Il Nuovo Cimento (1955-1965)

, Volume 29, Issue 6, pp 1244–1261 | Cite as

Recovery of aluminium after neutron-irradiation at 78 °K

  • S. Ceresara
  • T. Federighi
  • D. Gelli
  • F. Piergostini
Article

Summary

Zone-refined Al and 99.995% purity Al samples were irradiated at liquid-nitrogen temperature at fast (> 1 MeV) neutron doses of 1.4·1018 n/cm2 and of about 2·1017n/cm2. The recovery of radiation damage, as revealed by electrical resistivity, takes place mainly in two stages, indicated as stageIn-2 andIn-3, centered respectively at-150 °C and at -60 °C. StageIn-2, controlled by an activation energy of about 0.3 eV, is sensitive to the impurity content and has been ascribed to the release of trapped interstitials. StageIn-3, controlled by an activation energy of 0.59 eV, follows a complex kinetics which can be considered a generalization of’ a second-order reaction. Although the interpretation of this stage is not conclusive, some evidence supports the idea that a multiple vacancy-type defect (quadri-vacancy) annihilates by recombination with an immobile interstitial aggregate.

Riassunto

Sono presentati i risultati di uno studio resistometrico sugli effetti dell’irraggiamento neutronico veloce (> 1 MeV) a 78 °K su alluminio di zona fusa e alluminio 99.995%. II recovery dell’extra-resistività introdotta dall’irraggiamento avviene praticamente in due stadi, indicati stadioI-2 eIn-3 e centrati a -150 °C e a — 60 °C rispettivamente. Lo stadioIn-2, controllato da un’energia di attivazione di circa 0.3 eV, è stato attribuito al rilascio e all’eliminazione di interstiziali intrappolati da atomi di impurità. Lo stadioIn-3, controllato da un’energia di attivazione di (0.59±0.02 eV), segue una cinetica complessa che può considerarsi una generalizzazione di una cinetica del secondo ordine. Benchè l’interpretazione di questo stadio non sia conclusiva, alcuni dati sperimentali avvalorano l’ipotesi che un difetto multiplo tipo vacanza si elimini per ricombinazione con un aggregato immobile d’interstiziali.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. (1).
    Radiation Damage in Solids (Venice Conference, 7–11 May 1962), Ed. Intern. Atomic Energy Agency (Vienna, 1962).Google Scholar
  2. (2).
    T. H. Blewitt, R. E. Coltman andC. E. Klabunde: Report ORNL 2829, 69 (1959).Google Scholar
  3. (3).
    A. W. McReynolds, W. Augustyniak, M. McKeown andD. B. Rosenblatt:Phys. Rev.,98, 418 (1955).ADSCrossRefGoogle Scholar
  4. (4).
    C. Panseri andT. Federighi:Phil. Mag.,3, 1223 (1958).ADSCrossRefGoogle Scholar
  5. (5).
    C. Panseri, S. Ceresara andT. Federighi:Nuovo Cimento,29, 1223 (1963).CrossRefGoogle Scholar
  6. (6).
    A. Sosin andL. H. Eachal: to be published.Google Scholar
  7. (7).
    L. Bochirol, J. Doulat andL. Weil:Cryogenics,1, 44 (1960).ADSCrossRefMATHGoogle Scholar
  8. (8).
    C. J. Meechan andJ. A. Brinkman:Phys. Rev.,103, 1193 (1956).ADSCrossRefGoogle Scholar
  9. (9).
    P. G. Lucasson andR. M. Walker:Phys. Rev.,127, 485 (1962).ADSCrossRefGoogle Scholar
  10. (10).
    T. Fedeeighi:Phil. Mag.,4, 502 (1959).ADSCrossRefGoogle Scholar
  11. (1).
    P. B. Hiesch, J. Silcox, R. E. Smallman andK. H. Westmacott:Phil. Mag.,3, 897 (1958).ADSCrossRefMATHGoogle Scholar
  12. (12).
    A. H. Cottrell: Institute of Metals, Monograph, and Report Series No. 23, 1 (1958).Google Scholar
  13. (13).
    T. S. Lundy andJ. F. Murdock:Journ. Appl. Phys.,33, 1671 (1962).ADSCrossRefGoogle Scholar
  14. (14).
    T. Federighi andS. Ceresara:Phil. Mag., in press.Google Scholar

Copyright information

© Società Italiana di Fisica 1963

Authors and Affiliations

  • S. Ceresara
    • 1
  • T. Federighi
    • 1
  • D. Gelli
    • 1
  • F. Piergostini
    • 2
  1. 1.Istituto Sperimentale Metalli LeggeriNovara
  2. 2.SORINSaluggia

Personalised recommendations