Abstract
The development of eco-friendly chromium-free refractory products has been attracting more and more attention for environmental protection reasons. Refractories from the MgO-Al2O3-SnO2 system were selected as chrome-free alternatives. Novel spinel-based castables with SnO2 have the potential to be used in copper smelting. The effect of SnO2 addition up to 10 mass-% on the properties of spinel-based castables was investigated. Phase composition, microstructure, physical and mechanical properties as well as corrosion resistance of the refractories were characterized. The results showed that spinel-based castables with 10 mass-% SnO2 after firing at 1350 °C presented the best comprehensive performance due to lower porosity and higher strength.
Similar content being viewed by others
References
Bradt, R.C.: Mg-Al spinel: is it the mullite of the 21st century? Refract. Appl. News 9 (2004) [4] 8–10
Jin, L.P., Wang, W.X.: Application results of chrome free bricks based on magnesia-spinel brick in burning zone of cement rotary kilns. Foreign Refract. 19 (2004) [3] 54–55
Yuan, W.J., Zhu, Q.Y., Deng, C.J., Zhu, H.X.: Effects of SnO2 addition on the properties of alumina-magnesia refractory castables. N. J. Glass Ceram. 5 (2015) [1] 1–7
Wojsa, J., Jedynak, L., Podwórny, J., Wala, T.: New types of chrome free basic refractories. Procee. of UNITECR’07 (2007) 568–571
Jedynak, L., Wojsa, J., Podwórny, J., Wala, T.: Refractories from the MgO-Al2O3-SnO2 system for metallurgical applications. Ceram. Mater. 63 (2011) [1] 34–39
Ugur, P., Aksel, C.: The effect of SnO2 on the improvement of mechanical properties of MgO-MgAl2O4 composites. Compos. B43 (2012) 2217–2221
Yuan, W.J., Shang, H., Zhu, Q.Y., Deng, C.J., Zhu, H.X.: The effect of tin oxide on the properties of spinel castables. Refractories 49 (2015) [5] 335–338
Tripathi, H.S., Ghosh, A.: Spinelisation and properties of Al2O3-MgAl2O4-C refractory: Effect of MgO and Al2O3 reactants. Ceram. Int. 36 (2010) 1189–1192
Zou, Y., Huang, A., Gu, H.Z., Zhang, M.J., Lian P.F.: Effect of particle distribution of matrix on microstructure and slag resistance of lightweight Al2O3-MgO castables. Ceram. Int. 42 (2016) [1] 1964–1972
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Shang, H., Yuan, W.J., Zhu, Q.Y. et al. The Influence of SnO2 Addition on the Properties of Spinel-based Castables. Interceram. - Int. Ceram. Rev. 65, 71–74 (2016). https://doi.org/10.1007/BF03401192
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF03401192