Shape forming high-Tc superconductors

  • R. B. Poeppel
  • S. E. Dorris
  • C. A. Youngdahl
  • J. P. Singh
  • M. T. Lanagan
  • U. Balachandran
  • J. T. Dusek
  • K. C. Goretta
Superconductivity Materials Processing Technology

Abstract

Before the potential of high-temperature superconductors can evolve from the realm of science fantasy to the marketplace of practical reality, materials scientists and engineers must first develop viable methods for fabricating these revolutionary materials into a wide assortment of functional shapes and sizes.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    K.H. Miska, J. Met., 40 (1988), p. 14.Google Scholar
  2. 2.
    P. Chaudhari, R.H. Koch, R.B. Laibowitz, T.R. McGuire and R.J. Gambino, Phys. Rev. Lett., 58 (1987), p. 2684.Google Scholar
  3. 3.
    P.H. Carr, Microwave J., 31 (1987), p. 91.Google Scholar
  4. 4.
    J.R. Delayen, K.C. Goretta, R.B. Poeppel and K.W. Shepard, Appl. Phys. Lett., 52 (1988), p. 930.Google Scholar
  5. 5.
    K.C. Goretta, I. Bloom, N. Chen, G.T. Goudey, M.C. Hash, G. Klassen, M.T. Lanagan, R.B. Poeppel, J.P. Singh, D. Shi, U. Balachandran, J.T. Dusek and D.W. Capone II, Mater. Lett., vol. 7 (1988), p. 161.Google Scholar
  6. 6.
    G. Kordas, K. Wu, U.S. Brahme, T.A. Friedmann and D.M. Ginsberg, Mater. Lett., 5 (1987), p. 417.Google Scholar
  7. 7.
    S.E. Trolier, S.D. Atkinson, P.A. Fuierer, J.H. Adair and R.E. Newnham, Am. Ceram. Soc. Bull., 67 (1988), p. 759.Google Scholar
  8. 8.
    J.P. Singh, D. Shi and D.W. Capone II, Appl. Phys. Lett., 53 (1988), p. 237.Google Scholar
  9. 9.
    K.C. Goretta, D.W. Capone II, T.L. Tolt, R.B. Poeppel, J.P. Singh, A.J. Schultz, D. Shi, J.T. Dusek, D.S. Applegate and J.S. Kallend, Ceramic Superconductors II, ed. M.F. Yan (Am. Ceram. Soc., Westerville, OH, 1988), p. 323.Google Scholar
  10. 10.
    K.N. Tu, C.C. Tsuei, S.I. Park and A. Levi, Phys. Rev., B38 (1988), p. 772.Google Scholar
  11. 11.
    M.A. Subramanian, C.C. Torardi, J.C. Calabrese, J. Gopalakrishnan, K.J. Morrissey, T.R. Askew, R.B. Flippen, U. Chowdhry and A.W. Sleight, Science, 239 (1988), p. 1015.Google Scholar
  12. 12.
    T. Goto and M. Tsujihara, J. Mater. Sci. Lett., 7 (1988), p. 283.Google Scholar
  13. 13.
    T. Umeda, H. Kozuka and S. Sakka, Adv. Ceram. Mater., 3 (1988), p. 520.Google Scholar
  14. 14.
    A.K. Dhingra, Trans. R. Soc. Lond., A294 (1980), p. 411.Google Scholar
  15. 15.
    K. Okamura, Composites, 18 (1987), p. 107.Google Scholar
  16. 16.
    D.J. Pysher, K.C. Goretta, R.S. Hodder, Jr. and R.E. Tressler, J. ACerS., in press.Google Scholar
  17. 17.
    R.W. McCallum, J.D. Verhoeven, M.A. Noack, E.D. Gibson, F.C. Laabs, D.K. Finnemore and A.R. Moodenbaugh, Adv. Ceram. Mater., 3 (1987), p. 388.Google Scholar
  18. 18.
    N. Sadakata, Y. Ikeno, M. Nakagawa, K. Gotoh and O. Kohno, Mater. Res. Soc. Symp. Proc., 99 (1988), p. 293.Google Scholar
  19. 19.
    M. Okada, A. Okayama, T. Morimoto, T. Matsumoto, K. Aihara and S. Matsuda, Jpn. J. Appl. Phys., 27 (1988), p. L185.Google Scholar
  20. 20.
    T. Kodas, see report in High-T c Update, 2 (1988), no. 19.Google Scholar
  21. 21.
    R.S. Feigelson, D. Gazit, D.K. Fork and T.H. Geballe, Science, 240 (1988), p. 1642.Google Scholar
  22. 22.
    R.S. Feigelson, Mater. Sci. Eng., B1 (1988), p. 67.Google Scholar
  23. 23.
    S. Jin, T.H. Tiefel, R.C. Sherwood, R.B. van Dover, M.E. Davis, G.W. Kammlott and R.A. Fastnacht, Phys.Rev., B37 (1988), p. 7850.Google Scholar

Copyright information

© TMS 1989

Authors and Affiliations

  • R. B. Poeppel
    • 1
  • S. E. Dorris
    • 1
  • C. A. Youngdahl
    • 1
  • J. P. Singh
    • 1
  • M. T. Lanagan
    • 1
  • U. Balachandran
    • 1
  • J. T. Dusek
    • 1
  • K. C. Goretta
    • 1
  1. 1.Argonne National LaboratoryUSA

Personalised recommendations