Effect of Firing Temperature and Time on Hybrid Fiber-Reinforced Shell for Investment Casting
- 25 Downloads
Glass fiber combined with aluminum silicate fiber was mixed into the slurry for preparing fiber-reinforced shell. The fired bending strength, the self-load deformation at elevated temperature and the permeability of hybrid fiber-reinforced shells were investigated. Combining with the fracture morphology of reinforced shell by SEM, the properties of hybrid fiber-reinforced shell were investigated. The results show that the fired bending strength of shell first increases and then decreases with variation of the firing temperature from 900 to 1000 °C and reaches the maximum of 4.12 MPa with firing temperature of 950 °C. Comparison of firing time, the maximum fired bending strength was obtained when firing time was 120 min. The self-loaded deformation at elevated temperature decreases with 0.5 wt% fiber addition. The permeability increases with fiber reinforcement. It is found by SEM that the bending load was borne by deformation and fracture of aluminum silicate fiber, and the glass fiber melt transformed into globular fiber due to the heat deformation at high temperatures which would decrease the strength.
Keywordsceramic matrix composites fracture investment casting fiber strength
This project is supported by National Natural Science Foundation of China (Grant No. 51865042), National Natural Science Foundation of Inner Mongolia (Grant No. 2018MS05051) and Science Foundation for Universities in Inner Mongolia Autonomous Region of China (Grant No. NJZZ17080).
- 8.S.C. Luis, H.P.C. Sergio, G. Chris, A. Antonio, A. Simon, Fibre distribution and tensile response anisotropy in sprayed fibre reinforced concrete. Mater. Struct. 51(29), 12 (2018)Google Scholar
- 12.D.H. Lu, Z. Wang, Y.H. Jiang, R. Zhou, Effect of aluminium silicate fiber modification on crack-resistance of a ceramic mould. China Foundry 9, 322–327 (2012)Google Scholar