European Journal of Wood and Wood Products

, Volume 69, Issue 2, pp 317–323 | Cite as

Potential of shortening pressing time or reducing pressing temperature for plywood resinated with PF resin modified using alcohols and esters

  • Radosław Mirski
  • Dorota DziurkaEmail author
  • Janina Łęcka
Originals Originalarbeiten

Abstract

The study was an analysis of the potential to shorten pressing time or reduce pressing temperature for plywood resinated with alcohol- and ester-modified PF resin. Birch and pine plywoods were produced using such modified resin at a temperature range of 135 to 115 °C, at a constant pressing time (4 min) and at pressing times ranging from 240 to 150 s at a constant pressing temperature (135 °C). Tests showed that the application of PF resin modified with polyols and esters makes it possible, under standard pressing conditions, i.e. 135 °C and pressing time of 4 min, to produce plywood with improved properties in comparison to respective control plywoods. Moreover, it was shown that the used modifiers enhance resin reactivity, facilitating an adequate course of resin curing, resulting in the manufacture of plywoods with good properties even at a pressing temperature reduced by 20 °C or pressing time shortened to 150 s.

Keywords

Polyol Bond Quality Pressing Temperature Accelerate Aging Test Accelerate Aging Treatment 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Potential von mit Alkohol und Estern modifiziertem PF-Harz zur Reduzierung der Presszeit oder der Presstemperatur bei der Sperrholzherstellung

Zusammenfassung

In dieser Studie wurde untersucht, wie die Presszeit bzw. die Presstemperatur bei der Herstellung von Sperrholz durch Verwendung eines mit Alkohol- und Ester modifizierten PF-Harzes reduziert werden kann. Unter Verwendung solcher Harze wurde Birken- und Kiefernsperrholz hergestellt, und zwar bei einer Presstemperatur von 135 bis 115 °C und einer konstanten Presszeit von 4 min bzw. bei Presszeiten von 240 bis 150 s und einer konstanten Presstemperatur von 135 °C. Die Versuche zeigten, dass durch Verwendung von PF-Harz, das mit Polyolen und Estern modifiziert wurde, bei Standardbedingungen, d.h. bei 135 °C und einer Presszeit von 4 min, Sperrholz hergestellt werden kann, das im Vergleich zu Kontrollproben verbesserte Eigenschaften aufweist. Des Weiteren wurde gezeigt, dass die Modifizierung die Harzreaktivität verstärkt und somit den Härtungsverlauf verbessert, mit dem Ergebnis, dass auch bei einer um 20 °C reduzierten Presstemperatur oder einer auf 150 s verkürzten Presszeit Sperrholz mit guten Eigenschaften hergestellt werden kann.

References

  1. Andersen AW, Troughton GE (1996) New phenolic formulations for bonding higher moisture content OSB panels. For Prod J 46(10):72–76 Google Scholar
  2. Conner AH, Lorenz LF, Hirth KC (2002) Accelerated cure of phenol-formaldehyde resins: studies with model compounds. J Appl Polym Sci 86:3256–3263 Google Scholar
  3. Higuchi M, Tohmura S, Sakata I (1994) Acceleration of the cure of phenolic resin adhesives V: catalytic action of carbonates and formamide. J Jpn Wood Res Soc 40(6):604–611 Google Scholar
  4. Irle MA, Bolton AJ (1988) Physical aspects of wood adhesive bond formation with formaldehyde based adhesives. Part II: Binder physical properties and particleboard durability. Holzforschung 42(1):150–156 CrossRefGoogle Scholar
  5. Łęcka J, Mirski RA, Morze Z (2001a) Properties of particleboards glued with phenol-formaldehyde resin modified with esters. Part 1: The influence of acid that forms the esters. Ann Wars Agric Univ. For Wood Technol (Special issue I) 2001:118–125 Google Scholar
  6. Łęcka J, Mirski RA, Dziurka D (2001b) The effect of polyalcohols on the properties of particleboards glued with phenolic-formaldehyde resin. Zesz Nauk Politech Śl. Chem 146:177–179 Google Scholar
  7. Lei H, Pizzi A, Despres A, Pasch H, Du G (2006) Ester acceleration mechanisms in phenol-formaldehyde resin adhesives. J Appl Polym Sci 100:3075–3093 Google Scholar
  8. Mirski R, Dziurka D, Łęcka J (2004) Properties of particleboards glued with phenol-formaldehyde resin modified with esters. Part A: The influence of the kind of alcohol that forms the ester. Acta Sci Pol Silv Colendar Rat Ind Lignar 3(2):129–138 Google Scholar
  9. Mirski R, Dziurka D, Łęcka J (2005) Properties of alcohol-modified PF resin used in the production of wood-based materials. EJPAU 8(2):#22 Google Scholar
  10. Mirski R, Dziurka D, Łęcka J (2008a) Properties of phenol-formaldehyde resin modified with organic acid esters. J Appl Polym Sci 107(5):3358–3366 Google Scholar
  11. Mirski R, Dziurka D, Łęcka J (2008b) Properties of particleboards resinated with PF resin modified with diol esters. Acta Sci Pol Silv Colendar Rat Ind Lignar 7(1):115–121 Google Scholar
  12. Mirski R, Dziurka D, Łęcka J (2008c) Properties of plywood resinated with PF resin modified with polyols and esters. Ann WULS-SGGW, For Wood Technol 64:83–88 Google Scholar
  13. Orth H (1957) Verfahren zum Härten von alkalisch kondensierten Kondensationsprodukten aus Phenolen und Aldehyden. DE 1065605 Google Scholar
  14. Orth H (1958) Verfahren zum Haerten von Phenol-Aldehyd-Kondensaten. DE 1171606 Google Scholar
  15. Park BD, Riedl R (2000) 13C-NMR study on cure-accelerated phenol-formaldehyde resins with carbonates. J Appl Polym Sci 77:841–851 Google Scholar
  16. Pizzi A, Garcia R, Wang S (1997) On the networking mechanisms of additives-accelerated phenol-formaldehyde polycondensates. J Appl Polym Sci 66:255–256 Google Scholar
  17. Pizzi A, Stephanou A (1994) Phenol-formaldehyde wood adhesives under very alkaline conditions. Part II: Esters curing acceleration, its mechanism and applied results. Holzforschung 48(2):53–58 CrossRefGoogle Scholar
  18. Stephanou A, Pizzi A (1993) Rapid-curing lignin-based exterior wood adhesives. Part II: Esters acceleration mechanism and application to panel products. Holzforschung 47:501–506 CrossRefGoogle Scholar
  19. Tohmura S, Higuchi M (1995) Acceleration of the cure of phenolic resin adhesives VI: Cure-accelerating action of propylene carbonate. J Jap Wood Res Soc 41(12):1109–1114 Google Scholar
  20. Westwood GW, Higgins R (1985) Preparation of foundry moulds and cores. GB 2158448A Google Scholar

Copyright information

© Springer-Verlag 2010

Authors and Affiliations

  • Radosław Mirski
    • 1
  • Dorota Dziurka
    • 1
    Email author
  • Janina Łęcka
    • 1
  1. 1.Department of Wood-Based MaterialsPoznań University of Life SciencesPoznańPoland

Personalised recommendations