SERS based monitoring of toluene vapors at ambient and elevated temperatures by using a ruffled silver nanolayer as a substrate

Abstract

The authors describe a Surface enhanced Raman spectroscopy (SERS)-based method for the detection of gaseous toluene at different temperature regimes using 3D ruffled silver SERS substrates and a commercially available handheld Raman system equipped with a 785 nm laser. The 3D silver SERS substrates were synthesized via electroless deposition of silver on the ruffled sandpaper and HF-etched silicon wafers. The morphological characterization of the silver SERS substrates was carried out by atomic force microscopy and scanning electron microscopy. UV-Vis spectroscopy absorption spectra of the silver nanostructures showed plasmonic peaks at 522 nm and 731 nm. Toluene vapors were collected with a syringe at ambient temperature and at 100 °C, while SERS detection was always performed at room temperature. Toluene detection was based on the measurement of the Raman bands at 787 cm⁻¹ and 1003 cm⁻¹ (in the fingerprint region). The method allow gaseous toluene to be detected at its vapor concentrations of 522 ppm (mg/L), 261 ppm (mg/L) and 26 ppm (mg/L).