Fly Ash Containing Alkali Activated Geopolymer Concrete: Effect of the Na2SiO3:NaOH Ratio and Temperature

  • Ritwik Sarkar
  • S. P. Routray
Applications and Engineering Construction Materials
  • 21 Downloads

Abstract

Geopolymer concrete was prepared using stone chips of various sizes, sand and fly ash, without using any cement. Na2SiO3 and NaOH solutions with three different ratios were used as the alkaline activator for the geopolymer system, and the compositions were studied for density, strength and phase evaluation after ageing and heat treatment at different temperatures up to 90 °C. Sodium aluminium silicate hydrate phase was found to be formed in the compositions as the reaction product of geopolymerization process and is responsible for the strength and density development. The reduction in the hydrated phase content at higher temperatures results in the reduction of density and strength values.

Keywords

geopolymer flyash alkali activator Na2SiO3:NaOH ratio temperature 

References

  1. [1]
    Pacheco-Torgal, F., Castro-Gomes, J., Jalali, S.: Alkali-activated binders: A review? Part 1. Historical background, terminology, reaction mechanisms and hydration products. Constr. and Build. Mater. 22 (2008) 1305–1314CrossRefGoogle Scholar
  2. [2]
    Roy, D.M.: Alkali-activated cements: Opportunities and challenges. Cem. Concr. Res. 29 (1999) 249–254CrossRefGoogle Scholar
  3. [3]
    Palomo, A., Grutzeck, M.W., Blanco, M.T.: Alkali activated fly ashes: A cement for the future. Cem. Concr. Res. 29 (1999) 1323–1329CrossRefGoogle Scholar
  4. [4]
    Duxon, P., Fernández-Jiménez, A., Provis, J.L., Luckey, G.C., Palomo, A., van Deventer, J.S.J.: Geopolymer technology: The current state of the art. J. Mater. Sci. 42 (2007) 2917–2933CrossRefGoogle Scholar
  5. [5]
    Nataraja, M.C., Rajamane, N.P., Lakshmanan, N.: Geopolymer concrete — A new eco-friendly material of construction. J. Eng. Technol. Res. 3 (2011) [1] 1–4Google Scholar
  6. [6]
    Hardjito, D.: Studies on flyash based geopolymer concrete. Ph.D. Thesis, Dept. of Civil Engineering, Curtin University of Technology, Perth, Australia (2005)Google Scholar
  7. [7]
    Rangan, B.V.: lyash based geopolymer concrete. Curtin University of Technology, Perth, Australia Research Report GC 4 Engineering Faculty (2008)Google Scholar
  8. [8]
    Potharaju, M., Ramujee, K.: Development of mix design for low calcium based geopolymer concrete in low, medium and higher grades Indian Scenario. J. Civil Eng. & Technol. 1 (2013) [1] 15–25Google Scholar
  9. [9]
    Kurhade, S.D., Kawade, U.R., Salunkhe, P.A.: Flyash based geopolymer concrete. Int. J. Innovative Res. in Sci. Eng. and Technol. 3 (2014) 4Google Scholar
  10. [10]
    Fernández-Jiménez, A., Palomo, A.: Composition and microstructure of alkali activated fly ash binder: Effect of the activator. Cem. Concr. Res. 35 (2005) 1984–1992CrossRefGoogle Scholar
  11. [11]
    Rangan B.V.: Fly ash-based geopolymer concrete. Res. Report GC 4, Faculty of Engineering, Curtin University of Technology, Perth, Australia (2008)Google Scholar
  12. [12]
    Rattanasak, U., Chindaprasirt, P.: Influence of NaOH solution on the synthesis of fly ash geopolymer. Min. Eng. 22 (2009) 1073–1078CrossRefGoogle Scholar
  13. [13]
    Duchesne, J., Duong, L., Bostrom, T., Frost, R.: Microstructure study of early in situ reaction of fly ash geopolymer observed by environmental scanning electron microscopy (ESEM). Waste Biomass Valor. 1 (2010) 367–377CrossRefGoogle Scholar
  14. [14]
    Palomo, A., Grutzeck, M.W., Blanco, M.T.: Alkali-activated fly ashes: A cement for the future. Cem. Concr. Res. 29 (1999) 1323–1329CrossRefGoogle Scholar
  15. [15]
    Xu, H., van Deventer, J.S.J.: Ab initio calculations on the five-membered aluminosilicate framework rings model: Implications for dissolution in alkaline solutions. Comp. and Chem. 24 (2000) 391–404CrossRefGoogle Scholar
  16. [16]
    Tempest, B., Sanusi, O., Gergely, J., Ogunro, V., Weggel, D.: Compressive strength and embodied energy optimization of fly ash based geopolymer concrete. World of Coal Ash Conf., Lexington, KY, USA. Ed., (2009) 1–17Google Scholar
  17. [17]
    Chindaprasirt, P., Chareerat, T., Sirivivatnanon, V.: Workability and strength of coarse high calcium fly ash geopolymer. Cem. Concr. Compos. 29 (2007) 224–229CrossRefGoogle Scholar
  18. [18]
    Fernández-Jiménez, A., Palomo, A.: Characterization of fly ashes. Potential reactivity as alkaline cements. Fuel 82 (2003) 2259–2265Google Scholar
  19. [19]
    Temuujin, J., van Riessen, A.: Effect of fly ash preliminary calcination on the properties of geopolymer. J. Hazard. Mater. 164 (2009) 634–639CrossRefGoogle Scholar
  20. [20]
    Jones, M.R., McCarthy, A., Booth, A.P.P.G.: Characteristics of the ultrafine component of fly ash. Fuel 85 (2006) 2250–2259CrossRefGoogle Scholar
  21. [21]
    Ward, C.R., French, D.: Determination of glass content and estimation of glass composition in fly ash using quantitative X-ray diffractometry. Fuel 85 (2006) 2268–2277CrossRefGoogle Scholar
  22. [22]
    Kovalchuk, G Fernández-Jiménez, A., Palomo, A.: Alkali-activated fly ash: Effect of thermal curing conditions on mechanical and microstructural development 3—Part II. Fuel 86 (2007) 315–322CrossRefGoogle Scholar

Copyright information

© Springer Fachmedien Wiesbaden GmbH, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Department of Ceramic EngineeringNational Institute of TechnologyRourkelaIndia

Personalised recommendations