, Volume 16, Issue 1, pp 46–52 | Cite as

Single and double aging treatments on Mg97Zn1Y2 alloy

  • Di-qing WanEmail author
  • Ying-lin Hu
  • Hou-bin Wang
  • Shu-ting Ye
Research & Development
  • 6 Downloads

Abstract

The development of magnesium alloys was limited due to the low absolute strength and poor corrosion resistance. It was found that the optimal performance could not be achieved in some alloys by a single quenching and aging treatment, but could be achieved after a graded aging or multiple-stage aging heat treatment. The Mg97Zn1Y2 alloy was prepared and subjected to single and double aging treatments. Single aging was carried out at 250 ºC for 6 to 15 h. For double aging, the first step was performed the same as the single aging. The second step was performed at 350 ºC for 12 h. The microstructure and properties of the alloy with single and double aging were analyzed by means of hardness measurement, optical microscopy, scanning electron microscopy, X-ray diffraction, and polarization curve measurements. Results show that the precipitated nanoscale phases are formed during aging, and evenly distributed in the matrix. Compared with the single aging treatment, the hardness and corrosion resistance of the alloy are further improved due to the double aging treatment.

Key words

single aging double aging Mg97Zn1Y2 alloy LPSO phase 

CLC numbers

TG146.22 

Document code

References

  1. [1]
    Ando D, Sutou Y, Koike J. Internal microstructure observation of enhanced grain-boundary sliding at room temperature in AZ31 magnesium alloy. Materials Science and Engineering: A, 2016, 666: 94–99.CrossRefGoogle Scholar
  2. [2]
    Rashad M, Pan F S, Lin D, et al. High temperature mechanical behavior of AZ61 magnesium alloy reinforced with graphene nanoplatelets. Materials & Design, 2016, 89: 1242–1250.CrossRefGoogle Scholar
  3. [3]
    Feng H, Liu H P, Cao H, et al. Effect of precipitates on mechanical and damping properties of Mg-Zn-Y-Nd alloys. Materials Science and Engineering: A, 2015, 639: 1–7.CrossRefGoogle Scholar
  4. [4]
    Nagaraj M Chelliah, Ram Kumar, Harpreet Singh, et al. Microstructural evolution of die-cast and homogenized AZ91 Mg-alloys during dry sliding condition. Journal of Magnesium and Alloys, 2017, 5: 35–40.CrossRefGoogle Scholar
  5. [5]
    Mironov S, Onuma T, Sato Y S. Microstructure evolution during friction-stir welding of AZ31 magnesium alloy. Acta Materialia, 2015, 100: 301–312.CrossRefGoogle Scholar
  6. [6]
    Li C Q, Xu D K, Zeng Z R, et al. Effect of volume fraction of LPSO phases on corrosion and mechanical properties of Mg-Zn-Y alloys. Materials & Design, 2017, 121: 430–441.CrossRefGoogle Scholar
  7. [7]
    Miao H W, Huang H, Shi Y J, et al. Effects of solution treatment before extrusion on the microstructure, mechanical properties and corrosion of Mg-Zn-Gd alloy in vitro. Corrosion Science, 2017, 122: 90–99.CrossRefGoogle Scholar
  8. [8]
    Srinivasan A, Huang Y, Mendis C L, et al. Investigations on microstructures, mechanical and corrosion properties of Mg-Gd-Zn alloys. Materials Science and Engineering: A, 2014, 595: 224–234.CrossRefGoogle Scholar
  9. [9]
    Wang S D, Xu D K, Chen X B, et al. Effect of heat treatment on the corrosion resistance and mechanical properties of an asforged Mg-Zn-Y-Zr alloy. Corrosion Science, 2015, 92: 228–236.CrossRefGoogle Scholar
  10. [10]
    Mousavi Anijdan S H, Kang D, Singh N, et al. Precipitation behavior of strip cast Al-Mg-0.4Sc-0.15Zr alloy under single and multiple-stage aging processes. Materials Science and Engineering: A, 2015, 640: 275–279.CrossRefGoogle Scholar
  11. [11]
    Santhosh R, Geetha M, Saxena V K, et al. Studies on single and duplex aging of metastable beta titanium alloy Ti-15V-3Cr-3Al-3Sn. Journal of Alloys and Compounds, 2014, 605: 222–229.CrossRefGoogle Scholar
  12. [12]
    Oh-ishi K, Hono K, Shin K S. Effect of pre-aging and Al addition on age-hardening and microstructure in Mg-6wt% Zn alloys. Materials Science and Engineering A, 2008, 496 (1/2): 425–433.CrossRefGoogle Scholar
  13. [13]
    Wang Y, Dai S, Chen F, et al. Influence of single and double aging treatment on microstructures and mechanical properties of cold rolled Ti-30Nb-5Ta-6Zr alloy. Materials Science and Technology, 2014, 30: 189–195.CrossRefGoogle Scholar
  14. [14]
    Zhu S Z, Luo T J, Yang Y S. Improving mechanical properties of age-hardenable Mg-6Zn-4Al-1Sn alloy processed by doubleaging treatment. Journal of Materials Science & Technology, 2017, 11: 1–15.Google Scholar
  15. [15]
    Xu C, Zheng M Y, Xu S W, et al. Improving strength and ductility of Mg-Gd-Y-Zn-Zr alloy simultaneously via extrusion, hot rolling and ageing. Materials Science and Engineering: A, 2015, 643: 137–141.CrossRefGoogle Scholar
  16. [16]
    Fang Xiaogang, Wu Shusen, Lv Shuli, et al. Microstructure evolution and mechanical properties of quasicrystal-reinforced Mg-Zn-Y alloy subjected to ultrasonic vibration. Materials Science and Engineering: A, 2017, 679: 372–378.CrossRefGoogle Scholar
  17. [17]
    Kawamura Y, Kasahara T, Izumi S, et al. Elevated temperature Mg97Y2Cu1 alloy with long period ordered microstructure. Scripta Materialia, 2006, 55: 453–456.CrossRefGoogle Scholar
  18. [18]
    Hagihara K, Kinoshita A, Fukusumi Y, et al. High-temperature compressive deformation behavior of Mg97Zn1Y2 extruded alloy containing a long-period stacking ordered (LPSO) phase. Materials Science and Engineering: A, 2013, 560: 71–79.CrossRefGoogle Scholar
  19. [19]
    Hagihara K, Kinoshita A, Sugino Y, et al. Effect of longperiod stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy. Acta Materialia, 2010, 58(19): 6282–6293.CrossRefGoogle Scholar
  20. [20]
    Hagihara K, Kinoshita A, Fukusumi Y, et al. High-temperature compressive deformation behavior of Mg97Zn1Y2 extruded alloy containing a long-period stacking ordered (LPSO) phase. Materials Science and Engineering: A, 2013, 560: 71–79.CrossRefGoogle Scholar
  21. [21]
    Jin Q Q, Shao X H, Hu X B, et al. New polytypes of long-period stacking ordered structures in a near-equilibrium Mg97Zn1Y2 alloy. Philosophical Magazine Letters, 2017, 97: 180–187.CrossRefGoogle Scholar
  22. [22]
    Wan Diqing, Li Zhumin, Zhou Xinjian. Microstructure and Damping of Mg97Zn1Y2 Alloy with or without Solid Solution Treatment. Rare Metal Materials and Engineering, 2016, 45: 1245–1248. (In Chinese)Google Scholar
  23. [23]
    Mitsuhiro O, Shuhei T, Masafumi M, et al. Mechanical properties and failure characteristics of cast and extruded Mg97Y2Zn1 alloys with LPSO phase. Materials Science and Engineering: A, 2016, 652: 14–29.CrossRefGoogle Scholar
  24. [24]
    Zhu Y M, Morton A J, Nie J F. The 18R and 14H long-period stacking ordered structures in Mg-Y-Zn alloys. Acta Materialia, 2010, 58(8): 2936–2947.CrossRefGoogle Scholar
  25. [25]
    Gröbner J, Kozlov A, Fang X Y, et al. Phase equilibria and transformations in ternary Mg-rich Mg-Y-Zn alloys. Acta Materialia, 2012, 60(17): 5948–5962.CrossRefGoogle Scholar

Copyright information

© Foundry Journal Agency and Springer Nature Singapore Pte Ltd. 2019

Authors and Affiliations

  • Di-qing Wan
    • 1
    Email author
  • Ying-lin Hu
    • 1
  • Hou-bin Wang
    • 1
  • Shu-ting Ye
    • 1
  1. 1.School of Material Science and EngineeringEast China Jiaotong UniversityNanchangChina

Personalised recommendations