Studies on Slurry Erosion Behavior of HVOF Applied Y2O3-Added WC–10Co–4Cr Cermet on 13-4 Martensitic Stainless Steel

Technical Article
  • 68 Downloads

Abstract

Commercially 86WC–10Co–4Cr hard cermet coating is applied via high-velocity oxygen fuel thermal spray process on hydroturbine blade steel, i.e., 13Cr–4Ni martensitic stainless steel to help improve its wear resistance and life against the eroding action of hard silt particles present in the discharge. The erosive wear resistance of 86WC–10Co–4Cr cermet is improved upon by the addition of 2 wt.% of micro-sized yttrium oxide, which serves as a hard phase. These cermet coatings were deposited on 13Cr–4Ni martensitic stainless steel substrates via high-velocity oxygen fuel method to get an average thickness of 350 µm. Slurry pot wear test (duration 40 h) was used to evaluate the erosive wear resistance of the cermet coatings and the bare 13Cr–4Ni martensitic stainless steel substrate. Silica sand (size range 210–297 µm) was mixed with water to make a slurry of 100 kg/m3 concentration. A sliding speed of 4.45 m/s was maintained between the samples and the slurry. The increase in wear resistance of 86WC–10Co–4Cr cermet due to the addition of 2 wt.% yttrium oxide has been explained on the basis of improvement in hardness from 1048 ± 22 to 1154 ± 25 HV and due to densification effect of yttrium oxide.

Keywords

Coatings Ceramics Carbon steels Wear 

Notes

Acknowledgments

Authors thankfully acknowledge Metallurgical and Materials Engineering Department, IIT Roorkee, for providing access to their SEM and slurry erosion laboratory facilities for the completion of this work.

References

  1. 1.
    M.K. Padhy, R.P. Saini, A review on silt erosion in hydro turbines. Renew. Sustain. Energy Rev. 12(7), 1974–1987 (2008)CrossRefGoogle Scholar
  2. 2.
    B.S. Mann, V. Arya, Abrasive and erosive wear characteristics of plasma nitriding and HVOF coatings: their application in hydro turbines. Wear 249(5), 354–360 (2001)CrossRefGoogle Scholar
  3. 3.
    B.S. Mann, High-energy particle impact wear resistance of hard coatings and their application in hydro turbines. Wear 237(1), 140–146 (2000)CrossRefGoogle Scholar
  4. 4.
    B.S. Mann, High-power diode laser-treated 13Cr4Ni stainless steel for hydro turbines. J. Mater. Eng. Perform. 23(6), 1964–1972 (2014)CrossRefGoogle Scholar
  5. 5.
    D.A. Stewart, P.H. Shipway, D.G. McCartney, Abrasive wear behaviour of conventional and nanocomposite HVOF-sprayed WC–Co coatings. Wear 225–229(2), 789–798 (1999)CrossRefGoogle Scholar
  6. 6.
    P.H. Shipway, D.G. McCartney, T. Sudaprasert, Sliding wear behaviour of conventional and nanostructured HVOF sprayed WC–Co coatings. Wear 259(7), 820–827 (2005)CrossRefGoogle Scholar
  7. 7.
    L. Thakur, N. Arora, A study of processing and slurry erosion behaviour of multi-walled carbon nanotubes modified HVOF sprayed nano-WC–10Co–4Cr coating. Surf. Coat. Technol. 309, 860–871 (2017)CrossRefGoogle Scholar
  8. 8.
    C.N. Machio, G. Akdogan, M.J. Witcomb, S. Luyckx, Performance of WC–VC–Co thermal spray coatings in abrasion and slurry erosion tests. Wear 258(1), 434–442 (2005)CrossRefGoogle Scholar
  9. 9.
    D.P. Doan, T.B. Tran, V.A. Nguyen, A.T. Phan, Microstructural evolution and some mechanical properties of nanosized yttrium oxide dispersion strengthened 13Cr steel. Adv. Nat. Sci. Nanosci. Nanotechnol. 1(3), 035009 (2010)CrossRefGoogle Scholar
  10. 10.
    W.B. Bouaeshi, D.Y. Li, Effects of Y2O3 addition on microstructure, mechanical properties, electrochemical behavior and resistance to corrosive wear of aluminum. Tribol. Int. 40(2), 188–199 (2007)CrossRefGoogle Scholar
  11. 11.
    J. Al-Haidary, M. Al-Haidari, S. Qrunfuleh, Effect of yttria addition on mechanical, physical and biological properties of bioactive MgO–CaO–SiO2–P2O5–CaF2 glass ceramic. Biomed. Mater. 3(1), 015005 (2008)CrossRefGoogle Scholar
  12. 12.
    H. Ahmadi, D.Y. Li, M. Nouri, Effects of yttria addition on microstructure, mechanical properties, wear resistance and corrosive wear resistance of TiNi alloy. J. Mater. Sci. Technol. 25(5), 645 (2009)Google Scholar
  13. 13.
    O.A. El-Kady, Effect of nano-yttria addition on the properties of WC/Co composites. Mater. Des. 52, 481–486 (2013)CrossRefGoogle Scholar
  14. 14.
    J.R. Davis, Handbook of Thermal Spray Technology (ASM International, Materials Park, 2004)Google Scholar
  15. 15.
    L. Pawlowski, The Science and Engineering of Thermal Spray Coatings (Wiley, England, 2008)CrossRefGoogle Scholar
  16. 16.
    A.K. Maiti, N. Mukhopadhyay, R. Raman, Effect of adding WC powder to the feedstock of WC–Co–Cr based HVOF coating and its impact on erosion and abrasion resistance. Surf. Coat. Technol. 201(18), 7781–7788 (2007)CrossRefGoogle Scholar
  17. 17.
    D.K. Goyal, H. Singh, H. Kumar, V. Sahni, Slurry erosion behaviour of HVOF sprayed WC–10Co–4Cr and Al2O3 + 13TiO2 coatings on turbine steel. Wear 289, 46–57 (2012)CrossRefGoogle Scholar
  18. 18.
    G.E. Dieter, D.J. Bacon, Mechanical Metallurgy, vol. 3 (McGraw-Hill, New York, 1986)Google Scholar
  19. 19.
    I.M. Hutchings, P. Shipway, Tribology: Friction and Wear of Engineering Materials (Butterworth-Heinemann, Oxford, 1992)Google Scholar
  20. 20.
    R.J.K. Wood, B.G. Mellor, M.L. Binfield, Sand erosion performance of detonation gun applied tungsten carbide/cobalt–chromium coatings. Wear 211(1), 70–83 (1997)CrossRefGoogle Scholar
  21. 21.
    C. Verdon, A. Karimi, J.L. Martin, Microstructural and analytical study of thermally sprayed WC–Co coatings in connection with their wear resistance. Mater. Sci. Eng. A 234, 731–734 (1997)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature and ASM International 2018

Authors and Affiliations

  1. 1.Mechanical Engineering DepartmentThapar UniversityPatialaIndia

Personalised recommendations