Preparation of High-Quality Porous Calcium Hexa-Aluminate Ceramics using Salt as Both Reaction Medium and Pore-Former

  • Xueyin Liu
  • Yan-gai Liu
  • Zhaohui Huang
  • Minghao Fang
Research and Development Porous Ceramics
  • 3 Downloads

Abstract

Porous calcium hexa-aluminate (CA6) ceramics were synthesized by a molten salt-mediated technique using CaCO3 and α-Al2O3 powders as the main raw materials. The effects of salt type and content, along with firing temperature on phase formation, microstructural evolution, pore generation and size distribution, and mechanical strength of fired samples were investigated and compared. Among the three tested salts (KCl, NaCl, and CaCl2), KCl showed the best whereas CaCl2 showed the worst accelerating effect on CA6 formation. In the case of the former, phase-pure CA6 was formed after 3 h at 1500 °C, whereas in the case of the latter, CA2 was formed instead as a main phase. The salt not only acted as a reaction medium, accelerating CA6 formation, but also acted as a pore former, creating high levels of porosity in the fired samples. The apparent porosity of the fired samples clearly increased with an increase in KCl content. But the majority of pores were still micron sized and the pore size distribution was relatively narrow. This, along with the possible toughening effect from the well-developed plate-like CA6, conferred relatively high mechanical strength on the final highly porous CA6 ceramics.

Keywords

calcium hexa-aluminate porous ceramics molten salt pore size distribution 

Notes

Acknowledgment

This work was financially supported by the National Natural Science Foundation of China (Grant no. 51032007), the Fundamental Research Funds for the Central Universities (Grant no. 2012067), and the Doctoral Scientific Research Foundation of Quzhou University (Grant no. BSYJ201707).

References

  1. [1]
    Chen, J.H., Chen, H.-y., Yan, M.W., Cao, Z., Mi, W.J.: Formation mechanism of calcium hexaluminate. Int. J. Min. Metall. & Mater. 23 (2016) [10] 1225–1230CrossRefGoogle Scholar
  2. [2]
    de la Iglesia, P.G., García-Moreno, O. Torrecillas,,R., Menéndez, J.L.: Influence of different parameters on calcium hexaluminate reaction sintering by spark plasma. Ceram. Int. 38 (2012) [7] 5325–5332CrossRefGoogle Scholar
  3. [3]
    An, L., Chan, H.M., Soni, K.K.: Control of calcium hexaluminate grain morphology in in-situ toughened ceramic composites. J. Mater. Sci. 31 (1996) [12] 3223–3229CrossRefGoogle Scholar
  4. [4]
    Domínguez, C., Chevalier, J., Torrecillas, R., Fantozzi, G.: Microstructure development in calcium hexaluminate. J. Eur. Ceram. Soc. 21 (2001) [3] 381–387CrossRefGoogle Scholar
  5. [5]
    Domínguez, C., Chevalier, J., Torrecillas, R., Gremillard, L., Fantozzi, G.: Thermomechanical properties and fracture mechanisms of calcium hexaluminate. J. Eur. Ceram. Soc. 21 (2001) [7] 907–917CrossRefGoogle Scholar
  6. [6]
    An, L., Chan, H.M.: R-curve behavior of in-situ-toughened Al2O3:CaAl12O19 ceramic composites. J. Am. Ceram. Soc. 79 (1996) [12] 3142–3148CrossRefGoogle Scholar
  7. [7]
    Vishista, K., Gnanam, F.D., Awaji, H.: Sol-gel synthesis and characterization of alumina-calcium hexaaluminate composites. J. Am. Ceram. Soc. 88 (2005) [5] 1175–1179CrossRefGoogle Scholar
  8. [8]
    Buhr A., Büchel, G., Aroni, J.M., Racher, R.P.: Bonite - a new raw material alternative for refractory innovations. Proc. 47th Int. Colloquium on Refractories (Aachen, Germany) 40 (2006) 205–210Google Scholar
  9. [9]
    Pieta, A., Bucko, M.M., Janus, M. Lis, J., Jonas, S.: Calcium hexaaluminate synthesis and its influence on the properties of CA2-Al2O3-based refractories. J. Eur. Ceram. Soc. 35 (2015) 4567–4571CrossRefGoogle Scholar
  10. [10]
    Ianoş, R., Lazău, I., Păcurariu, C., Barvinschi, P.: Peculiarities of CaO·6Al2O3 formation by using low-temperature combustion synthesis. Eur. J. Inorg. Chem. 6 (2008) 925–930CrossRefGoogle Scholar
  11. [11]
    Chandradass, J., Bae, D.S., Kim, K.H.: Synthesis of calcium hexaaluminate (CaAl12O19) via reverse micelle process. J. Non-Crystall. Sol. 355 (2009) [48–49] 2429–2432CrossRefGoogle Scholar
  12. [12]
    Tulliani, J.M., Pagès, G., Fantozzi, G., Montanaro, L.: Dilatometry as a tool to study a new synthesis for calcium hexaluminate. J. Therm. Analysis & Calorimetry 72 (2003) 1135–1140CrossRefGoogle Scholar
  13. [13]
    Altay, A., Carter, C.B., Arslan, I., Gülgün, M.A.: Crystallization of CaAl4O7 and CaAl12O19 powders. Philos. Mag. 89 (2009) [7] 605–621CrossRefGoogle Scholar
  14. [14]
    Dong, B., Yuan, B., Wang, G., Chen, K., Han, J., Li, H.: Fabrication of porous SiC/Calcium hexaluminate composites. J. Eur. Ceram. Soc. 36 (2016) 3889–3893CrossRefGoogle Scholar
  15. [15]
    Colombo, P.: Conventional and novel processing methods for cellular ceramics. Philos. Trans. Royal Soc. A: Math., Phys. and Eng. Sci. 364 (2006) [1838] 109–124CrossRefGoogle Scholar
  16. [16]
    Peng, H.X., Fan, Z., Evans, J.R.G., Busfield, J.J.C.: Microstructure of ceramic foams. J. Eur. Ceram. Soc. 20 (2000) [7] 807–813CrossRefGoogle Scholar
  17. [17]
    Singh, V., Chakradhar, R.P.S., Rao, J.L., Kim, D.-K.: Photoluminescence and EPR studies of Cr-doped hibonite (CaAl12O19) phosphors. Solid State Sci. 10 (2008) [11] 1525–1532CrossRefGoogle Scholar
  18. [18]
    Nagaoka, T., Tsugoshi, T., Hotta, Y., Yasuoka, M., Watari, K.: Forming and sintering of porous calcium-hexaaluminate ceramics with hydraulic alumina. J. Materials Science 41 (2006) [22] 7401–7405CrossRefGoogle Scholar
  19. [19]
    Salomão, R., Ferreira, V.L., de Oliveira, I.R., Souza, A.D.V., Correr, W.R.: Mechanism of pore generation in calcium hexaluminate (CA6) ceramics formed in situ from calcined alumina and calcium carbonate aggregates. J. Eur. Ceram. Soc. 36 (2016) 4225–4235CrossRefGoogle Scholar
  20. [20]
    Salomão, R., Ferreira, V.L., Costa, L.M.M., de Oliveira, I.R.: Effects of the initial CaO-Al2O3 ratio on the microstructure development and mechanical properties of porous calcium hexaluminate. Ceram. Int. 44 (2018) 2626–2631CrossRefGoogle Scholar
  21. [21]
    Kawaguchia, K., Suzukia, Y., Gotoc, T., Choc, S.H., Sekinoc, T.: Homogeneously bulk porous calcium hexaaluminate (CaAl12O19): Reactive sintering and microstructure development. Ceram. Int. 44 (2018) 4462–4466CrossRefGoogle Scholar
  22. [22]
    Li, Y., Xiang, R., Xu, N., Wang, Q., Li, S., Wu, M., Yang, C.: Fabrication of calcium hexaluminate-based porous ceramic with microsilica addition. Int J Appl Ceram Technol. 15 (2018) 1054–1059CrossRefGoogle Scholar
  23. [23]
    Feng, Y., Wang, K., Yao, J., Webley, P.A., Smart, S., Wang, H.: Effect of the addition of polyvinylpyrrolidone as a pore-former on microstructure and mechanical strength of porous alumina ceramics. Ceram. Int. 39 (2013) [7] 7551–7556CrossRefGoogle Scholar
  24. [24]
    Gregorová, E., Pabst, W.: Process control and optimized preparation of porous alumina ceramics by starch consolidation casting. J. Eur. Ceram. Soc. 31 (2011) [12] 2073–2081CrossRefGoogle Scholar
  25. [25]
    Li, Z., Zhang, S., Lee, W.E.: Molten salt synthesis of LaAlO3 powder at low temperatures. J. Eur. Ceram. Soc. 27 (2007) [10] 3201–3205CrossRefGoogle Scholar
  26. [26]
    Ye, J., Zhang, S., Lee, W.E.: Molten salt synthesis and characterization of SiC coated carbon black particles for refractory castable applications. J. Eur. Ceram. Soc. 33 (2013) [10] 2023–2029CrossRefGoogle Scholar
  27. [27]
    Zhang, S., Jayaseelan, D.D., Bhattacharya, G., Lee, W.E.: Molten Salt Synthesis of magnesium aluminate (MgAl2O4) spinel powder. J. Am. Ceram. Soc. 89 (2006) [5] 1724–1726CrossRefGoogle Scholar
  28. [28]
    Liu, X., Yang, D., Huang, Z., Yi, S., Ding, H., Fang, M., Zhang, S., Liu, Y.-g.: Novel synthesis method and characterization of porous calcium hexaaluminate ceramics. J. Am. Ceram. Soc. 97 (2014) [9] 2702–2704CrossRefGoogle Scholar
  29. [29]
    Wang, S., Zhang, F., Liu, X., Zhang, L.: CaO solubility and activity coefficient in molten salts CaCl2-x (x = 0, NaCl, KCl, SrCl2, BaCl2 and LiCl). Thermochimica Acta 470 (2008) 105–107CrossRefGoogle Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2018

Authors and Affiliations

  • Xueyin Liu
    • 1
  • Yan-gai Liu
    • 2
  • Zhaohui Huang
    • 2
  • Minghao Fang
    • 2
  1. 1.College of Civil Engineering and ArchitectureQuzhou UniversityQuzhou, ZhejiangChina
  2. 2.School of Materials Science and Technology, Beijing Key Laboratory of Materials Utilization of Nonmetallic Minerals and Solid Wastes, National Laboratory of Mineral MaterialsChina University of GeosciencesBeijingChina

Personalised recommendations