, Volume 28, Issue 4, pp 283–290 | Cite as

Novel natural rubber latex/lignin-based bio-adhesive: synthesis and its application on medium density fiber-board

  • Jayshree Thuraisingam
  • Puranjan Mishra
  • Arun GuptaEmail author
  • Triveni Soubam
  • Bijarami Mat Piah
Original Research
  • 27 Downloads

Abstract

The phenolic content in lignin makes it a potential substitute for formaldehyde-based synthetic wood adhesives. In the present work, lignin isolated from Hevea brasiliensis was treated with laccase enzyme to obtain active lignin. The activated lignin (NaOH treated) was further formulated with natural rubber latex (NR-latex) to prepare bio-adhesive. Complementary analysis such as modulus of rupture (MoR), modules of elasticity (MoE), internal bonding (IB), Fourier transform infrared (FTIR) spectroscopy, thickness swelling (TS), and scanning electron microscopy (SEM) were applied to characterize a medium density fibre-board (MDF) prepared based on bio-adhesive formulation. It was found that bio-adhesive formulation of 10 g NR-latex with 10 g of lignin has the highest MoR of 16 MPa, while the formulation of 15 g NR-latex with 5 g lignin showed the highest MoE of 15 MPa. The TS result showed that there is a weight gain on MDFs with a lower proportion of NR-latex content which consequently increases the density of the composites. The FTIR analysis of formulated bio-adhesive revealed the significant difference in chemical composition with different proportions of lignin and NR-latex in bio-adhesive. Finally, SEM examination of the interfaces of formulated bio-adhesive and wood fibre material showed the better dispersion with no adhesive lumps.

Keyword

Bio-adhesive Lignin Natural rubber latex Medium density fibre-board Bending strength Internal bonding Synthetic-adhesive 

Notes

Acknowledgements

The author would like to thank Faculty of Chemical and Natural Resources Engineering from University Malaysia Pahang for the cooperation provided by all technical staffs for conducting this research work in the polymer lab. We gratefully acknowledge the financial support of the UMP, Malaysia (RDU170132).

References

  1. 1.
    Pizzi A (2006) Recent developments in eco-efficient bio-based adhesives for wood bonding: opportunities and issues. J Adhes Sci Technol 20:829–846CrossRefGoogle Scholar
  2. 2.
    Lei H, Pizzi A, Du G (2008) Environmentally friendly mixed tannin/lignin wood resins. J Appl Polym Sci 107:203–209CrossRefGoogle Scholar
  3. 3.
    Zhang X, Wang F, Keer LM (2015) Influence of surface modification on the microstructure and thermo-mechanical properties of bamboo fibers. Materials 8:6597–6608CrossRefGoogle Scholar
  4. 4.
    Nasir M, Gupta A, Beg MD, Chua GK, Jawaid M, Kumar A, Khan TA (2013) Fabricating eco-friendly binderless fiberboard from laccase-treated rubber wood fiber. Bioresources 8:3599–3608CrossRefGoogle Scholar
  5. 5.
    Demircioglu E, Sofuoglu A, Odabasi M (2011) Particle-phase dry deposition and air–soil gas exchange of polycyclic aromatic hydrocarbons (PAHs) in Izmir, Turkey. J Hazard Mater 186:328–335CrossRefGoogle Scholar
  6. 6.
    Nasir M, Hashim R, Sulaiman O, Gupta A, Khan TA, Jawaid M, Asim M (2017) Natural fiber improvement by laccase; optimization, characterization and application in medium density fiberboard. J Nat Fibers 14:379–389CrossRefGoogle Scholar
  7. 7.
    Davies JC, Mazurek J (2014) Pollution control in United States: evaluating the system. Taylor & Francis Group, New YorkCrossRefGoogle Scholar
  8. 8.
    Pradyawong S, Qi G, Li N, Sun XS, Wang D (2017) Adhesion properties of soy protein adhesives enhanced by biomass lignin. Int J Adhes Adhes 75:66–73CrossRefGoogle Scholar
  9. 9.
    Kumar A, Sharma KV, Gupta A, Tywoniak J, Hajek P (2017) Optimization of processing parameters of medium density fiberboard using response surface methodology for multiwalled carbon nanotubes as a nanofiller. Eur J Wood Wood Prod 72:203–213CrossRefGoogle Scholar
  10. 10.
    Eslah F, Jonoobi M, Faezipour M, Afsharpour M, Enayati AA (2016) Preparation and development of a chemically modified bio-adhesive derived from soybean flour protein. Int J Adhes Adhes 71:48–54CrossRefGoogle Scholar
  11. 11.
    Khan TA, Gupta A, Jamari SS, Jose R, Nasir M, Kumar A (2013) Synthesis and characterization of carbon fibers and their application in wood composites. Bioresources 8:4171–4184CrossRefGoogle Scholar
  12. 12.
    Khalil HA, Aprilia NS, Bhat AH, Jawaid M, Paridah MT, Rudi D (2103) A Jatropha biomass as renewable materials for biocomposites and its applications. Renew Sust Energ Rev 22:667–685CrossRefGoogle Scholar
  13. 13.
    Ashkani M, Kabiri K, Salimi A, Bouhendi H, Omidian H (2108) Hybrid hydrogel based on pre-gelatinized starch modified with glycidyl-crosslinked microgel. Iran Polym J 27:183–192CrossRefGoogle Scholar
  14. 14.
    Dhanania S, Mahata D, Prabhavale O, Cornish K, Nando GB, Chattopadhyay S (2018) Phosphorylated cardanol prepolymer grafted guayule natural rubber: an advantageous green natural rubber. Iran Polym J 27:307–318CrossRefGoogle Scholar
  15. 15.
    Bakar NH, Muda NH, Tan WL, Bakar MA, Yusli F, Nawi MA, Sabri NA (2018) Eco-friendly natural rubber–silver (NR–Ag) composites for photo-assisted degradation of methyl orange dye. Iran Polym J 27:23–32CrossRefGoogle Scholar
  16. 16.
    Nasir M, Gupta A, Beg MD, Chua GK, Kumar A (2013) Fabrication of medium density fibreboard from enzyme treated rubber wood (Hevea brasiliensis) fibre and modified organosolv lignin. Int J Adhes Adhes 44:99–104CrossRefGoogle Scholar
  17. 17.
    Mugableh MI (2015) Aggregate economic forces and Malaysian equity market: equilibrium time-series approach. In: 4th ICMFE, Indonesia, p 192Google Scholar
  18. 18.
    Novaes E, Kirst M, Chiang V, Winter-Sederoff H, Sederoff R (2010) Lignin and biomass: a negative correlation for wood formation and lignin content in trees. Plant Physiol 154:555–561CrossRefGoogle Scholar
  19. 19.
    Zhang X, Zhu Y, Yu Y, Song J (2017) Improve performance of soy flour-based adhesive with a lignin-based resin. Polymers 9:261CrossRefGoogle Scholar
  20. 20.
    Khan TA, Gupta A, Jamari SS, Jose R, Nasir M, Kumar A (2015) Examination of selected synthesis parameters for composite adhesive-type urea-formaldehyde/activated carbon adhesives. Int J Eng Technol Sci 3:52–59Google Scholar
  21. 21.
    Varodi AM, Petrovici V (2008) Study concerning the quality of some lignin-based adhesive compositions for glued-laminated beech wood. Pro Ligno 4:55–64Google Scholar
  22. 22.
    Mate DM, Alcalde M (2017) Laccase: a multi-purpose biocatalyst at the forefront of biotechnology. Microb Biotechnol 10:1457–1467CrossRefGoogle Scholar
  23. 23.
    Nasir M, Gupta A, Beg MD, Chua GK, Asim M (2014) Laccase application in medium density fibreboard to prepare a bio-composite. RSC Adv 4:11520–11527CrossRefGoogle Scholar
  24. 24.
    Sidiras D, Batzias F, Ranjan R, Tsapatsis M (2011) Simulation and optimization of batch autohydrolysis of wheat straw to monosaccharides and oligosaccharides. Bioresour Technol 102:10486–10492CrossRefGoogle Scholar
  25. 25.
    Hill CA (2007) Wood modification: chemical, thermal and other processes, vol 5. John Wiley & Sons, ChichesterGoogle Scholar
  26. 26.
    Nasir M, Gupta A, Beg MD, Chua GK, Kumar A (2014) Physical and mechanical properties of medium-density fibreboards using soy—lignin adhesives. J Trop For Sci 1:41–49Google Scholar
  27. 27.
    McNatt JD, Link CL (1989) Analysis of ASTM D 1037 accelerated-aging test. For Prod J 39:51–57Google Scholar
  28. 28.
    Koo BW, Min BC, Gwak KS, Lee SM, Choi JW, Yeo H, Choi IG (2012) Structural changes in lignin during organosolv pretreatment of Liriodendron tulipifera and the effect on enzymatic hydrolysis. Biomass Bioenerg 42:24–32CrossRefGoogle Scholar
  29. 29.
    Asrul M, Othman M, Zakaria M, Fauzi MS (2013) Lignin filled unvulcanised natural rubber latex: effects of lignin on oil resistance, tensile strength and morphology of rubber films. Int J Eng Sci Invent Res Dev 5:38–43Google Scholar
  30. 30.
    Shaha RK, Punichelvana YN, Afandi A (2013) Optimized extraction condition and characterization of pectin from kaffir lime (Citrus hystrix). Res J Agric For Sci 1:1–11Google Scholar
  31. 31.
    Idrus MM, Hamdan S, Rahman MR, Islam MS (2011) Treated tropical wood sawdust-polypropylene polymer composite: Mechanical and morphological study. J Biomater Nanobiotechnol 2:435CrossRefGoogle Scholar
  32. 32.
    Risanto L, Hermiati E, Sudiyani Y (2014) Properties of lignin from oil palm empty fruit bunch and its application for plywood adhesive. Makara J Technol 18:67–75CrossRefGoogle Scholar
  33. 33.
    Datta J, Parcheta P (2017) A comparative study on selective properties of Kraft lignin—natural rubber composites containing different plasticizers. Iran Polym J 26:453–466CrossRefGoogle Scholar
  34. 34.
    Watkins D, Nuruddin M, Hosur M, Tcherbi-Narteh A, Jeelani S (2015) Extraction and characterization of lignin from different biomass resources. J Mater Res Technol 4:26–32CrossRefGoogle Scholar
  35. 35.
    Thakur VK, Thakur MK (2015) Recent advances in green hydrogels from lignin: a review. Int J Biol Macromol 72:834–847CrossRefGoogle Scholar
  36. 36.
    Mohammadi M, McMahon G, Sun L, Tang C, Hirth P, Yeh BK, Hubbard SR, Schlessinger J (1997) Structures of the tyrosine kinase domain of fibroblast growth factor receptor in complex with inhibitors. Science 276:955–960CrossRefGoogle Scholar
  37. 37.
    Sahoo D, Ummalyma SB, Okram AK, Sukumaran RK, George E, Pandey A (2017) Potential of Brachiaria mutica (Para grass) for bioethanol production from Loktak Lake. Bioresour Technol 242:133–138CrossRefGoogle Scholar
  38. 38.
    Arroyo M, Lopez-Manchado MA, Herrero B (2003) Organo-montmorillonite as substitute of carbon black in natural rubber compounds. Polymer. 44:2447–2453CrossRefGoogle Scholar
  39. 39.
    Phakkeeree T, Ikeda Y, Yokohama H, Phinyocheep P, Kitano R, Kato A (2016) Network-like structure of lignin in natural rubber matrix to form high performance elastomeric bio-composite. J Fiber Sci Technol 72:160–165CrossRefGoogle Scholar

Copyright information

© Iran Polymer and Petrochemical Institute 2019

Authors and Affiliations

  • Jayshree Thuraisingam
    • 1
  • Puranjan Mishra
    • 2
  • Arun Gupta
    • 1
    Email author
  • Triveni Soubam
    • 1
  • Bijarami Mat Piah
    • 1
  1. 1.Faculty of Chemical and Natural Resource EngineeringUniversity Malaysia PahangKuantanMalaysia
  2. 2.Faculty of Engineering TechnologyUniversiti Malaysia PahangKuantanMalaysia

Personalised recommendations