Abstract
The possibility of veneer bonding with recycled polystyrene was examined. Five pressing regimes were studied. It was shown that low-pressure pre-heating is a necessary step allowing for increasing final shear strength of the wood-thermoplastic joints and avoiding indentation of thermoplastic particles to wood.
Similar content being viewed by others
References
Borysiuk P, Pawlicki J, Nicewicz D (2006) New types of raw materials in technologies of wood-based materials. In: Proceedings of COST action E44-49 wood resources and panel properties, Valencia, pp 277–281
EN 205 (2005) Adhesives—Wood adhesives for non-structural applications—Determination of tensile shear strength of lap joints
Hu Y, Nakao T, Gu J, Wang F (2005) Vibrational properties of wood plastic plywood. J Wood Sci 51:13–17
Pawlicki J, Nicewicz D (2002) New kinds of wood-thermoplastics composites. In: Proceedings of workshop: innovative materials on the base of modified wood fiber and polyolefins, Kassel
Pritchard G (2004) Two technologies merge: wood plastic composites. Reinf Plast 6:26–29
Selke S, Wachman I (2004) Wood fiber/polyolefin composites. Composites: Part A 35:321–326
Tangram Technology (2002) Wood-plastic composites a technical review of materials, processes and applications. Tangram technology Ltd. Forest Products Laboratory, Wood-Plastic Composites, Tech line; COM-1 01/04
Youngquist JA, Myers GE, Muehl JH, Krzysik AM, Clemons CM (1994) Composites from recycled wood and plastics. Report prepared for US Environmental Protection Agency, Cincinnati
Acknowledgement
This work was financed by the Polish Department of Education and Science; Project no. N 309 2869 33.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Borysiuk, P., Mamiński, M.Ł., Parzuchowski, P. et al. Application of polystyrene as binder for veneers bonding—the effect of pressing parameters. Eur. J. Wood Prod. 68, 487–489 (2010). https://doi.org/10.1007/s00107-010-0418-x
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00107-010-0418-x