Mechanisms of damage and fracture in high-temperature, low-cycle fatigue of a cast nickel-based superalloy
- 762 Downloads
In cast Udimet 500 subjected to high-temperature, low-cycle fatigue, localized oxidation at grain boundaries plays an important role in crack nucleation and propagation. Evidence is presented of a surface ridging and pronounced grain boundary penetration due to oxidation, a denudedγ′ zone adjacent to the oxide, and cracking of the oxide. The ridging is selective, and is presumed to occur on those boundaries where high stress exists. The phenomenon is viewed as analogous to stress-corrosion cracking.
KeywordsFatigue Metallurgical Transaction Metallurgical Transaction Volume Localize Oxidation Boundary Penetration
Unable to display preview. Download preview PDF.
- 1.L. F. Coffin, Jr.: General Electric Research and Development Center, Schenectady, N.Y., unpublished research.Google Scholar
- 2.E. Glenny, J. E. Northwood, W. K. Shaw, and T. A. Taylor:J. Inst. Metals, 1958-59, vol. 87, p. 294.Google Scholar
- 3.L. F. Coffin, Jr.:Trans. Quart. ASM, 1963, vol. 56, p. 339.Google Scholar
- 4.W. R. Butts, C. E. Johnson, and H. T. McHenry: Thermal Fatigue Comparison of Turbine Blade Alloys, Report R63FPD124, April 17, 1963, General Electric Co., Evendale, Ohio.Google Scholar
- 5.H.J. Murphy and C. D. Walker: General Electric Co., Schenectady, N.Y., unpublished work, 1967 and 1968.Google Scholar
- 6.N. T. Wagenheim and E. V. Giaquinto: General Electric Co., Schenectady, N.Y., unpublished work, 1969.Google Scholar
- 7.G. J. Hill:Thermal and High Strain Fatigue, p. 312, The Metals and Metallurgy Trust, London, 1967.Google Scholar
- 8.J. L. Walker: General Electric Research and Development Center, Schenectady, N.Y., unpublished research.Google Scholar