Application of Laser Radiation for Intensification of Chemical Heat Treatment

  • Walid AlnusiratEmail author
Original Research
  • 6 Downloads

Abstract

The processes of chemical heat treatment were analyzed. The areas of their application, productivity, energy intensity, advantages and disadvantages are highlighted. The surface nitrided layers with hardness up to 800–900 HV were obtained. In this case, nitriding thickness does not exceed 0.15–0.2 mm, which is insufficient, especially if the value of residual deformations exceeds the thickness of the diffusion layer. It is shown that to increase the efficiency of nitriding, it is advisable to pre-modify the microstructure of the layer of the sample by laser irradiation. Modeling of thermal processes occurring in steels under irradiation and experimental studies have determined the conditions under which highly dispersed, with a high dislocation density, disoriented in space structures are formed in the surface layers. Dislocations, located on the grain boundaries and having a complex configuration, form paths along which nitrogen atoms can move, forming nitrides with alloy elements. It was shown that in U8 tool carbon steel (AISI M2) after laser treatment and subsequent nitriding in ammonia at a temperature of 780–800 °К for 12 h, a nitrided layer is formed. The depth of the nitrided layer without prior laser treatment is 0.115 mm, on laser-treated it varies within 0.12–0.46 mm depending on the processing speed. The results of the combined nitriding of 40Cr13 stainless steels (AISI 420 Stainless Steel) and 12Cr18Ni10Ti (AISI 321 Stainless Steel), in which the thickness of the hardened layer with a hardness of 815.7–917.7 HV is 0.4–0.5 mm, with a significantly shorter (by 3–5 times) process time and its cost, are presented. The expediency of manufacturing discretely located nitrided zones on the working surfaces of products is discussed.

Keywords

Chemical heat treatment Nitriding Laser irradiation Surface treatment Dislocations Structure Dispersion Wear resistance 

Notes

References

  1. 1.
    Gerasimov S. А., Kuksenova L. I., Lapteva V. G. (2014). Structure and wear resistance of nitrided structural steels and alloys. 2nd ed. publishing house of Moscow state Technical University. N.E. Bauman, Moscow, 518Google Scholar
  2. 2.
    Beliy, A.V., Kalinichenko, A.S., Devoyno, O.G., Kukareko, V.A.: Engineering of surfaces of construction materials using plasma and beam technologies. Belarusian science, Minsk. 457, (2017)Google Scholar
  3. 3.
    Belashova, I.S., Shashkov, D.P.: Influence of thermogasocyclic effects on the process of nitriding. Metal technology. 11, 48–56 (2003)Google Scholar
  4. 4.
    Hertsriken D.S., Mazanko V.F., Falchenko V.M. (1991). Pulsed treatment and mass transfer in metals at low temperatures. Naukova Dumka, Kyiv, 208Google Scholar
  5. 5.
    Pereloma, V.A., Likhoshva, V.P., Sementsev, A.M., Shevchenko, A.G.: Non-metallic inclusions in the zone of laser exposure to steel. News of universities Metals. 2, 139–142 (1997)Google Scholar
  6. 6.
    Holovko, L.F., Luk’yanenko, S.O.: Laser technology and computer models. Viska, Kyiv. 296, (2009)Google Scholar
  7. 7.
    Zenker, R., Spies, H.-J., Buchwalder, A., Sacher, G.: Combination of high-energy beam treatment: state of art. International heat treatment and surface engineering, Vol. 1. I. 4, 152–155 (2007)Google Scholar
  8. 8.
    Speidel A., Lutey A. H. A., Mitchell-Smith J., Rance G. A., Liverani E., Ascari A., Fortunato A. Clare A., (2016). Surface modification of mild steel using a combination of laser and electrochemical processes. Surf. Coatings Technol., vol. 307, 849–860,Google Scholar
  9. 9.
    Ischuk N.V., Pisarenko V.M., Kindrachuk M.V., Holovko L.F. (2006). Pat. No 19551 UA. Method for combined laser -chemico-thermal treatment of materials. МPK: C23C 8/02. No. u200607450; declareted: 04.07.2006; published: 15.12.2006, Bul. No.12Google Scholar
  10. 10.
    Golovko L.F., Luk’yanenko S.O., Goroshko I.O., Mit'ko L.O. (2006). Mathematical modeling by adaptive method of temperature fields at laser processing of materials. Modeling and information technologies: collection of scientific works of the Institute of Modeling Problems in power engineering of the National Academy of Sciences of Ukraine, Vol. 38 Kyiv, 142-150Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Maan University CollegeMaanJordan
  2. 2.Al-Balqa Applied UniversityAmmanJordan

Personalised recommendations