Abstract
Poly(anilino sulphamicphosphazenes) such as [NP(HNC6H5)2−x(HNC6H4SO3H)x]n for polymer (I) x=0.3 and for polymer (II) x=0.8 were prepared by the reaction of poly(anilinophosphazene) [NP(HNC6H5)2]n and sulphonic chloride HSO3Cl in tetrachloroethane solvent several timeS. Also, H protons in the polymer (I) and (II) were prepared from lithum hydroxide in aqueous solution. It was found, by chemical analysis, that the product prepared with (I) and (II) had compositions such as [NP(HNC6H5)1.7 (HNC6H4SO3H)0.1(HNC6H4SO3Li)0.2]n(III) and [NP(HNC6H5)1.2(HN-C6H4SO3Li)0.8]n(IV). Also, the resistivity of products (III) and (IV) were determined and found to be 3.3×107 and 1.5×107 Ωcm−1, respectively.
Similar content being viewed by others
References
P. M. Blonsk and D. F. Shriver, J. Am. Chem. Soc. 106 (1984) 6854.
K. M. Abraham, M Alamgir and S. J. Perrotli, J. Electrochem. Soc. 135 (1988) 535.
H. Saito and M. Kajiwara, Kogyo Kagaku Zasshi. 66 (1963) 61.
M. Kajiwara and K. Shiomoto, Polym Comm. 25 (1983) 93.
T. Hayashi and H. Saito, Bull. Chem. Soc. Jpn. 50 (1977) 1023.
H. R. Allcock and R. L. Kugel, Inorg. Chem., 5 (1966) 1716.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kurachi, Y., Kajiwara, M. Synthesis and properties of poly (organophosphazenes) ionomers [NP(HNC6H5)2−(x+y)(HNC6H4SO3H)x (HNC6H4SO3Li)y]n . J Mater Sci 26, 1799–1802 (1991). https://doi.org/10.1007/BF00543605
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00543605