Il Nuovo Cimento D

, Volume 19, Issue 8–9, pp 1123–1129 | Cite as

Jc enhancement by partial melting in BSCCO 2223 ceramics

  • M. Marchetta
  • L. Dimesso
  • A. Migliori
  • R. Masini
  • G. Calestani


The application of partial melting techniques to the densification of BSCCO 2223 ceramics is presented. A new method has been developed, that avoids the peritectic decomposition of the 2223 phase and exploits the existence of a limited region of the phase diagram, occurring for composition richer in Ca and Cu, in which this phase is the only BSCCO phase coexisting with the liquid. This allows the densification process assisted by the liquid phase, limiting at the same time the formation of undesired intergrowths of lower Tc phases. In comparison with the usually adopted processes, the new method results in a dramatic decrease of the post-treatment times, which are typically limited to a few hours. By optimising the thermal as well as the temporal parameters governing a standard two-steps procedure, values of Jc of the order of 103 A cm-2, at 77 K, can be obtained for a global process time not exceeding 6 hours.

PACS 74.62.Bf

Effects of material synthesis crystal structure and chemical composition 

PACS 01.30.Cc

Conference proceedings 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. [1]
    Yamada Y., Oobst B. andFlükiger R.,Supercond. Sci. Technol.,4 (1991) 165.CrossRefADSGoogle Scholar
  2. [2]
    Flukiger al., Supercond. Sci. Technol.,5 (1992) 561.CrossRefGoogle Scholar
  3. [3]
    Motowidlo L. R., Haldar P., Jin S. andSpencer N.D.,IEEE Trans. Appl. Supercond.,3 (1993) 942.CrossRefGoogle Scholar
  4. [4]
    Guo Y. C., Liu H. K. andDou S. X.,Physica B,194-196 (1994) 2075.CrossRefADSGoogle Scholar
  5. [5]
    Murayama N. andVander Sande J. B.,Physica C,241 (1995) 235.CrossRefADSGoogle Scholar
  6. [6]
    Marchetta M., Thesis, University of Parma (1996).Google Scholar
  7. [7]
    Strobel P. andFournier T.,J. Less Common Metals,164-165 (1990) 519.CrossRefGoogle Scholar
  8. [8]
    Morin al., Physica C,185-189 (1991) 487.CrossRefADSGoogle Scholar
  9. [9]
    Strobel al., Physica C,201 (1992) 27.CrossRefADSGoogle Scholar
  10. [10]
    Mansori M., Satre P., Roubin M., Vacquier G., Strobel P. andSebaoun A.,Physica C,235-240 (1994) 331.CrossRefADSGoogle Scholar
  11. [11]
    Toledano J. al., Physica C,253 (1995) 53.CrossRefADSGoogle Scholar
  12. [12]
    Bean C. P.,Rev. Mod. Phys.,36 (1964) 31.CrossRefADSGoogle Scholar

Copyright information

© Società Italiana di Fisica 1997

Authors and Affiliations

  • M. Marchetta
    • 1
  • L. Dimesso
    • 1
  • A. Migliori
    • 2
  • R. Masini
    • 3
  • G. Calestani
    • 2
    • 4
  1. 1.CNR-CSSDUniversità di ParmaParmaItaly
  2. 2.CNR-LAMELArea della Ricerca di BolognaBolognaItaly
  3. 3.CNR-ITMMilano
  4. 4.Dipartimento di Chimica Fisica ed InorganicaUniversità di BolognaBolognaItaly

Personalised recommendations