Il Nuovo Cimento B (1971-1996)

, Volume 33, Issue 1, pp 354–367 | Cite as

Internal friction in iron-chromium alloys

  • B. Dubois
  • S. A. Rizkallah
  • G. Brun
  • G. Flamant
  • G. Bouquet
Article

Summary

After the quenching of three iron-chromium alloys from 1100°C, the internal friction was studied as a function of the tempering temperature. Between room temperature and 400°C, internal-friction maxima appeared and the tempering behaviour was different depending on the chromium concentration. The chromium content of the three alloys was 2%, 12% and 17%, but for a given chromium concentration the alloy structure is determined by the carbon content. The effect of the carbon concentration was particularly studied for every alloy. In the case of the 17% chromium steel we have tried to relate the internal-friction measurements to the tensile tests: it seems that the carbide precipitation only decreases the serration effects on the tensile curves. For this alloy we believe that we have a relaxation effect or a precipitation process depending on the carbon content.

Riassunto

Dopo la tempra di tre leghe di ferro-cromo da 1100°C, si è studiato l'attrito interno in funzione della temperatura di tempra. I massimi dell'attrito interno sono apparsi fra la temperatura ambiente e 400°C mentre il comportamento della tempra era diverso dipendendo dalla concentrazione del cromo. Il contenuto di cromo delle tre leghe era 2%, 12% e 17%, ma per una data concentrazione di cromo la struttura della lega è determinata dal contenuto di carbonio. Si è studiato in modo particolare l'effetto della concentrazione del carbonio per ciascuna lega. Nel caso di acciaio con il 17% di cromo si è cercato di mettere in relazione le misure di attrito interno con le prove di trazione: sembra che la precipitazione di carbonio diminuisca solo gli effetti di striatura sulle curve di trazione. Per questa lega si pensa che esista un effetto di rilassamento od un processo di precipitazione che dipende dal contenuto in carbonio.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. (1).
    S. Bouquet-Maille andB. Dubois:Journée des Aciers Speciaux (Nantes, 1971); Mém. Sci. Rev. Mét.,68, 871 (1971).Google Scholar
  2. (2).
    S. Bouquet-Maille andB. Dubois:XIV Colloque de Métallurgie de Saclay, 1971 (Paris, 1973), p. 293.Google Scholar
  3. (3).
    G. Brun andB. Dubois:XVI Colloque de Métallurgie de Saclay, 1973 (Paris, 1974), p. 603.Google Scholar
  4. (4).
    G. Brun andB. Dubois:Colloque International de Saint Etienne sur les Aciers au Chrome (Saint Etienne, 1973), p. 415.Google Scholar
  5. (5).
    V. Djafari andB. Dubois:Métaux, Corrosion, Industrie,596, 146 (1975).Google Scholar
  6. (6).
    B. Dubois:Seminario de Aceros Especiales (Buenos Aires, 1975), H. 1.Google Scholar
  7. (7).
    R. Ward andJ. M. Capus:Journ. Iron Steel Inst. 201, 1038 (1963).Google Scholar
  8. (8).
    T. Gladman andF. B. Pickering:Journ. Iron Steel Inst. 204, 112 (1966).Google Scholar
  9. (9).
    M. Lacoude andC. Goux:Mém. Sci. Rev. Mét.,63, 805 (1966).Google Scholar
  10. (10).
    A. M. Huntz, P. Guiraldenq, M. Aucouturier andP. Lacombe:Mém. Sci. Rev. Mét.,66, 85 (1969).Google Scholar
  11. (11).
    P. Poyet, P. Guiraldenq andJ. Hochmann:Mém. Sci. Rev. Mét.,69, 775 (1972).Google Scholar
  12. (12).
    M. J. Roberts andW. S. Owen:Met. Trans.,1, 3203 (1970).Google Scholar
  13. (13).
    Y. Nakada andA. S. Keh:Act. Met.,18, 437 (1970).CrossRefGoogle Scholar
  14. (14).
    T. S. Kê andY. L. Ma:Sci. Sinica,6, 81 (1957).Google Scholar
  15. (15).
    K. Bungardt andH. Preisendanz:Arch. Eisenh.,27, 715 (1956).Google Scholar
  16. (16).
    Y. L. Ma andT. S. Kê:Sci. Sinica,15, 153 (1966).Google Scholar

Copyright information

© Società Italiana di Fisica 1976

Authors and Affiliations

  • B. Dubois
    • 1
  • S. A. Rizkallah
    • 1
  • G. Brun
    • 1
  • G. Flamant
    • 1
  • G. Bouquet
    • 1
  1. 1.Laboratoire de Métallurgie et MatériauxEcole Nationale Supérieure de Chimie de ParisParis, Cedex 05France

Personalised recommendations