Effect of surface damage on the tendency for darkening of ZnS single crystals

  • P. Sviszt
  • P. Kovács
  • M. Farkas-Jahnke
Article

Abstract

The tendency for darkening of the mechanically abraded and polished, etched and cleaved surfaces of hexagonal ZnS single crystals has been examined simultaneously with electron diffraction studies. The obtained results showed that there is a strong connection between the quality of the crystal surface and the tendency for darkening.

Keywords

Crystal Surface Electron Diffraction Pattern Acta Phys Surface Damage Abrasive Particle 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Влияние повреждения поверхности монокристаллов ZnS на их склонность к почернению

Резюме

Исследовалась склонность к почернению гексагональных монокристаллов ZnS с механически шлифованной и поливоранной, расколотой, а также травленной поверхностью. Параллельно было также произведено электроннодифракционное изучение этих поверхностей. Полученные экспериментальные результаты показывают, что имеется тесная связь между качеством поверхности кристаллов и их склонностью к почернению.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    P. Sviszt, phys. stat. sol.,4, 931, 1964.Google Scholar
  2. 2.
    L. T. Chadderton, A. G. Fitzgerald andA. D. Yoffe, Phil. Mag.,8, 167, 1963.CrossRefADSGoogle Scholar
  3. 3.
    P. Kovács andJ. Szabó, Acta Phys. Hung.,14, 131, 1962.CrossRefGoogle Scholar
  4. 4.
    L. E. Samuels, The Surface Chemistry of Metals and Semiconductors, New York-London 1959 (p. 82).Google Scholar
  5. 5.
    T. M. Buck, The Surface Chemistry of Metals and Semiconductors, New York-London 1959 (p. 107).Google Scholar
  6. 6.
    W. J. Dunning, Physics and Chemistry of the Organic Solid State, New York-London 1963 (p. 411).Google Scholar
  7. 7.
    P. Sviszt andP. Kovács, phys. stat. sol.,9, K5, 1965.CrossRefGoogle Scholar
  8. 8.
    Z. G. Pinsker, Electron Diffraction, London 1953.Google Scholar
  9. 9.
    H. Gobrecht undW. Kunz, Z. Phys.,136, 21, 1953.CrossRefADSGoogle Scholar
  10. 10.
    В. Л. Левшун иБ. Д. Рыжуков, Изв. AH CCCP cep. физ.,25, 362, 1961.Google Scholar

Copyright information

© with the authors 1966

Authors and Affiliations

  • P. Sviszt
    • 1
  • P. Kovács
    • 1
  • M. Farkas-Jahnke
    • 1
  1. 1.Research Institute for Technical Physics of the Hungarian Academy of SciencesBudapest

Personalised recommendations