Remarks on the martensitic transformation in some iron-nickel alloys

  • G. Bordin
  • G. C. Cecchi
  • G. B. Fratucello
Article

Summary

Resistive and magnetic measurements have been performed on some iron-nickel system alloys in order to study the martensitic transformation as a function of temperature. The analysis of the experimental results enables us to obtain some information about the mechanism of transformation. The free-energy changes accompanying the transformation of various alloys appear to cause either the organization of embryos into groups giving rise to bursts, or the activation of single embryos that control the smooth behaviour of transformation.

Замечания о мартенситном превращении в некоторых железо-никелевых сплавах

Резюме

Проводятся измерения сопротивления и магнитные измерения на некоторых железо-никелевых сплавах, чтобы исследовать мартенситное преобразование, как функцию температуры. Анализ экспериментальных результатов позволяет нам получить некоторую информацию о механизме преобразования. Изменения свободной энергии, сопровождающие преобразование различных сплавов, по-видимому, вызывают либо преващение зародышей в группы, что приводит к возникновению импулясов, или активацию отдельных зародышей, что определяет плавное поведение преобразования.

Riassunto

Sono state effettuate misure di resistenza elettrica e di momento magnetico in funzione della temperatura di raffreddamento su leghe di ferro-nichel allo scopo di studiare la trasformazione martensitica. L’analisi dei risultati sperimentali permette di ottenere informazioni sulla variazione di energia libera che accompagna la trasformazione martensitica delle varie leghe. Essa sembra essere responsabile sia dell’organizzazione degli embrioni in gruppi che, successivamente, si trasformano come burst, sia dell’attivazione dei singoli embrioni che permettono di ottenere un comportamento regolare nella trasformazione della lega.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. (1).
    J. J. Kramer andR. K. Raheja:Techniques for investigating phase transition kinetics in metals, inTechniques of Metals Research, edited byR. F. Bunshah, Vol. IV, part I (New York, N. Y., 1970), p. 488.Google Scholar
  2. (2).
    Y. Nakamura:IEEE Trans. Magn.,12, 278 (1976).ADSCrossRefGoogle Scholar
  3. (3).
    M. Hansen:Constitution of Binary Alloys (New York, N. Y., 1958), p. 680.Google Scholar
  4. (4).
    S. S. Hsu, J. H. Chen andP. C. Clapp:Phys. Status Solidi A,50, 393 (1978).ADSCrossRefGoogle Scholar
  5. (5).
    A. W. Mc Reynolds:J. Appl. Phys.,17, 823 (1946).ADSCrossRefGoogle Scholar
  6. (6).
    M. Peschard:Rev. Met.,22, 490, 581, 663 (1925).Google Scholar
  7. (7).
    Y. Tino andH. Kagawa:J. Phys. Soc. Jpn.,28, 1445 (1970).ADSCrossRefGoogle Scholar
  8. (8).
    S. Chikazumi, T. Mizoguchi andN. Yamaguchi:J. Appl. Phys.,39, 939 (1968).ADSCrossRefGoogle Scholar
  9. (9).
    W. F. Schlosser:J. Phys. Chem. Solids,32, 939 (1971).ADSCrossRefGoogle Scholar
  10. (10).
    P. C. Clapp:Phys. Status Solidi B,57, 561 (1963).ADSCrossRefGoogle Scholar
  11. (11).
    H. Knapp andV. Dehlinger:Acta Met.,4, 289 (1956).CrossRefGoogle Scholar
  12. (12).
    L. Kaufman andM. Cohen:Prog. Metal. Phys.,7, 165 (1958).ADSCrossRefGoogle Scholar
  13. (13).
    L. Kaufman andM. Cohen:Trans. AIME,206, 1393 (1956).Google Scholar

Copyright information

© Società Italiana di Fisica 1981

Authors and Affiliations

  • G. Bordin
    • 1
    • 2
  • G. C. Cecchi
    • 1
    • 2
  • G. B. Fratucello
    • 1
    • 2
  1. 1.Istituto di Fisica dell’UniversitàFerrara
  2. 2.G.N.S.M. del C.N.R.Ferrara

Personalised recommendations