Remanent microwave absorptin in Y−Ba−Cu−O at low magnetic fields

  • W. M. Woch
  • A. Kołodziejczyk
  • Z. Trybuła
  • J. Stankowski


Polycrystalline samples of YBa2Cu3O7 were studied by the microwave absorption technique at the low magnetic fields in the temperature range from 5 to 80 K. The direct microwave absorption and the field modulated microwave absorption were measured at 77 K. Analysis of the microwave absorption curves indicates that the field penetration into the sample starts from the lowest values of applied magnetic field within the whole temperature range.


Applied Magnetic Field Josephson Junction Microwave Absorption Zero Field Cool Reversibility Field 


Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.


  1. [1]
    Stankowski J., Kahol P.K., Dalal N.S., Moodera J.S.: Phys. Rev. B36, 5940 (1987)CrossRefGoogle Scholar
  2. [2]
    Dulcić A., Rakvin B., Pozek M.: Europhys. Letters4, 593 (1987)Google Scholar
  3. [3]
    Pakulis E.J., Osada T.: Phys. Rev. B37, 5940 (1988)CrossRefADSGoogle Scholar
  4. [4]
    Dulcić A., Crepeau R.H., Freed J.H.: Phys. Rev. B39, 4249 (1989)CrossRefADSGoogle Scholar
  5. [5]
    Vedeshwar A.G.: Solid State Commun.74, 23 (1990)CrossRefADSGoogle Scholar
  6. [6]
    Bist H.D., Vedeshvar A.G.: Physica C162–164, 1577 (1990)Google Scholar
  7. [7]
    Vedeshwar A.G., Bist H.D., Agarval S.K., Narlikar A.V.: Physica C162–164, 1575 (1989)CrossRefGoogle Scholar
  8. [8]
    Vedeshwar A.G., Bist H.D., Agarval S.K., Narlikar A.V.: Physica C162–164, 1573 (1989)CrossRefGoogle Scholar
  9. [9]
    Czyżak B., Stankowski J.: Acta Phys. Polonica80, 99 (1991)Google Scholar
  10. [10]
    Misra S.K., Kaharizi M.: Physica C195 71 (1992)CrossRefADSGoogle Scholar
  11. [11]
    Stankowski J., B. Czyżak B., Martinek J.: Phys. Rev. B42, 10245 (1990)CrossRefADSGoogle Scholar
  12. [12]
    Stankowski J., Andrzejewski B., Czyżak B., Hilczer W.: Molecular Phys. Reports5, 269 (1994)Google Scholar
  13. [13]
    Ramachandran J.S., Huang M.X., Bhagat S.M., Kish K., Tyagi S., Physica C202, 151 (1992); Gould A., Bhagat S.M., Wellstood F.C., Tyagi S.: Solid State Commun.81, 339 (1992)CrossRefADSGoogle Scholar
  14. [14]
    Balzey K.W.: Springer Series in Solid-State Sciences (Bednorz J.G., Müller K.A., eds.), vol. 90. Berlin, Heidelberg: Springer-Verlag, 1990.Google Scholar
  15. [15]
    Müller K.A., Takashige M., Bednorz J.G.: Phys. Rev. Lett.58, 1143 (1987)CrossRefADSGoogle Scholar
  16. [16]
    de Almeida J.R.L., Thouless D.J.: J. Phys. A11, 983 (1978)CrossRefADSGoogle Scholar
  17. [17]
    Yeshurun Y., Malozemoff A.P.: Phys. Rev. Lett.60, 2202 (1988)CrossRefADSGoogle Scholar
  18. [18]
    See for instance: McElfresh M.W., Yeshurun, Y., Malozemoff A.P., Holtzberg F.: Physica A168, 308 (1990); Adrian H., Assmus W., Hohr A., Kowalewski J., Spille H., Steglich F.: Physica C162–164, 329 (1989)CrossRefADSGoogle Scholar
  19. [19]
    Czyżak B., Stankowski J.: Phys. stat. sol. (b)166, 219 (1991)CrossRefGoogle Scholar
  20. [20]
    Chmist J.: Thesis. Cracow: University of Mining and Metallurgy 1991.Google Scholar
  21. [21]
    Pakulis E.J.: Phys. Rev. B39, 9618 (1989)CrossRefADSGoogle Scholar
  22. [22]
    Malozemoff A.P., Worthington T.K., Yeshurun Y., Holtzberg F.: Phys. Rev. B38, 7203 (1988); Sagdahl L.T., Gjolmesli S., Laegreid T., Fossheim K., Assums W.: Phys. Rev. B42, 6797 (1990); Krusin-Elbaum L., Civale L., Holtzberg F., Malozemoff A.P., Feild C.: Phys Rev. Lett.67, 3156 (1991)CrossRefADSGoogle Scholar

Copyright information

© Springer 1995

Authors and Affiliations

  • W. M. Woch
    • 2
  • A. Kołodziejczyk
    • 2
  • Z. Trybuła
    • 1
  • J. Stankowski
    • 1
  1. 1.Institute of Molecular PhysicsPoznanPoland
  2. 2.Solid State Physics Dept., Faculty of Physics and Nuclear TechniquesUniversity of Mining and MetallurgyKrakówPoland

Personalised recommendations