Processing-structure relationships for multiphase epoxy matrix systems

Abstract

A styrene-modified diglycidyl ether of bisphenol-A (DGEBA) epoxy system cured with trimellitic anhydride (TMA) has been investigated to explore processing and structure relationships. During cure, the reactive styrene precipitated with polymerization into phase domains separate from the epoxy phase. Dynamic mechanical analysis and microscopy studies were performed to gain insight to matrix structure. The DMA studies showed that the styrenemodified epoxy system after cure exhibited two partially overlapped but distinct relaxation peaks, which are associated with the T gs of the polystyrene and epoxy phases. The glass transition of the polystyrene phase was shown to be broadened and the T g to depend strongly on processing temperature profiles. While the T g of the epoxy phase increases with curing agent concentrations, the T g of the polystyrene phase does not. Microscopic studies showed that the styrene-modified system exhibited a rougher fracture surface but did not reveal well defined phase domains in which the precipitated polystyrene component was aggregated. Overall, the study has demonstrated correlations of the kinetic factors in controlling the morphology in reactive modifier-epoxy systems.

This is a preview of subscription content, access via your institution.

References

  1. 1.

    E. M. Woo and J. C. Seferis, J. Appl. Polym. Sci. (1988) 40 (1990) 1237.

    CAS  Article  Google Scholar 

  2. 2.

    S. G. Chu, H. Jabloner and B. J. Swetlin, US Patent 4 656 208 (1987).

  3. 3.

    A. Noshay and L. M. Robeson, J. Polym. Sci. Chem. Edn 12 (1974) 689.

    CAS  Article  Google Scholar 

  4. 4.

    A. M. Ibrahim, T. J. Quinlivan and J. C. Seferis, ACS Polym. Prep. 26 (1985) 277.

    CAS  Google Scholar 

  5. 5.

    P. D. Mclean, A. Garton and W. T. K. Stevenson and K. E. Macphee, Polym. Comp. 7 (1987) 330.

    Article  Google Scholar 

  6. 6.

    D. A. Shimp, F. A. Hudock and W. S. Bobo, 18th Int. SAMPE Tech. Conf. Ser., (1986) pp. 851.

  7. 7.

    C. B. Bucknall and I. K. Partridge, Polym. Eng. Sci. 26 (1986) 54.

    CAS  Article  Google Scholar 

  8. 8.

    C. B. Bucknall and T. Yoshii, Brit. Polym. J. 10 (1978) 53.

    CAS  Article  Google Scholar 

  9. 9.

    Z. Nir, W. J. Gilwee, D. A. Kourtides and J. A. Parker, Polym. Comp. 6 (1985) 72.

    CAS  Article  Google Scholar 

  10. 10.

    L. T. Manzione and J. K. Gillham, J. Polym. Sci. 26 (1981) 889.

    CAS  Google Scholar 

  11. 11.

    R. W. Hewitt, Jr, US Patent 4 284 753 (1981).

  12. 12.

    O. Olabishi, L. M. Robeson and M. T. Shaw, “Polymer-Polymer Miscibility” (Academic, New York, 1979) Ch. 2

    Google Scholar 

  13. 13.

    A. V. Tobolsky, “Properties and Structures of Polymers” (Wiley, New York, 1960) p. 95

    Google Scholar 

  14. 14.

    T. Murayama and J. P. Bell, J. Polym. Sci. A8 (1970) 437.

    Google Scholar 

  15. 15.

    D. S. Kaplan, J. Appl. Polym. Sci. 20 (1976) 2615.

    CAS  Article  Google Scholar 

  16. 16.

    U. T. Kreibich and R. Schmid, J. Polym. Sci., Symp. Edn 53 (1975) 177.

    CAS  Article  Google Scholar 

  17. 17.

    J. L. Racich and J. A. Koutsky, J. Appl. Polym. Sci. 20 (1976) 2111.

    CAS  Article  Google Scholar 

  18. 18.

    H. S. Chu and J. C. Seferis, in “TheRole of the Polymeric Matrix in the Processing and Structural Properties of Composites Materials”, edited by J. C. Seferis and L. Nicolais (Plenum, New York, 1983) p. 53.

    Google Scholar 

Download references

Author information

Affiliations

Authors

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Woo, E.M., Seferis, J.C. & Bravenec, L.D. Processing-structure relationships for multiphase epoxy matrix systems. J Mater Sci 26, 1691–1698 (1991). https://doi.org/10.1007/BF00544684

Download citation

Keywords

  • Epoxy
  • Dynamic Mechanical Analysis
  • Epoxy Matrix
  • Diglycidyl Ether
  • Diglycidyl