Comparative study on successive and simultaneous double-sided laser beam welding of AA6056/AA6156 aluminum alloy T-joints for aircraft fuselage panels

  • Zhibin Yang
  • Xin Zhao
  • Wang Tao
  • Cheng Jin
  • Shiming Huang
  • Yuxi Wang
  • En Zhang
ORIGINAL ARTICLE
  • 4 Downloads

Abstract

Double-sided laser beam welding—successive and simultaneous—is a promising method for joining the skin-stringer T-joints in the aircraft industry, because higher production efficiency and lower airframe weight can be achieved. In this work, a comparative study on the microstructure, mechanical properties, and porosity defects of the successive and simultaneous double-sided laser beam-welded AA6056-AA6156 aluminum alloy T-joints was conducted. The results indicate that there are no significant differences in the microstructure near the fusion line in the two cases, but the microstructure characteristics are markedly different at the centre of the fusion zone. The micro-hardness of the simultaneous weld fusion zone is lower than that of the successive weld unaffected fusion zone but higher than that of the successive weld reheat region. Lower head tensile strength and higher hoop tensile strength are obtained for the successively welded specimens. For the two T-joints, the failure propagates along the fusion layer upon tensile loading, but their final fracture positions are distinctly different. The radiographs of the optimized successively and simultaneously welded T-joints show that many porosity defects exist in the successively welded T-joints, whereas there are very few and even no porosity defects exist in the simultaneously welded T-joints.

Keywords

Double-sided laser beam welding Aluminum alloy T-joint Microstructure Mechanical properties Porosity defects 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgements

This research was supported by the State Key Lab of Advanced Welding and Joining, Harbin Institute of Technology (AWJ-M16-05), the Guidance Plan Project of Doctoral Scientific Research Foundation of Liaoning Province (201601253), the Project funded by China Postdoctoral Science Foundation (2017M611213), the Scientific Research Project of Liaoning Provincial Education Department (JDL2016009), and the National Key R&D Program (2016YFF0203000).

References

  1. 1.
    Sun X, Shehab E, Mehnen J (2013) Knowledge modelling for laser beam welding in the aircraft industry. Int J Adv Manuf Technol 66:763–774CrossRefGoogle Scholar
  2. 2.
    Pacchione M, Telgkamp J (2006) Challenges of the metallic fuselage. In: Pro ICAS, Hamburg, GermanyGoogle Scholar
  3. 3.
    Schubert E, Klassen M, Zerner I, Walz C, Sepold G (2001) Light-weight structures produced by laser beam joining for future applications in automobile and aerospace industry. J Mater Process Technol 115:2–8CrossRefGoogle Scholar
  4. 4.
    Huang Y, Li G, Shao WJ, Gong SH, Zhang XL (2017) A novel dual-channel weld seam tracking system for aircraft T-joint welds. Int J Adv Manuf Technol 91:751–761CrossRefGoogle Scholar
  5. 5.
    Enz J, Riekehr S, Ventzke V, Kashaev N, Huber N (2012) Process optimisation for the laser beam welding of high-strength aluminium-lithium alloys. Schweißen Schneiden 64:482–485Google Scholar
  6. 6.
    Siqueira RHM, Capella A, Riva R, Abdalla AJ, Lima SFM (2016) Comparing mechanical behavior of aluminum welds produced by laser beam welding (LBW), friction stir welding (FSW) and riveting for aeronautic structures. Weld Int 19:1–7Google Scholar
  7. 7.
    Janasekaran S, Jamaludin MF, Muhamad MR, Yusof F, Shukor MHA (2017) Autogenous double-sided T-joint welding on aluminum alloys using low power fiber laser. Int J Adv Manuf Technol 90:3497–3505CrossRefGoogle Scholar
  8. 8.
    Brenner B, Stabdfuβ J, Dittrich D, Winderlich B, Liebscher J, Hackius J (2008) Laser beam welding of aircraft fuselage structures. In: Proc ICALEO, Temecula, USA, pp 838–845Google Scholar
  9. 9.
    Yang ZB, Tao W, Zhao X, Chen YB, Shi CY (2017) Numerical modelling and experimental verification of thermal characteristics and their correlations with mechanical properties of double-sided laser welded T-joint. Int J Adv Manuf Technol 92:1609–1618CrossRefGoogle Scholar
  10. 10.
    Brenner B, Standfuß J, Morgenthal L, Dittrich D, Fux V, Winderlich B, Brenneis H, Zink W, Hachius J, Held J, Schwabe C (2004) Neue technoloqische aspekte des laserstrahlschweißens von flugzeugstrukturen. Düsseldorf: DVS 229:19–24 [In German] Google Scholar
  11. 11.
    Yang ZB, Tao W, Li LQ, Chen YB, Li FZ, Zhang YL (2012) Double-sided laser beam welded T-joints for aluminium aircraft fuselage panels: process, microstructure, and mechanical properties. Mater Des 33:652–658CrossRefGoogle Scholar
  12. 12.
    Enz J, Khomenko V, Riekehr S, Ventzke V, Huber N, Kashaev N (2015) Single-sided laser beam welding of a dissimilar AA2024-AA7050 T-joint. Mater Des 76:110–116CrossRefGoogle Scholar
  13. 13.
    Oliveira AC, Siqueira RHM, Riva R, Lima MSF (2015) One-sided laser beam welding of autogenous T-joints for 6013-T4 aliminium alloy. Mater Des 65:726–736CrossRefGoogle Scholar
  14. 14.
    Schumacher J, Zerner I, Neye G, Thormann K (2002) Laser beam welding of aircraft fuselage panels. In: Proc ICALEO Section A, Scottsdale, USAGoogle Scholar
  15. 15.
    Squillace A, Prisco U (2013) Influence of filler material on micro- and macro- mechanical behaviour of laser-beam-welded T-joint for aerospace applications. Mat Res 16:1106–1112CrossRefGoogle Scholar
  16. 16.
    Braun R (2006) Nd: YAG laser butt welding of AA6013 using silicon and magnesium containing filler powders. Mater Sci Eng A 426:250–262CrossRefGoogle Scholar
  17. 17.
    Ventzke V, Riekehr S, Horstmann M, Haack P, Kashaev N (2014) One-sided Nd:YAG laser beam welding for the manufacture of T-joints made of aluminium alloys for aircraft construction. Weld Cutt 13:245–249Google Scholar
  18. 18.
    Dittrich D, Standfuss J, Liebscher J, Brenner B, Beyer E (2011) Laser beam welding of hard to weld Al alloys for a regional aircraft fuselage design—first results. Phys Proc 12:113–122CrossRefGoogle Scholar
  19. 19.
    Machold W, Staron P, Bayraktar F, Riekehr S, Koçak M, Schreyer A (2008) Influence of the welding sequence on residual stresses in laser welded T-joints of an airframe aluminium alloy. Mater Sci Forum 571:375–380CrossRefGoogle Scholar
  20. 20.
    Chang KH, Lee CH (2009) Finite element analysis of the residual stresses in T-joint fillet welds made of similar and dissimilar steels. Int J Adv Manuf Technol 41:250–258CrossRefGoogle Scholar
  21. 21.
    Chen J, Yang ZB, Zhan XH, Wang YH, Chen YB (2011) Experimental properties study on both-side laser beam welding of T-joint aluminum alloy. Appl Laser 31:130–134 [In Chinese] CrossRefGoogle Scholar
  22. 22.
    Wu NQ, Xia C, Li M, Perrusquia N, Mao SX (2004) Interfacial structure and micro and nano-mechanical behaviour of laser-welded 6061 aluminium alloy blank. Trans ASME J Eng Mater Technol 126:8–13CrossRefGoogle Scholar
  23. 23.
    Huang C, Kou S (2001) Partially melted zone in aluminium welds: solute segregation and mechanical behaviour. Weld Res Suppl 80:9–17Google Scholar
  24. 24.
    Prasad RK, Ramanaiah N, Viswanathan N (2008) Partially melted zone cracking in AA6061 welds. Mater Des 29:179–186CrossRefGoogle Scholar
  25. 25.
    Yu YC, Wang CY, Hu XY, Wang J, Yu SF (2010) Porosity in fibre laser formation of 5A06 aluminium alloy. J Mech Sci Technol 24:1077–1082CrossRefGoogle Scholar
  26. 26.
    Miao HB, Yu G, He XL, Li SX, Chen XY (2017) Comparative study of hybrid laser-MIG leading configuration on porosity in aluminum alloy bead-on-plate welding. Int J Adv Manuf Technol 91:2681–2688CrossRefGoogle Scholar
  27. 27.
    Wei M, Li ZG, Lu FG, Wu YX, Chen JH, Katayama S (2014) Porosity formation mechanism and its prevention in laser lap welding for T-joints. J Mater Process Technol 214:1658–1664CrossRefGoogle Scholar
  28. 28.
    Zhang C, Gao M, Wang D, Yin J, Zeng X (2017) Relationship between pool characteristic and weld porosity in laser arc hybrid welding of AA6082 aluminum alloy. J Mater Process Technol 240:217–222CrossRefGoogle Scholar
  29. 29.
    Bai Y, Gao HM, Wu L, Ma ZH, Cao N (2010) Influence of plasma-MIG welding parameters on aluminium weld porosity by orthogonal test. Trans Nonferrous Met Soc China 20:1392–1396CrossRefGoogle Scholar

Copyright information

© Springer-Verlag London Ltd., part of Springer Nature 2018

Authors and Affiliations

  • Zhibin Yang
    • 1
  • Xin Zhao
    • 2
  • Wang Tao
    • 3
  • Cheng Jin
    • 1
  • Shiming Huang
    • 1
  • Yuxi Wang
    • 1
  • En Zhang
    • 1
  1. 1.School of Materials Science and EngineeringDalian Jiaotong UniversityDalianChina
  2. 2.School of Mechanical EngineeringDalian Institute of Science and TechnologyDalianChina
  3. 3.State Key Laboratory of Advanced Welding and JoiningHarbin Institute of TechnologyHarbinChina

Personalised recommendations