Effect of Vanadium and Zirconium Additions on Mechanical Properties and Microstructure of Gravity Die-Cast AlSi9Cu2 Alloy Cylinder Heads
- 97 Downloads
Systematic work was performed in the present study to investigate the effect of V and Zr additions on microstructural evolution and mechanical properties of the gravity die-cast AlSi9Cu2 alloy in T6 temper. The equiaxed dendritic structure typical of AlSi9Cu2 alloy is replaced by a much finer columnar dendritic network when modified with V and Zr additions. This remarkable structural refinement is believed to be linked with the formation of the V- and Zr-containing phases that form during solidification. The co-addition of V and Zr affects the tensile properties and hardness more significantly than individual additions. While the increase in strength is accompanied by a decrease in elongation, the penalty to be paid, particularly in the case of co-addition of V and Zr, is rather small and thus could be tolerated for the superior strength in some applications.
Keywordsaluminium alloys automotive microstructure mechanical properties
It is a great pleasure to thank Kent Jiang, Yinxia Song, Yinz Hongli, Erkan Ertan (Chongqing QIN’AN Foundry Co. Ltd.) for their help with the experiments.
- 5.R. Molina, P. Amalberto, M. Rosso, Mechanical characterization of aluminium alloys for high temperature applications, part 1: Al–Si–Cu alloys. Metall. Sci. Technol. 29, 5–15 (2011)Google Scholar
- 6.M. Garat, G. Laslaz, Improved aluminum alloys for common rail diesel cylinder heads. AFS Trans. 115, 89–96 (2007)Google Scholar
- 8.H.S.S. Seoul, G.D.K. Gyeonggi-do, US Patent, 2012/0275949 A1 Nov. 22 (2012)Google Scholar
- 15.W. Kasprzak, Z. Deng, J. Powell and M. Niewczas, Aging characteristics, dimensional stability and assessment of high temperature performance of cast Al–Si alloy for power train applications, in 12th International Conference on Aluminum Alloys, Yokohama, Japan (2010)Google Scholar
- 22.G. Laslaz, US Patent, 0133949 Al, June 22 (2006)Google Scholar
- 23.K.E. Knipling, D.C. Dunand, D.N. Seidman, Criteria for developing castable, creep-resistant aluminum-based alloys—a review. Int. J. Mater. Res. 97, 246–265 (2006)Google Scholar
- 34.F. Czerwinski, S.K. Shaha, W. Kasprzak, J. Friedman, D.L. Chen, Aging characteristics of the Al-Si-Cu-Mg cast alloy modified with transition metals Zr, V and Ti, in 4th International Conference on Advances in Solidification Processes (ICASP-4), IOP Conference. Series: Materials Science and Engineering, vol. 117, p. 012031 (2016)Google Scholar