About the possibility of producing wood particle boards with extremely low formaldehyde content

  • A. K. Tsapuk
Article
  • 31 Downloads

Abstract

Laboratory investigations have been conducted with the aim of producing wood particle boards with formaldehyd content less than that of initial wood particles. Wood particle boards have been produced on the basis of low-mole urea-formaldehyde resins using mole ratios of urea to formaldehyde 1∶1.2 and 1∶1.15. Physical-mechanical properties of the boards are similar to those made on the basis of commercial-grade resins.

Keywords

Formaldehyde Emission Formaldehyde Content Urea Formaldehyde Wood Particle Particle Board 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Versuche zur Herstellung von Spanplatten mit extrem niedrigem Formaldehydgehalt

Zusammenfassung

Laborversuche wurden durchgeführt mit dem Ziel, Spanplatten zu produzieren, deren Formaldehydgehalt geringer ist als derjenige der eingesetzten Holzspäne. Die Späne wurden mit Harnstoff-Formaldehyd-Harz verleimt, wobei Molverhältnisse von 1∶1,2 und 1∶1,15 (Harnstoff: Formaldehyd) verwendet wurden. Die physikalischmechanischen Eigenschaften dieser Platten waren mit denen von Kontrollplatten auf der Basis kommerzieller Harzgemische vergleichbar.

Literature

  1. Beketov, V. D.: Analysis of production effectiveness and application of structural wood materials. Derevoobratyvayuschaja promyshlenost. 4 (1990) 22–24Google Scholar
  2. Chetyrkin, E. M.: Statistical prediction methods. Moscow. Statistika. 188 p. 1975Google Scholar
  3. DIN EN 120: Spanplatten-Bestimmung des Formaldehydgehaltes. Extraktionsverfahren genannt Perforatormethode (October 1984Google Scholar
  4. Dunky, M.: Die Langzeit-Formaldehydemission aus Spanplatten. Holz Roh-Werkstoff 48 (1990) 371–375Google Scholar
  5. Elbert, A. A.: Chemical technology of wood particle boards. M. Lesnaja promyshlennost. 224 p. 1984Google Scholar
  6. Ernst, K.: Die verschiedenen Herstellverfahren für Spanplatten der Emissionsklasse E1. Holz Roh-Werkstoff 40 (1982) 249–253CrossRefGoogle Scholar
  7. Lecka, J.; Morze, L.; Synowiec, J.: Organiczenie emisji formaldehydu z plyt wicrowych przez nasycanie ich powierzchni srodkami wiazacymi. Przemysl drzewy. N 1 (1988) 12–13Google Scholar
  8. Methodical instructions on sanitary control of polymeric structural materials for dwelling houses and public buildings. Approved by USSR chief sanitary physician Kovshilo V.E. 28.03.80. N2158-80. M. Health Ministry Publishing House. 81 p.Google Scholar
  9. Pizhurin, A. A.; Rozenblit, M. S.: Study of wood-working processes. Moscow. Lesnaja Promyshlenost. 232 p. 1984Google Scholar
  10. Roffael, E.; Schriever, E.: Einfluß des Kondensationsgrades von UF-Harzen auf die Formaldehydabgabe von Spanplatten. Holz Roh-Werkstoff 43 (1985) 38CrossRefGoogle Scholar
  11. Schwarzman, G. M.; Schedro, D. A.: Production of wood particle boards. Moscow. Lesnaja Promyshlennost. 320 p. 1987Google Scholar
  12. Tsapuk, A. K.: Possibility of sanitary-chemical estimation of wood particle boards by perforator method. Derevoobrabotka. Information collected volume. Issue 1 (1991) 17Google Scholar
  13. Vasilgev, O. A.; Ivanova, N. I.; Kudinova, E. A.: Our experience of low-toxicity wood particle board production. Derevoobrabaty-vayuschaja promyshlennost. N8 (1990) 27–28Google Scholar
  14. Wirpsza, Z.; Brzezinski, J.: Aminoplasty. Moscow. Chemistry. 344 p. 1972Google Scholar

Copyright information

© Springer-Verlag 1992

Authors and Affiliations

  • A. K. Tsapuk
    • 1
  1. 1.All-Union Research Wood Working InstituteUSSR

Personalised recommendations