Properties of refractories from ZrO2 stabilized by the method of plasmachemical treatment
Results of an experimental study of the sinterability and resistance of zirconia-base materials stabilized by the method of plasmachemical synthesis to the action of the main components of metallurgical slags are presented. It is shown that the materials possess the highest resistance to the action of Fe2O3, Al2O3, and basic slag of the SiO2−CaO−Fe2O3 system, are less resistant to the action of acid slag of this system, and decompose actively under the effect of SiO2.
KeywordsOpen Porosity Firing Temperature Baddeleyite ZrSiO4 Basic Slag