Abstract
Specimens of powder fabricated by codeposition of zirconium and yttrium nitrates with the using special dry ing techniques and regranulation by the method of hot isostatic pressing have been tested in air allowing for the laws of compaction of granulated powder at a final firing temperature of about 1500°C. The resulting ma terial had the following properties: a density p = 5.91 g/cm (98% of the theoretical value), an ultimate bend ing strength a = 1100 MPa, and a crack resistance K = 19.5 MPa . rn A set of the specimens was sub jected to hot isostatic pressing after natural sintering and exhibited the following properties: p = 6.08 g/cm = 1400 MPa, K = 17.5 MPa · m1/2.
Similar content being viewed by others
References
R. C. Garuie, R. H. Hannik, andR. T. Pascoe,“Ceramic steel,”Nature (London), No. 258(5537), 703–704 (1975).
S. Rajendran,“Production of reactive single- and multi-component ceramics oxide powders and fabrication of high-strength ceramics,”J. Mater. Sci., No. 27, 433–440 (1992).
E. V. Dudnik, Z. A. Zaitseva, A. V. Shevchenko, andL. M. Lopato,“Sintering of ultradisperse powders based on zirconia (a review),”Powder Met., No. 5/6, 43–52 (1995).
V. V. Storozh, G. Ya. Akimov, et al.,“Press mold for installation for hydrostatic pressing of articles from powder materials,” USSR Inventor’s Certificate No. 1433804,Otkryt. Izobret., No. 40 (1988).
T. K. Gupta, F. F. Lange, andJ. H. Bechtold, “Effect of stressinduced phase transformation on the properties of polycrystalline zirconia containing metastable tetragonal phase,”J. Mater. Sci., No. 13,1464-1470(1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Akimov, G.Y., Vereshchak, V.G., Vasil’ev, A.D. et al. High-strength ceramics from Zr02 . Refract Ind Ceram 39, 324–325 (1998). https://doi.org/10.1007/BF02770593
Issue Date:
DOI: https://doi.org/10.1007/BF02770593