Preparation and thermoelectric properties of Cu1.8S/CuSbS2 composites
- 7 Downloads
Chalcostibite (CuSbS2) is composed of earth-abundant elements and has a proper band gap (Eg = 1.05 eV) as a thermoelectric (TE) material. Herein, we report the TE properties in the CuSbS2based composites with a mole ratio of (1−x)CuSbS2−xCu18S (x = 0, 0.1, 0.2, 0.3), which were prepared by mechanical alloying (MA) combined with spark plasma sintering (SPS). X-ray diffraction (XRD) and back-scattered electron image (BSE) results indicate that a single phase of CuSbS2 is synthesized at x = 0 and the samples consist of CuSbS2, Cu3SbS4, and Cu12Sb4S13 at 0.1 ⩽ x ⩽ 0.3. The correlation between the phase structure, microstructure, and TE transport properties of the bulk samples is established. The electrical conductivity increases from 0.14 to 50.66 S·cm−1 at 723 K and at 0 ⩽ x ⩽ 0.03, while the Seebeck coefficient holds an appropriate value of 190.51 µV·K−1. The highest ZT value of 0.17 is obtained at 723 K and at x = 0.3 owing to the combination of a high PF 183 µW·m−1·K−2 and a low κ 0.8 W·m−1·K−1.
KeywordsCuSbS2 phase structure ZT thermoelectric
This work was supported by National Key R&D Program of China (Grant No. 2018YFB0703600) and the National Natural Science Foundation of China (Grant No. 11474176).
- Chen K. Synthesis and thermoelectric properties of Cu-Sb-S compounds. Ph.D. Thesis. London (UK): Queen Mary, University of London, 2016.Google Scholar
- Rabhi A, Kanzari M. Structural, optical and electrical properties of CuSbS2 these amorphous films: effect of the thickness variation. Chalcogenide Lett 2011, 8: 383–390.Google Scholar
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.