1 Introduction

Refractories are substances that can be used as a thermal insulation for high temperatures and it can withstand high temperatures without breaking or deformation. It also preserves several of their properties under various operating conditions. Refractory ceramics have special characteristics such as high resistance to thermal shock, high resistance to melting, with low thermal conductivity and a low thermal expansion. Furnace linings wall was considered one of the most important applications of refractory materials [1].

Refractories are generally classified into two types brick and monolithic refractories. Mortars are available in compositions that either approximate the bricks they are holding together, or they are chosen so that their thermal expansion will be comparable to the bricks [2].

In many researches, it has been discussed in the field of refractory mortar and its properties, in 2004, Christianto, and Heru Ari prepared self-compacting mortar using different mineral admixtures. Limestone powder, fly ash, kaolinite, and brick powder were used as mineral admixtures. Workability of fresh mortar studied by preparing 43 different mixes of SCM. Results showed that workability increased only with fly ash and limestone powder [3]. In 2006, Al-Amaireh studied the improvement of physical and thermal properties of fire clays produced from bauxite and found that the improvement of this type of refractories had a high strength and hardness. This product can be used in the cement industry [4]. In 2012, Andreev et al studied the compressive behavior of dry joins closure of two types of refractory bricks in a large temperature range. Measurements showed that the stiffness of the material influenced on the stress that needed to close the joints also temperature influenced on the closure of the joints by stiffness changing [5]. In 2015, Mahdi prepared a refractory mortar from fire-clay brick scraps by adding Iraqi kaolin with different percentage contents (21, 27, 32, 40, and 47%). Disks specimens were used for bulk density, thermal conductivity, specific heat capacity, and bond strength tests. The results showed that the specimens with 40% kaolin had the best properties [6]. In 2016, Torres and Matias used ceramic residues to form a lime mortar which can be used as a plaster. Mechanical and physical properties for different mortar were studied. Results showed that the ceramic residues mortar had good mechanical properties which made it suitable for plaster repairing [7]. The study aims to prepare a refractory mortar from Iraqi locally clays which can be used for construction and plastering the lining furnace walls at temperature up to 1200 °C.

2 Experimental work

For preparing the specimens, the kaolin and bauxite rocks were sintered at 1200 °C and metakaolin was obtained by firing kaolin up to 700 °C then crushed to a fine powder and finally sieved to different particle sizes (0.2 and 1.18 mm). Bauxite and metakaolin were used as additives in (10, 20, 30, and 40 wt%) of kaolin weight. First, a dry mixing to the kaolin and the additives were done, and then, water (6 ml) and potassium silicate (4 ml) were added as a binding material for the total mix. The specimens were prepared by hand molding method. They pressed in a cylindrical mold with diameter of (10 mm) and left in the air for 24 h then fired at 1200 °C for 1 h. The specimens were prepared according to standard ASTM F1097–91 [8]. The chemical analysis for kaolin, bauxite, and metakaolin rocks used in this research is shown in Table 1 also the block diagram of the experimental work is shown in Fig. 1.

Table 1 Chemical analysis for raw materials
Fig. 1
figure 1

Schematic representation of the experimental work

The X-ray diffraction test for kaolin rocks shows that they consist basically of kaolinite and quartz; it is illustrated in Fig. 2. For bauxite rocks, it shows that bauxite rocks consist of kaolinite and boehmite, as illustrated in Fig. 3. While for metakaolin shows that it consists of kaolinite and quartz, as illustrated in Fig. 4.

Fig. 2
figure 2

X-ray diffraction for kaolin

Fig. 3
figure 3

X-ray diffraction for bauxite

Fig. 4
figure 4

X-ray diffraction for metakaolin

3 Test procedure

3.1 Apparent porosity and bulk density

Apparent porosity and bulk density were measured by immersion of specimens in water for a few seconds using Archimedes method. The mass of specimens was measured in the air when suspended in water and when dried. Cylindrical specimens of (20 × 10 mm) were used according to ASTM C 20 [9] using the following equations:

$${\text{Apparent porosity}}\;=\;\left[ {\left( {W - D} \right)/\left( {W - S} \right)} \right]\; \times \;{\text{1}}00,$$
(1)
$${\text{Bulk density}}\;=\;D/W - S,$$
(2)

where D is the dry weight (g), and W is the saturated weight (g) and S weight (g) of dry specimen in the air.

3.2 Thermal conductivity, volumetric heat capacity, and thermal diffusivity

In this study, three thermal properties: thermal conductivity, thermal diffusivity, and volumetric heat capacity, which were determined using a transient plane heat source method. The commercial thermal constants analyzer TPS 500 (Hot Disk) was used to determine the thermal properties for cylindrical specimens. The analysis was based on embedding a hot disk probe within a sample, as shown in Fig. 5. The hot disk probe was used as both a heating plate (source) and a dynamic temperature sensor.

Fig. 5
figure 5

Hot disk transient plane heat source probe and sample assembly

An electrical current in the form of a step function was applied to the heating plate to generate a heat pulse for a duration of 20 s. Thermal conductivity (λ) and thermal diffusivity (α) values were determined by fitting the increasing temperature curve using least-squares analysis. Consequently, the volumetric heat capacity can be obtained by dividing thermal conductivity by thermal diffusivity (using Eq. 3):

$$\alpha \;=\;\lambda /C,$$
(3)

where C is the volumetric heat capacity. The test was done according to ISO 22007-2 [10].

4 Results and discussion

4.1 Apparent porosity and bulk density

Increase in bulk density leads to a decrease in porosity. The density depends more on raw materials which are used, and also on firing temperature and soaking time. Results showed that there was a decrease in porosity and an increase in density for bauxite additives as shown in Figs. 6 and 8. This is because the mullite phase possesses high density than kaolin, while the porosity increased and density decreased with the addition of metakaolin additives, because the change in phases during firing leads to formation of vacancies in the structure, as shown in Figs. 7 and 9, respectively.

Fig. 6
figure 6

Apparent porosity of refractory specimens change with different bauxite additions

Fig. 7
figure 7

Apparent porosity of refractory specimens change with different metakaolin additions

Fig. 8
figure 8

Bulk density of refractory specimens change with different bauxite additions

Fig. 9
figure 9

Bulk density of refractory specimens with different metakaolin additions

In general, porosity was high and density was low when compared to dense refractories due to the loss on ignition and evaporation of formation water, as well as increasing the space between the particles of powder as a result of hand molding. All this leads to a weak stacking between grains after firing.

4.2 Thermal conductivity

Thermal conductivity was increased with bauxite additives increases, because the porosity decreases due to glass phase increasing from fluxing oxides, which melt at temperatures below 1200 °C. As well as the main effect of porosity is to reduce thermal conductivity, because porosity acts as a barrier to the flow of heat within the ceramic product while decreasing occurred with increasing metakaolin additives, this decreasing resulted from the high porosity that found with metakaolin additives. The results are shown in Fig. 10. The relation between thermal conductivity and porosity is shown in Figs. 11 and 12. The thermal conductivity was decreased with porosity increases from 0.5 to 0.4 W/m K for bauxite additions and to 0.36 W/m K for metakaolin additions. The effect of porosity is important; when the thermal conductivity of the air is negligible compared to the solid phases, the addition of large volume fractions of pores can dramatically reduce thermal conductivity. This approach is used in the fabrication of insulation refractories. Briefly, the large amount of porosity leads to improved thermal shock resistance of refractory insulating bricks [11].

Fig. 10
figure 10

Thermal conductivity of refractory specimens with different bauxite and metakaolin additions

Fig. 11
figure 11

Relation between thermal conductivity and porosity of refractory specimens with different bauxite additions

Fig. 12
figure 12

Relation between thermal conductivity and porosity of refractory specimens with different metakaolin additions

4.3 Volumetric heat capacity

The more measurable volumetric heat capacity the more the amount of heat that required to change the temperature of one unit volume of a material by 1 °C. The increment in volumetric heat capacity with increasing the addition of bauxite and decrement with increasing metakaolin additives is shown in Fig. 13.

Fig. 13
figure 13

Volumetric heat capacity of refractory specimens with different bauxite and metakaolin additions

The volumetric heat capacity and thermal conductivity of the specimens are strongly dependent on the ratio of density and porosity. However, addition of bauxite leads to decrease the porosity, as shown in Fig. 6, therefore, that leads to increase in the volumetric heat capacity, while in the case of adding metakaolin, it decreases it. During the firing process, the amount of porosity decreases, whereas at the same time, there is a glass phase formation which fills the pores; this implies an increment in volumetric heat capacity. Figures 14 and 15 show the relation between volumetric heat capacity and porosity.

Fig. 14
figure 14

Relation between volumetric heat capacity and porosity of refractory specimens with different bauxite additions

Fig. 15
figure 15

Relation between volumetric heat capacity and porosity of refractory specimens with different metakaolin additions

We can neglect thermal radiation at ordinary temperatures. Then, the heat capacity per unit volume is reduced by the existence of pores, because the heat capacity of pores per unit volume is negligibly small compared with that of the solid phase in a material [12].

4.4 Thermal diffusivity

The change in thermal diffusivity with increasing the addition of bauxite and metakaolin is shown in Fig. 16. The results showed that the thermal diffusivity values decrease with addition bauxite, because it is affected by the high density which resulted with adding this material, because the diffusivity depends on the movement of molecules; therefore, the thermal diffusivity increases after adding metakaolin, because it forms a high porosity product. Figures 17 and 18 show the relation between thermal diffusivity and porosity. The coefficient of thermal diffusivity increases with an increase in the amount of additives. The thermal diffusivity of specimen without any additive was 0.07 m2/s, which decreased by 57% for 40 wt.% bauxite additives and increased with porosity ranged from 17 to 18%. As well as, the thermal diffusivity of specimen was increased by 67% for 40 wt.% metakaolin additives and increased with porosity ranged from 18 to 25.4%.

Fig. 16
figure 16

Thermal diffusivity of refractory specimens with different bauxite and metakaolin additions

Fig. 17
figure 17

Relation between thermal diffusivity and porosity of refractory specimens with different bauxite additions

Fig. 18
figure 18

Relation between thermal diffusivity and porosity of refractory specimens with different metakaolin additions

The low thermal diffusivity values are required for minimizing heat conduction. The physical significance of low thermal diffusivity is associated with the low rate of change of temperature through the material during the heating process. The observed low values of the coefficient of thermal diffusivity in the present study demonstrated that the investigated samples are suitable for use as thermal insulators [13].

5 Conclusion

Depending on the experimental procedure and the carried out tests on different types of the prepared mortars, it concluded that the addition of bauxite and flint led to an increasing in density and decreasing in porosity ratio. The decrease in porosity of refractory products leads to increased thermal properties such as thermal conductivity and volumetric heat capacity by the addition of bauxite and flint, but the addition of metakaolin led to decrease them. Thermal diffusivity increased with increasing metakaolin additives, while it decreased with bauxite and flint additives. The addition of potassium silicate as a bonding material has improved physical properties due to the role of the potassium element in forming a perfect glass phase during the sintering process.