Abstract
Unidirectional solidification of Sb-InSb alloys, 26-34wt% In, was carried out in the range of growth rate 1.2 × 10−4 to 1.2 × 10−1 cms−1 and with a temperature gradient 57° C cm−1. An explanation is given which relates the coupled region with quantitative data concerning the primary phases, e.g. the area fraction and the protrusion length ahead of the eutectic interface. The coupled region can be constructed with reasonable accuracy from those quantities measured. The estimated coupled region is in qualitative agreement with the experimental result.
Similar content being viewed by others
References
W. Kurz and D. J. Fisher, Int. Met. Rev. 24 (1979) (5/6) 177.
R. Elliott, “Eutectic Solidification Processing” (Butterworths, London, 1983) p. 284.
D. J. Fisher and W. Kurz, in “Solidification and Casting of Metals”, edited by B. B. Argent (Metal Society, London, 1979) p. 57.
F. R. Mollard and M. C. Flemings, Trans. Met. Soc. AIME 239 (1967) 1526.
R. M. Sharp and M. C. Flemings, Met. Trans. 4A (1973) 997.
J. D. Verhoe Yen and E. D. Gibson, ibid. 4A (1973) 2581.
H. Jones and W. Kurz, ibid. 11A (1980) 1265.
I. S. Ahn, PhD thesis, Han Yang University, Seoul (1986).
M. J. Suk, I. S. Ahn and I. H. Moon, J. Mater. Sci. 21 (1986) l451.
M. J. Suk, G. H. Choi and I. H. Moon, J. Korean Inst. Met. 23 (1990) (5) 462.
R. C. Sharma, T. L. Ngai and Y. A. Chang, Bull. Alloy Phase Diagrams 10 (1989) 657.
K. A. Jackson and J. D. Hunt, Trans. Met. Soc. AIME 236 (1966) 1129.
M. H. Burden and J. D. Hunt, J. Cryst. Growth 22 (1974) 328.
Idem., ibid. 22 (1974) 109.
E. E. Underwood, “Quantitative Stereology“ (Addison-Wesley, Reading, 1970) p. 25.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Suk, M.J., Moon, I.H. Coupled region and area fraction of primary phases in Sb-InSb eutectic alloys. J Mater Sci 26, 4931–4936 (1991). https://doi.org/10.1007/BF00549873
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00549873