Effects of Microstructure on the Dynamic Strain Aging in Ferritic-Pearlitic Steels
- 48 Downloads
Effects of microstructure on the high strain rate high temperature mechanical response and dynamic strain aging of C45 and 27MnCr5 ferritic-pearlitic steels were studied using four different microstructural variants of the standard alloys. The high strain rate high temperature behavior of the steels was studied using a compression Split Hopkinson Pressure Bar device with high temperature testing capabilities. The steels were studied at strain rates up to 4500 s−1 and at temperatures from RT to 680 °C. Strong dynamic strain aging was observed for both steels in the studied temperature range. The results also show that the microstructure has a strong effect on the dynamic strain aging sensitivity of the steel. This is especially true at low plastic strains, where the effect of the microstructure is strongest. The effect of microstructure decreases as plastic strain increases. A coarse-grained microstructure showed the strongest dynamic strain aging sensitivity for both steels.
KeywordsHigh temperature High strain rate Dynamic strain aging Steels Effects of microstructure
The funding by the European Research Fund for Coal and Steel in the frame of the research project RFSR-CT-2014-00020 (IMMAC) is gratefully acknowledged.
- 1.Portevin A, Le-Chatelier H (1924) Heat treatment of aluminum–copper alloys. Trans Am Soc Steel Treat 52:457–478Google Scholar
- 9.Baird J, Jamieson A (1966) Effects of manganese and nitrogen on the tensile properties of iron in the range of 20–600 centigrades. J Iron Steel Inst 204:793–803Google Scholar
- 19.Baird J (1971) Effects of strain aging due to interstitial solutes on the mechanical properties of metals. Metall Rew 149:1–18Google Scholar
- 29.Apostol M (2007) Strain rate and temperature dependence of the compression behavior of FCC and BCC metals. Development of experimental techniques and their application to material modeling. Ph.D. thesis. Tampere University of TechnologyGoogle Scholar