The Young’s and shear moduli of NaCl whiskers

  • E. Hartmann
  • A. Tóth
Article

Abstract

The static and dynamic Young’s moduli, and the dynamic shear modulus of sodium chloride whiskers grown by various methods were measured at room temperature in the <100> direction. In the thickness range of 2–18 μ no dependence on whisker dimension was detected. According to the experimental results the values of the elastic moduli measured correspond to values obtained with large single crystals.

Keywords

Shear Modulus Polyvinyl Alcohol Thickness Dependence Large Single Crystal Torsional Pendulum 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Модуль юнга и модуль сдвига нитевидных кристаллов NaCl

Резюме

Определены величины статического и динамического модулей юнга и величина динамического модуля сдвига при комнатной температуре в направлении <100> для интевидных кристаллов NaCl, выращенных разными методами. Толщина интевидных кристаллов изменялась от 2 мк до 18 мк. Не обнаружена зависимость модулей от толщины образцов. По экспериментальным данным величины модулей согласуются с величинами модулей монокристаллов NaCl большого размера.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. V. Coleman, Metallurgical Reviews,9, 261, 1964.Google Scholar
  2. 2.
    S. S. Brenner, J. Appl. Phys.,27, 1484, 1956.CrossRefADSGoogle Scholar
  3. 3.
    С.З. Бокштейи, Т. Н. Зайцев, М.Р. Назарова, И. Л. Светлов, физ. тверд. тела,10, 564, 1968.Google Scholar
  4. 4.
    А. А. Шпунт, физ. тверд. тела,9, II22, 1967.Google Scholar
  5. 5.
    A. P. Levitt, Materials Research and Standards,6, 64, 1966.Google Scholar
  6. 6.
    L. R. Mc Creight, H. W. Rauch, Sr. andW. H. Sutton, Ceramic and Graphite Fibers and Whiskers, Acad. Press, New-York, 1965, p. 102.Google Scholar
  7. 7.
    R. Conte, B. Dreyfus andL. Weil, Acta Met.,10, 1125, 1962.CrossRefGoogle Scholar
  8. 8.
    Б. Есенски, З. Хартманн, Кристаллография,7, 435, 1962.Google Scholar
  9. 9.
    F. Kohlrausch, Praktische Physik, Band 1. B. G. Teubner Verlagsges. Leipzig, 1951.Google Scholar
  10. 10.
    H. B. Huntington, Solid State Phys.,7, 213, 1958.CrossRefGoogle Scholar
  11. 11.
    Н. М. Беляев, Сопротивление материалов, физматгиз, Москва 1959.Google Scholar

Copyright information

© with the authors 1969

Authors and Affiliations

  • E. Hartmann
    • 1
  • A. Tóth
    • 1
  1. 1.Research Group for Crystal Growth of the Hungarian Academy of Sciences, Institute for Experimental PhysicsTechnical UniversityBudapest

Personalised recommendations