Effect of Al on Expansion Behavior of Mg–Al Alloys During Solidification

  • Yi MengEmail author
  • Jian Sun
  • Lei-Gang Cao
  • Yue Yang
  • Hai-Tao Zhang
  • Jian-Zhong Cui
Article
  • 38 Downloads

Abstract

The cooling curves and the change of contraction/expansion during solidification and cooling were tested by using a self-made device which could achieve the one-dimensional contraction instead of three-dimensional contraction of the casting. Then, the effects of Al content (0, 1.1, 3, 5, 10, 12.9, 15, 17, 19, 22, 24 and 30 wt%) on the thermal contraction/expansion of the binary Mg–Al as-cast alloys during solidification were obtained. The results showed that expanding instead of contraction was present in Mg–Al alloys with the addition of 0–30 wt% Al during solidification. The values of expansion significantly increased at first and then decreased with the increase in Al content. And the maximum expansion ratio of 0.44% (maximum expansion value: 0.841 mm) was present in the Mg–15 wt% Al alloy. Contraction instead of expansion occurred once the temperature drops to the temperature corresponding to the expansion value in total, indicating the occurrence of a continuous expansion during the solidification process in mushy zone for the Mg alloys with Al addition of 5–30 wt%. The expansion value in total consisted of two parts: the expansions occurring in the liquid-phase zone and mushy zone. The expansion in liquid zone was present in every Mg–Al alloy, and it contributed to the most proportion of the total expansion value when the Al content in Mg–Al alloy was lower than 10 wt% or higher than 22 wt%. However, the total expansion value was mainly determined by the solidification behavior in mushy zone when the Al content was among 10–22 wt% in Mg–Al alloys.

Keywords

Solidification Mg alloys Al content Expansion 

Notes

Acknowledgements

This work was financially supported by the Beijing Natural Science Foundation (No. 2164060), the Training Program Foundation for the Talents by Beijing (No. 2015000020124G023) and Yuqing Talent Development Program of North China University of Technology (No. 18XN012-079).

References

  1. [1]
    G. Cao, S. Kou, Mater. Sci. Eng. A 417, 230 (2006)CrossRefGoogle Scholar
  2. [2]
    M. Paliwal, I.H. Jung, Acta Mater. 61, 4848 (2013)CrossRefGoogle Scholar
  3. [3]
    W.C. Zheng, S.S. Li, B. Tang, D.B. Zeng, Chin. Foundary 3, 270 (2006)Google Scholar
  4. [4]
    Y.S. Wang, B.D. Sun, Q.D. Wang, Mater. Lett. 53, 35 (2002)CrossRefGoogle Scholar
  5. [5]
    H. Huang, P.H. Fu, Y.X. Wang, L.M. Peng, H.Y. Jiang, Trans. Nonferr. Met. Soc. Chin. 24, 922 (2014)CrossRefGoogle Scholar
  6. [6]
    H.W. Pan, Z.Q. Han, B.C. Liu, J. Mater. Sci. Technol. 32, 68 (2016)CrossRefGoogle Scholar
  7. [7]
    S. Zhao, Q. Peng, H. Li, B. Liu, J. Alloys Compd. 584, 56 (2014)CrossRefGoogle Scholar
  8. [8]
    I.I. Novikov, O.E. Grushko, Mater. Sci. Technol. 11, 926 (1995)CrossRefGoogle Scholar
  9. [9]
    J.M. Drezet, M. Rappaz, Modeling of Casting, Welding, and Advanced Solidification Process VIII (Springer, San Antonio, 1998), pp. 883–890Google Scholar
  10. [10]
    D.G. Eskin, L.Katgerman Suyitno, Prog. Mater Sci. 49, 629 (2004)CrossRefGoogle Scholar
  11. [11]
    P. Gunde, A. Schiffl, P.J. Uggowitzer, Mater. Sci. Eng. A 527, 7074 (2010)CrossRefGoogle Scholar
  12. [12]
    G. Cao, S. Kou, Metall. Mater. Trans. A 37, 3647 (2006)CrossRefGoogle Scholar
  13. [13]
    G. Cao, I. Haygood, S. Kou, Metall. Mater. Trans. A 41, 2139 (2010)CrossRefGoogle Scholar
  14. [14]
    Z. Zhen, N. Hort, Y. Huang, N. Petri, O. Utke, K.U. Kainer, Mater. Sci. Forum 618–619, 533 (2009)CrossRefGoogle Scholar
  15. [15]
    K. Hu, A.B. Phillion, D.M. Maijer, S.L. Cockcroft, Scr. Mater. 60, 427 (2009)CrossRefGoogle Scholar
  16. [16]
    J.F. Song, F.S. Pan, B. Jiang, A. Atrens, M.X. Zhang, Y. Lu, J. Magnes, Alloys 4, 151 (2016)CrossRefGoogle Scholar
  17. [17]
    Z.S. Zhen, N. Hort, Y.D. Huang, O. Utke, N. Petri, Cast Met. 22, 331 (2013)CrossRefGoogle Scholar
  18. [18]
    G.P. Cao, S. Kou, Y.A. Chang, Magnesium Technology (Springer, Hoboken, 2014), pp. 205–209Google Scholar
  19. [19]
    N. Katarzyna, B. Malik, Precipitates of γ–Mg 17 Al 12 Phase in AZ91 Alloy, Magnesium Alloys—Design, Processing and Properties (Springer, Croatia, 2011), pp. 95–112Google Scholar
  20. [20]
    M. Esmaily, M. Shahabi-Navid, N. Mortazavi, J.E. Svensson, M. Halvarsson, M. Wessén, A.E.W. Jarfors, L.G. Johansson, Mater. Charact. 95, 50 (2014)CrossRefGoogle Scholar
  21. [21]
    A. Stangeland, A. Mo, N. Øyvind, D.G. Eskin, M. M’Hamdi, Metall. Mater. Trans. A 35, 2903 (2004)CrossRefGoogle Scholar
  22. [22]
    C.R. Clopet, R.F. Cochrane, A.M. Mullis, Acta Mater. 61, 6894 (2013)CrossRefGoogle Scholar

Copyright information

© The Chinese Society for Metals and Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  • Yi Meng
    • 1
    Email author
  • Jian Sun
    • 1
  • Lei-Gang Cao
    • 1
  • Yue Yang
    • 1
  • Hai-Tao Zhang
    • 2
  • Jian-Zhong Cui
    • 2
  1. 1.School of Mechanical and Materials EngineeringNorth China University of TechnologyBeijingChina
  2. 2.Key Laboratory of Electromagnetic Processing of Materials, Ministry of EducationNortheastern UniversityShenyangChina

Personalised recommendations