A systematic study of carbide and nitride additions on the heterogeneous nucleation behavior of supercooled liquid iron was undertaken. It was found that titanium nitride and titanium carbide were very effective in promoting heterogeneous nucleation. These compounds were followed by silicon carbide, zirconium nitride, zirconium carbide, and tungsten carbide in decreasing order of effectiveness. The degree of potency of the nucleation catalysts is explained on the basis of the disregistry between the lattice parameters of the substrate and the nucleating phase. Through the inclusion of planar terms the Turnbull-Vonnegut “linear” disregistry equation was modified to more accurately describe the crystallographic relationship at the interface during heterogeneous nucleation.
This is a preview of subscription content, log in to check access.
Buy single article
Instant access to the full article PDF.
Price includes VAT for USA
Subscribe to journal
Immediate online access to all issues from 2019. Subscription will auto renew annually.
This is the net price. Taxes to be calculated in checkout.
L.M. Hogan and G. L. F. Powell:J. Austral. Inst. Metals, 1966, vol. 11, p. 235.
A. Walton:International Science and Technology, Dec. 1966, p. 28.
K. A. Jackson,Ind. Eng. Chem., 1965, vol. 57, p. 28.
G. A. Chadwick:Metals and Materials, 1969, vol. 3, no. 3, p. 77.
B. E. Sundquist and L.F. Mondolfo:Trans. TMS-AIME, 1961, vol. 221, p. 607.
G. M. Pound:Liquid Metals and Solidification, p. 87, ASM, 1958.
W. A. Tiller and T. Takahashi:Acta Met., 1969, vol. 17, p. 483.
D. Tumbull and R. Vonnegut:Ind. Eng. Chem., 1952, vol. 44, p. 1292.
P. J. Bradshaw, M. E. Gasper, and S. Pearson:J. Inst. Metals, 1958, vol. 87, p. 15.
B.E. Sundquist and L. F. Mondolfo:Trans. TMS-AIME, 1961, vol. 221, p. 157.
J. A. Reynolds and C. R. Tottle:J. Inst. Metals, 1951, vol. 80, p. 1328.
M. E. Glicksman and W. J. Childs:Acta Met, 1962, vol. 10, p. 925.
G. K. Turnbull, D. M. Patton, G. W. Form, and J. F. Wallace:Trans. Am. Foundrymen’s Soc, 1960, vol. 69, p. 792.
N. Church, P. Wieser, and J. F. Wallace:Mod. Castings, 1966, p. 129.
J. F. Wallace:Proc. Electric Furnace Conf., 1962, p. 125.
G. K. Turnbull, G. W. Form, and J. F. Wallace: 1962, U. S. Patent No. 3,308,515.
J. E Wallace:J. Metals, 1963, p. 372.
P. B. Crosley, A. W. Douglas, and L. F. Mondolfo:Iron Steel Institute, Publication 110,1967, p. 10.
A. Goldsmith, T. E. Waterman, and H. J. Hirschhorn:Handbook of Thermophysical Properties of Solid Materials, 1961, vol. 4.
F. Kralik and P. Seb.:Kovove Materialy, 1965, vol. 3, p. 106.
A. Hoffmann:Arch. Eisenhuttenw., 1967, vol. 38, p. 785.
A. Taylor and B. J. Kagel: Crystallographic Data on Metal and Alloy Structures, Dover, New York, 1963.
An erratum to this article is available at http://dx.doi.org/10.1007/BF03037838.
About this article
Cite this article
Bramfitt, B.L. The effect of carbide and nitride additions on the heterogeneous nucleation behavior of liquid iron. Metall Mater Trans B 1, 1987–1995 (1970). https://doi.org/10.1007/BF02642799
- Tungsten Carbide
- Heterogeneous Nucleation
- Titanium Carbide
- Liquid Iron