio, was observed using field-emission scanning electron microscopy. The MTBS was also measured to evaluate the desensitizing effect of the treatments. Cytotoxicity was examined using the MTT assay. Antibacterial activity was detected against Lactobacillus casei, and ion dissolution was evaluated using inductively coupled plasma optical emission spectrometry.
Ag-BGN@MSN effectively occluded the dentinal tubule and formed a membrane-like layer. After the acid challenge, Ag-BGN@MSN had the highest rate of dentinal tubule occlusion. There were no significant differences in MTBS among the four groups (P > 0.05). All concentrations of Ag-BGN@MSN used had a relative cell viability above 72%.
Ag-BGN@MSN was successfully fabricated using a modified sol-gel method. The Ag-BGN@MSN biocomposite effectively occluded dentinal with acid-resistant stability, did not decrease bond strength in self-etch adhesive system, had low cytotoxicity, and antibacterial effect.
Dentinal tubule sealing induced by Ag-BGN@MSN biocomposite with antibacterial effect is likely to increase long-term stability in DH.
KeywordsBioactive glass Mesoporous silica Nanoparticle Antibacterial effect Remineralization Dentin hypersensitivity
This study was supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIP) (NRF-2015R1C1A1A01051832).
Compliance with ethical standards
Conflict of interest
YI Kim has received research grants from the National Research Foundation of Korea (NRF) for this study. All authors declare that they have no competing interest.
The study was approved by the Ethics Committee of Pusan National University Dental Hospital (PNUDH-2016-033).
Informed consent was obtained from all individual participants included in the study.
- 2.Holland GR, Narhi MN, Addy M, Gangarosa L, Orchardson R (1997) Guidelines for the design and conduct of clinical trials on dentine hypersensitivity. J Clin Periodontol 24:808–813. https://doi.org/10.1111/j.1600-051X.1997.tb01194.x CrossRefPubMedGoogle Scholar
- 9.Absi EG, Addy M, Adams D (1987) Dentine hypersensitivity: a study of the patency of dentinal tubules in sensitive and non-sensitive cervical dentine. J Clin Periodontol 14:280–284. https://doi.org/10.1111/j.1600-051X.1987.tb01533.x CrossRefPubMedGoogle Scholar
- 14.Reis C, De-Deus G, Leal F, Azevedo E, Coutinho-Filho T, Paciornik S (2008) Strong effect on dentin after the use of high concentrations of citric acid: an assessment with co-site optical microscopy and ESEM. Dent Mater 24:1608–1615. https://doi.org/10.1016/j.dental.2008.03.027 CrossRefPubMedGoogle Scholar
- 20.Prabhakar AR, Paul MJ, Basappa N (2010) Comparative evaluation of the remineralizing effects and surface micro hardness of glass ionomer cements containing bioactive glass (S53P4): an in vitro study. Int J Clin Pediatr Dent 3:69–77. https://doi.org/10.5005/jp-journals-10005-1057 CrossRefPubMedPubMedCentralGoogle Scholar
- 24.Hoppe A, Güldal NS, Boccaccini AR (2011) A review of the biological response to ionic dissolution products from bioactive glasses and glass-ceramics. Biomaterials 32:2757–2774. https://doi.org/10.1016/j.biomaterials.2011.01.004 CrossRefPubMedGoogle Scholar
- 30.Horcajada P, Rámila A, Boulahya K, González-Calbet J, Vallet-Regí M (2004) Bioactivity in ordered mesoporous materials. Solid State Sci 6:1295–1300. https://doi.org/10.1016/j.solidstatesciences.2004.07.026 CrossRefGoogle Scholar
- 35.Izquierdo-Barba I, Ruiz-González L, Doadrio JC, González-Calbet JM, Vallet-Regí M (2005) Tissue regeneration: a new property of mesoporous materials. Solid State Sci 7:983–989. https://doi.org/10.1016/j.solidstatesciences.2005.04.003 CrossRefGoogle Scholar
- 37.Vallet-Regí M, Izquierdo-Barba I, Rámila A, Pérez-Pariente J, Babonneau F, González-Calbet JM (2005) Phosphorous-doped MCM-41 as bioactive material. Solid State Sci 7:233–237. https://doi.org/10.1016/j.solidstatesciences.2004.10.038 CrossRefGoogle Scholar
- 41.Yang H, Pei D, Liu S, Wang Y, Zhou L, Deng D (2013) Effect of a functional desensitizing paste containing 8% arginine and calcium carbonate on the microtensile bond strength of etch-and-rinse adhesives to human dentin. Am J Dent 26:137–142. https://doi.org/10.1186/s40563-014-0024-y PubMedGoogle Scholar