Pearlite Development in Commercial Hadfield Steel by Means of Isothermal Reactions
- 54 Downloads
The Fe–12Mn–1C Hadfield steel is an abrasion-resistant alloy of high technological relevance for mining and heavy machinery. This composition is susceptible to pearlite formation which is detrimental for the material’s ductility. Although its spread use, the study of pearlite formation has been preserved to laboratory conditions which cannot be transferred to industrial practices. This manuscript provides updated information about this phenomenon by constructing the time–temperature-transformation diagram of the alloy between 400 and 600 °C. The pearlitic reaction occurs above 450 °C and begins on the grain boundaries. Only 7 min is needed for the transformation to start at 550 °C, and a maximum pearlite fraction of 35% is reached after 150 min at this temperature. Results are compared with the Fe–12Mn–0.8C composition mostly found in literature. The discussion comprises the effects of carbon and manganese content on the pearlitic reaction with the support of thermodynamics calculations.
KeywordsHadfield steel Isothermal reaction Pearlite TTT-diagram Thermodynamics
The authors acknowledge the support of CONICET, Argentina, under Grants PIP 0488 and PDTS-251.
- 2.Y. Ono, T. Tsuchiyama, and S. Takaki, Mechanism of Embrittlement in Hadfield Steel, in Steels and Materials for Power Plants (Wiley, New York, 2006) FRG, pp. 143–148Google Scholar
- 17.N. Ridley, The Pearlite Reaction, in Proceedings of International Conference on Phase Transformations in Ferrous alloys, eds. by A.R. Marder, J.I. Goldstein (TMS-AIME, Warrendale, 1984), p. 201–236Google Scholar
- 18.M. Hillert, Analysis of the Effect of Alloying Elements on the Pearlite Reaction, in Proceedings of an International Conference on Solid to Solid Phase Transformations, ed. by H.I. Aaronson (TMS-AIME, Warrendale, 1982), p. 789–806Google Scholar
- 22.J.D. Verhoeven, Fundamentals of Physical Metallurgy (Wiley, New York, 1975), p. 458Google Scholar