Der Einfluß der Naßlagerung auf das Wasseraufnahmevermögen des Kiefernsplintholzes

  • O. Suolahti
  • Aini Wallén
Article

The influence of water storage on the waterabsorption capacity of pine sapwood

Summary

The paper deals with the determination of the influence which water storage exerts on the absorption capacity of pine sapwood. Sapwood cubes of 1.5×2.5×5.0 cm were used as specimens. They were weighed dry and then immersed in water for half an hour or 24 hours. The amount of water imbibed was determined by weighing and related in percent to the dry weight of the wood. The results permitted of the following conclusions: There is no relationship between the water absorption capacity and the anatomical structure of wood. Wood that has been quickly dried by usual methods absorbs only slowly and little water. However, floated wood or wood that has been stored in a wet condition for some time has a good absorption capacity after being dried. Resin components do not account for this phenomenon whereas an increase in water absorption was always accompanied by a decrease in pectines which apparently were decomposed by micro-organisms. Bacteria that were not strictly identified, Trichoderma- and Aspergillus moulds increased the water absorption capacity with simultaneously decreasing pectin content. The same effect could be obtained by heating the wood in a pectin dissolving ammonium oxalate solution applying a pressure of I atm. or by heating it at 35°C in an ammonium oxalate solution with pectin enzym.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Schrifttum

  1. 1.
    Bailey, A. J.: Lignin in Douglas Fir. Ind. Eng. Chem. Anal. Ed. Bd.8 (1936) S. 389.CrossRefGoogle Scholar
  2. 2.
    Bashenow, W. A.: Die Flüssigkeitsdurchlässigkeit von Holzgeweben und ihre praktische Anwendung. Berlin 1956: Akademie-Verlag.Google Scholar
  3. 3.
    Fichte, E.: Strukturveränderungen am toten Holz durch technische Einflüsse und ihre Sichtbarmachung durch Färbungen. Angew. Bot. Bd.11 (1929) S. 77/112.Google Scholar
  4. 4.
    Frey-Wyßling, A., u. H. H. Bosshard: Über den Feinbau der Schließhäute in Hoftüpfeln. Holz als Roh- und Werkstoff Bd.11 (1953) S. 417.CrossRefGoogle Scholar
  5. 5.
    Griffin, G. J.: Bordered Pits in Douglas Fir. Journ. Forestry Bd.18 (1919) S. 813.Google Scholar
  6. 6.
    Grindell, P.: Pressure Creosoting and the Requirements for Treating Practice, BWPA Record of the 1955 Annual Convention. S. 85.Google Scholar
  7. 7.
    Holmgren, H.: Om impregneringens beroende av furuvirkets förbehandling med hänsyn till barknings-metoder och vattenläggning. Sv. flottledsförbundets arsskrift26 (1952).Google Scholar
  8. 8.
    Koljo, B.: Über die Mechanik der Flüssig-keitsbewegung bei der Holzimprägnierung. Diss. Universität Hamburg. Druck: Svenska Träforskningsinstitutet. Trätekniska Avdelningen. Stockholm 1951. Medelande 25 B.Google Scholar
  9. 9.
    Kollmann, F.: Technologie des Holzes und der Holzwerkstoffe, I. Band. 2. Aufl. S. 154. Berlin/Göttingen/Heidelberg 1951: Springer.Google Scholar
  10. 10.
    Kontio, P.: Untersuchungen über die Bildung der Pektinenzyme beiAspergillus niger r. Tieghem. Diss. Helsinki 1950.Google Scholar
  11. 11.
    Liese, W.: Über die Eindringung von öligen Schutzmitteln in Fiehtenholz. Holz als Roh- und Werkstoff Bd.9 (1951) S. 374/78.Google Scholar
  12. 12.
    Liese, W., und M. Fahnenbrock: Elektronenmikroskopische, Untersuchungen über den Bau der Hoftüpfel. Holz als Roh- und Werkstoff Bd.10 (1952) S. 197/200.CrossRefGoogle Scholar
  13. 13.
    Lüdtke, M.: Über die Pektinstoffe des Holzes. Holz als Roh- und Werkstoff Bd.5 (1942) S. 338/44.Google Scholar
  14. 14.
    Lüdtke, M., u. H. Felser: Zur Kemtnis der Pektinstoffe. Liebigs Ann. Bd.549 (1941) S. 4/43.Google Scholar
  15. 15.
    Phillips, E. W. J.: Movement in the Pit Membrane in Coniferons Woods, with Special Reference to Preservative Treatment. Forestry Bd.7 (1933) S. 109.Google Scholar
  16. 16.
    Sandermann, W., u. G. Z. Jonas: Über die Imprägnierung von Hölzern mit öligen Schutzmitteln unter hesonderer Berücksichtigung der Fichte. Holz als Roh- und Werkstoff Bd.10 (1952) S. 305/11.CrossRefGoogle Scholar
  17. 17.
    Stemsrud, F.: Über die Feinstruktur der Hoftüpfel-Schließhaut von Nadelhölzern. Holzforsehung Bd.10 (1956) S. 69/75.Google Scholar
  18. 18.
    Suolahti, O.: Effect of Barking and Storage Time in the Impregnability of Poles. Finn. Paper a. Timb. Jg.1954, H. 1. S. 8/9.Google Scholar
  19. 19.
    Suolahti, O.: Laboratory Tests on Soaking and Drying of Sound and Decayed Wood. Helsinki 1949, Staatliche Technische Forsehungsanstalt. Mitteilung 65.Google Scholar

Copyright information

© Springer-Verlag 1958

Authors and Affiliations

  • O. Suolahti
    • 1
  • Aini Wallén
    • 1
  1. 1.Staatliche Technische ForschungsanstaltHelsinki

Personalised recommendations