Effects of surface pretreatments and coating period on hydroxyapatite coating of Ti6Al4V alloy

  • T. Hacioglu
  • Z. EvisEmail author
  • A. Tezcaner
  • M. K. Aydınol
Research
  • 8 Downloads

Abstract

In this study, Ti6Al4V plates were gone through three steps of pretreatment process (sandblasting + acid etching + preheating) followed by biomimetic coating of pure hydroxyapatites (HAp) on pretreated substrate. Pretreated substrates were examined by SEM, EDS, AFM, FTIR, and XRD; meanwhile, prepared coatings were examined by SEM, EDS, FTIR, XRD, XPS, scratch test, and in vitro cell studies (SaOS-2 cell line). Prepared coatings were also investigated in terms of antibacterial property by determining the survival of the Staphylococcus epidermidis on the surface. Structural analysis results of pretreated substrates proved that surface roughness increased proportionally as sandblasting, acid etching, and preheating process were performed. Successively, surface became more porous according to SEM images which were also supported by AFM results that indicate that Ra increased up to 953 nm values. EDS and FTIR spectra showed that functional groups were formed with the pretreatment procedure. Especially titanium salts were formed during acid etching process while preheating caused oxidation. XRD spectra revealed that as-received substrates mostly consisted of α-Ti, acid etching resulted in formation of TiH2 structure and oxidation resulted to form rutile and anatase structure patterns. Pretreatment procedure had positive effect on biomimetic coatings according to the evaluation of structural, mechanical, and biological properties. SEM analysis revealed that HAp nucleation started 4 days after immersion and nucleation increased with the incubation time. EDS results indicated that maximum Ca/P ratio (1.48) was achieved by P14. FTIR, XRD, and XPS analysis proved the presence of hydroxyapatite on the substrate surface. The pretreatment procedure had significant influence on mechanical properties of the coatings resulting in increase of critical loads. P14 sample had the highest critical load. In terms of biological evaluation, P14 exhibited the highest cell proliferation and lowest bacterial adhesion. The highest stability and coherence of P14 coating was also confirmed by mechanical test results. Eventually, it was observed that pretreatment technique has great effect on surface properties. In addition, 14 days immersion period was found to be optimum along the investigated immersion times.

Keywords

Sand blasting Acid etching Preheating Hydroxyapatite Ti6Al4V 

Notes

References

  1. 1.
    Chen, W., Liu, Y., Courtney, H.S., Bettenga, M., Agrawal, C.M., Bumgardner, J.D., Ong, J.L.: In vitro anti-bacterial and biological properties of magnetron co-sputtered silver-containing hydroxyapatite coating. Biomater. 27, 5512–5517 (2006)CrossRefGoogle Scholar
  2. 2.
    Dobzyniak, M., Fehring, T.K., Odum, S.: Early failure in total hip arthroplasty. Clin. Orthop. Relat. Res. 447, 76–78 (2006)CrossRefGoogle Scholar
  3. 3.
    Losina, E., Barrett, J., Mahomed, N.N., Baron, J.A., Katz, J.N.: Early failures of total hip replacement: effect of surgeon volume. Arthritis Rheum. 50, 1338–1343 (2004)CrossRefGoogle Scholar
  4. 4.
    Long, M., Rack, H.J.: Titanium alloys in total joint replacement-a materials science perspective. Biomater. 19, 1621–1639 (1998)CrossRefGoogle Scholar
  5. 5.
    Xu, S., Xiaoyu, Y., Yuan, S., Minhua, T., Jian, L., Aidi, N., Xing, L.: Morphology improvement of sandblasted and acid-etched titanium surface and osteoblast attachment promotion by hydroxyapatite coating. Rare Metal Mater. Eng. 44, 67–72 (2015)CrossRefGoogle Scholar
  6. 6.
    Fujibayashi, S., Neo, M., Kim, H.M., Kokubo, T., Nakamura, T.: Osteoinduction of porous bioactive titanium metal. Biomater. 25, 443–450 (2004)CrossRefGoogle Scholar
  7. 7.
    Kokubo, T., Yamaguchi, S.: Novel bioactive materials developed by simulated body fluid evaluation: surface-modified Ti metal and its alloys. Acta Biomater. 44, 16–30 (2016)CrossRefGoogle Scholar
  8. 8.
    Liu, X., Chu, P.K., Ding, C.: Surface modification of titanium, titanium alloys, and related materials for biomedical applications. Mater. Sci. Eng. R. Rep. 47, 49–121 (2004)CrossRefGoogle Scholar
  9. 9.
    Liu, Y., Jiang, T., Zhou, Y., Zhang, Z., Wang, Z., Tong, H., Shen, X., Wang, Y.: Evaluation of the attachment, proliferation, and differentiation of osteoblast on a calcium carbonate coating on titanium surface. Mater. Sci. Eng. C. 31, 1055–1061 (2011)CrossRefGoogle Scholar
  10. 10.
    Yanovska, A., Kuznetsov, V., Stanislavov, A., Danilchenko, S., Sukhodub, L.: Synthesis and characterization of hydroxyapatite-based coatings for medical implants obtained on chemically modified Ti6Al4V substrates. Surf. Coat. Technol. 205, 5324–5329 (2011)CrossRefGoogle Scholar
  11. 11.
    An, S.H., Matsumoto, T., Miyajima, H., Sasaki, J.I., Narayanan, R., Kim, K.H.: Surface characterization of alkali- and heat-treated Ti with or without prior acid etching. Appl. Surf. Sci. 258, 4377–4382 (2012)CrossRefGoogle Scholar
  12. 12.
    Chen, J.C., Ko, C.L., Lin, D.J., Wu, H.Y., Hung, C.C., Chen, W.C.: In vivo studies of titanium implant surface treatment by sandblasted, acid-etched and further anchored with ceramic of tetracalcium phosphate on osseointegration. J. Aust. Ceram. Soc. (2019).  https://doi.org/10.1007/s41779-018-00292-5
  13. 13.
    Deng, F., Zhang, W., Zhang, P., Liu, C., Ling, J.: Improvement in the morphology of micro-arc oxidised titanium surfaces: a new process to increase osteoblast response. Mater. Sci. Eng. C. 30, 141–147 (2010)CrossRefGoogle Scholar
  14. 14.
    Ban, S., Iwaya, Y., Kono, H., Sato, H.: Surface modification of titanium by etching in concentrated sulfuric acid. Dent. Mater. 22, 1115–1120 (2006)CrossRefGoogle Scholar
  15. 15.
    Turk, S., Altınsoy, I., Çelebi, G.E., Ipek, M., Ozacar, M., Bindal, C.: A comparison of pretreatments on hydroxyapatite formation on Ti by biomimetic method. J. Aust. Ceram. Soc. 54, 533–543 (2018)CrossRefGoogle Scholar
  16. 16.
    Kokubo, T., Takadama, H.: How useful is SBF in predicting in vivo bone bioactivity? Biomater. 27, 2907–2915 (2006)CrossRefGoogle Scholar
  17. 17.
    Ohtsu, N., Kakuchi, Y., Ohtsuki, T.: Antibacterial effect of zinc oxide/hydroxyapatite coatings prepared by chemical solution deposition. Appl. Surf. Sci. 445, 596–600 (2017)CrossRefGoogle Scholar
  18. 18.
    Yang, A., Han, Y., Pan, Y., Xing, H., Li, J.: Optimum surface roughness prediction for titanium alloy by adopting response surface methodology. Results Phys. 7, 1046–1050 (2017)CrossRefGoogle Scholar
  19. 19.
    Henriques, B., Sampaio, M., Buciumeanu, M., Souza, J.C.M., Gomes, J.R., Silva, F., Carvalho, O.: Laser surface structuring of Ti6Al4V substrates for adhesion enhancement in Ti6Al4V-PEEK joints. Mater. Sci. Eng. C. 79, 177–184 (2017)CrossRefGoogle Scholar
  20. 20.
    Baek, S.M., Polyakov, A.V., Moon, J.H., Semenova, I.P., Valiev, R.Z., Kim, H.S.: Effect of surface etching on the tensile behavior of coarse- and ultrafine-grained pure titanium. Mater. Sci. Eng. A. 707, 337–343 (2017)CrossRefGoogle Scholar
  21. 21.
    Hatamleh, M.M., Wu, X., Alnazzawi, A., Watson, J., Watts, D.: Surface characteristics and biocompatibility of cranioplasty titanium implants following different surface treatments. Dent. Mater. 34, 676–683 (2018)CrossRefGoogle Scholar
  22. 22.
    Li, B., Li, J., Liang, C., Li, H., Guo, L., Liu, S., Wang, H.: Surface roughness and hydrophilicity of titanium after anodic oxidation. Rare Metal Mater. Eng. 45, 858–862 (2016)CrossRefGoogle Scholar
  23. 23.
    Shokri, B., Firouzjah, M.A., Hosseini, S.I.: FTIR analysis of silicon dioxide thin film deposited by metal organic-based PECVD. Proc. 19th Int. Plasma Chem Soc, pp. 1–4 (2009)Google Scholar
  24. 24.
    Givan, A., Grothe, H., Loewenschuss, A., Nielsen, C.J.: Infrared spectra and ab initio calculations of matrix isolated dimethyl sulfone and its water complex. Phys. Chem. Chem. Phys. 4, 255–263 (2002)CrossRefGoogle Scholar
  25. 25.
    Hamadanian, M., Reisi-Vanani, A., Majedi, A.: Sol-gel preparation and characterization of co/TiO2 nanoparticles: application to the degradation of methyl orange. J. Iran. Chem. Soc. 7, 52–58 (2010)CrossRefGoogle Scholar
  26. 26.
    Infrared Spectroscopy Absorption Table-Chemistry LibreTexts. https://chem.libretexts.org/Reference/Reference_Tables/Spectroscopic_Parameters/Infrared_Spectroscopy_Absorption_Table. Accessed 17 March 2018
  27. 27.
    Yilmaz, B., Evis, Z., Güldiken, M.: Titanyum Alaşımının Biyomimetik Yöntemle Kalsiyum Fosfat Kaplanması. J. Fac. Eng. Archit. Gazi Univ. 29, 105–109 (2014)Google Scholar
  28. 28.
    Teker, D., Muhaffel, F., Menekse, M., Karaguler, N.G., Baydogan, M., Cimenoglu, H.: Characteristics of multi-layer coating formed on commercially pure titanium for biomedical applications. Mater. Sci. Eng. C. 48, 579–585 (2015)CrossRefGoogle Scholar
  29. 29.
    Liu, D.M., Troczynski, T., Tseng, W.J.: Water-based sol-gel synthesis of hydroxyapatite: process development. Biomater. 22, 1721–1730 (2001)CrossRefGoogle Scholar
  30. 30.
    Avci, M., Yilmaz, B., Tezcaner, A., Evis, Z.: Strontium doped hydroxyapatite biomimetic coatings on Ti6Al4V plates. Ceram. Int. 43, 9431–9436 (2017)CrossRefGoogle Scholar
  31. 31.
    Silva, C.C., Pinheiro, A.G., Miranda, M.A.R., Góes, J.C., Sombra, A.S.B.: Structural properties of hydroxyapatite obtained by mechanosynthesis. Solid State Sci. 5, 553–558 (2003)CrossRefGoogle Scholar
  32. 32.
    Pylypchuk, I.V., Gorbyk, P.P., Petranovska, A.L., Korduban, O.M., Markovsky, P.E., Ivasyshyn, O.M.: Chapter 7 - Formation of Biomimetic Hydroxyapatite Coatings on the Surface of Titanium and Ti-Containing Alloys: Ti-6Al-4V and Ti-Zr-Nb. Appl. Nanobiomater. 3, 193–229 (2016)Google Scholar
  33. 33.
    Durdu, S., Usta, M., Berkem, A.S.: Bioactive coatings on Ti6Al4V alloy formed by plasma electrolytic oxidation. Surf. Coat. Technol. 301, 85–93 (2016)CrossRefGoogle Scholar
  34. 34.
    Al-Hazmi, F.E.: Synthesis and electrical properties of Bi doped hydroxyapatite ceramics. J. Alloys Compd. 665, 119–123 (2016)CrossRefGoogle Scholar
  35. 35.
    Wang, H.Y., Zhu, R.F., Lu, Y.P., Xiao, G.Y., He, K., Yuan, Y.F., Ma, X.N., Li, Y.: Effect of sandblasting intensity on microstructures and properties of pure titanium micro-arc oxidation coatings in an optimized composite technique. Appl. Surf. Sci. 292, 204–212 (2014)CrossRefGoogle Scholar
  36. 36.
    Sumathi, S., Buvaneswari, G.: Synthesis of apatite structure based BiNaCa3(PO4)3OH and its application for condensation reaction. Ceram. Int. 38, 3547–3552 (2012)CrossRefGoogle Scholar
  37. 37.
    Cochis, A., Azzimonti, B., Valle, C.D., De Giglio, E., Bloise, N., Visai, L., Cometa, S., Rimondini, L., Chiesa, R.: The effect of silver or gallium doped titanium against the multidrug resistant Acinetobacter baumannii. Biomater. 80, 80–95 (2016)CrossRefGoogle Scholar
  38. 38.
    Forsgren, J., Svahn, F., Jarmar, T., Engqvist, H.: Formation and adhesion of biomimetic hydroxyapatite deposited on titanium substrates. Acta Biomater. 3, 980–984 (2007)CrossRefGoogle Scholar
  39. 39.
    Yilmaz, B., Evis, Z., Tezcaner, A., Banerjee, S.: Surface characterization and biocompatibility of selenium-doped hydroxyapatite coating on titanium alloy. Int. J. Appl. Ceram. Technol. 13, 1059–1068 (2016)CrossRefGoogle Scholar
  40. 40.
    Andrukhov, O., Huber, R., Shi, B., Berner, S., Rausch-Fan, X., Moritz, A., Spencer, N.D., Schedle, A.: Proliferation, behavior, and differentiation of osteoblasts on surfaces of different microroughness. Dent. Mater. 32, 1374–1384 (2016)CrossRefGoogle Scholar
  41. 41.
    Rupp, F., Liang, L., Geis-Gerstorfer, J., Scheideler, L., Hüttig, F.: Surface characteristics of dental implants: a review. Dent. Mater. 34, 40–57 (2018)CrossRefGoogle Scholar
  42. 42.
    Yilmaz, B., Alshemary, A.Z., Evis, Z.: Co-doped hydroxyapatites as potential materials for biomedical applications. Microchem. J. 144, 443–453 (2019)CrossRefGoogle Scholar

Copyright information

© Australian Ceramic Society 2019

Authors and Affiliations

  • T. Hacioglu
    • 1
  • Z. Evis
    • 1
    • 2
    Email author
  • A. Tezcaner
    • 2
  • M. K. Aydınol
    • 1
    • 3
  1. 1.Department of Micro and Nano TechnologyMiddle East Technical UniversityAnkaraTurkey
  2. 2.Department of Engineering SciencesMiddle East Technical UniversityAnkaraTurkey
  3. 3.Department of Metallurgical and Materials EngineeringMiddle East Technical UniversityAnkaraTurkey

Personalised recommendations