Solvent-free synthesis of nano-cancrinite from rice husk ash

  • Peng Zhang
  • Suqin LiEmail author
  • Changquan Zhang
Review Article
  • 8 Downloads

Abstract

The solvent used in the hydrothermal synthesis of zeolites is a major obstacle to achieve green and sustainable methods of synthesis, so the development of environmentally friendly zeolite synthesis technology has aroused widespread concern. As a solid waste, it still has a challenge for zeolites synthesis from rice husk ash by solvent-free method to increase its recovery rate and economic value. Our approach focused on reutilization of rice husk ash by converting it to cancrinite without employing solvents. The raw and as-synthesized products were characterized by XRD, XRF, SEM, FT-IR, UV-Raman, and BET analysis. The influence of Na2CO3·10H2O/SiO2 molar ratio and synthesis time on cancrinite crystal growth and properties was evaluated by various analytical methods. The results suggested that the optimal conditions of Na2CO3·10H2O/SiO2 and synthesis time for the cancrinite synthesis were 0.3 and 72 h, at this condition, the size of cancrinite was about 200 nm, the BET surface area was estimated to 59.909 m2/g, and the external surface area was 55.456 m2/g, which indicate the cancrinite was a good mesoporous material. From this study, it could be known that the synthesis process of cancrinite by solvent-free route was an amorphous sodium aluminosilicate phase followed by sodalite and finally cancrinite, which is different from the traditional hydrothermal method.

Keywords

Sodalite Cancrinite Solvent-free method Rice husk ash 

Notes

Acknowledgements

The authors would like to thank Jianming Liu from Shiyanjia lab for the support of UV-Raman analysis.

Funding information

This work is supported by Major Science and Technology Program for Water Pollution Control and Treatment (2017ZX07402001).

Reference

  1. 1.
    Ren LM, Wu QM, Yang CG, Zhu LF, Li CJ, Zhang PL, Zhang HY, Meng XJ, Xiao FS (2012) Solvent-free synthesis of zeolites from solid raw materials. J Am Chem Soc 134:15173–15176CrossRefGoogle Scholar
  2. 2.
    Zeng SJ, Wan RW, Zhang ZT, Qiu SL (2016) Solventless green synthesis of sodalite zeolite using diatomite as silica source by a microwave heating technique. Inorg Chem Commun 70:168–171CrossRefGoogle Scholar
  3. 3.
    Wei F, Kazumasa M, Riichiro K, Toshiyuki Y, Tatsuya O (2008) Synthesis of nanometer-sized sodalite without adding organic additives. Langmuir 24:6952–6958CrossRefGoogle Scholar
  4. 4.
    Ma YA, Yan CJ, Alshameri A, Qiu XM, Zhou CY, Li D (2014) Synthesis and characterization of 13X zeolite from low-grade natural kaolin. Adv Powder Technol 25:495–499CrossRefGoogle Scholar
  5. 5.
    Yao JF, Wang HT, Ratinac KR, Ringer SP (2006) Formation of colloidal hydroxy-sodalite nanocrystals by the direct transformation of silicalite nanocrystals. Chem Mater 18:1394–1396CrossRefGoogle Scholar
  6. 6.
    Nabavi MS, Mohammadi T, Kazemimoghadam M (2014) Hydrothermal synthesis of hydroxy sodalite zeolite membrane: separation of H2/CH4. Ceram Int 40:5889–5896CrossRefGoogle Scholar
  7. 7.
    Dey KP, Ghosh S, Naskar MK (2013) Organic template-free synthesis of ZSM-5 zeolite particles using rice husk ash as silica source. Ceram Int 39:2153–2157CrossRefGoogle Scholar
  8. 8.
    Parker WG, Stephen C (2010) Structure of zeolite a (LTA) surfaces and the zeolite A/water interface. J Phys Chem C 114:9739–9747CrossRefGoogle Scholar
  9. 9.
    Selim AQ, Mohamed EA, Seliem MK, Zayed AM (2018) Synthesis of sole cancrinite phase from raw muscovite: characterization and optimization. J Alloys Compd 762:653–667CrossRefGoogle Scholar
  10. 10.
    Barnes MC, Jonas AM, Gerson AR (1999) A methodology for quantifying sodalite and cancrinite phase mixtures and the kinetics of the sodalite to cancrinite phase transformation. Microporous Mesoporous Mater 31:303–319CrossRefGoogle Scholar
  11. 11.
    Ventura GD, Bellatreccia F, Bonaccorsi E (2005) CO2 in minerals of the cancrinite-sodalite group: pitiglianoite. Eur J Mineral 17:847–851CrossRefGoogle Scholar
  12. 12.
    Ventura GD, Bellatreccia F, Parodi GC, Camara F, Piccinini M (2007) Single crystal FT-IR and X-ray study of vishnevite, ideally [Na6(SO4)] [Na2(H2O)2] [Si6Al6O24]. Am Mineral 92:713–721CrossRefGoogle Scholar
  13. 13.
    Ventura GD, Bellatreccia F, Piccinini M (2008) Channel CO2 in feldspathoids: new data and new perspectives. Rendiconti Lincei 19:141–159CrossRefGoogle Scholar
  14. 14.
    Hassan I, Antao SM, Parise JB (2006) Cancrinite: crystal structure, phase transitions and dehydration behavior with temperature. Am Mineral 91:1117–1124CrossRefGoogle Scholar
  15. 15.
    Gatta GD, Lotti P (2016) Cancrinite-group minerals: crystal-chemical description and properties under non-ambient conditions: a review. Am Mineral 101:253–265CrossRefGoogle Scholar
  16. 16.
    Lotti P, Gatta GD, Rotiroti N, Camara F (2012) High-pressure study of a natural cancrinite. Am Mineral 97:872–882CrossRefGoogle Scholar
  17. 17.
    Lotti P, Gatta GD, Merlini M, Hanfland M (2014) High-pressure behavior of davyne [CAN-topology]: an in situ single-crystal synchrotron diffraction study. Microporous Mesoporous Mater 198:203–214CrossRefGoogle Scholar
  18. 18.
    Shao H, Pinnavaia TJ (2010) Synthesis and properties of nanoparticle forms saponite clay, cancrinite zeolite and phase mixtures thereof. Microporous Mesoporous Mater 133:10–17CrossRefGoogle Scholar
  19. 19.
    Zhang CQ, Li SQ, Bao SC (2018) A facile and green method for the synthesis of hierarchical ZSM-5 zeolite aggregates from rice husk ash. Res Chem Intermed 44:3581–3595CrossRefGoogle Scholar
  20. 20.
    Meng X, Xiao FS (2014) Green routes for synthesis of zeolites. Chem Rev 114:1521–1543CrossRefGoogle Scholar
  21. 21.
    Zhang P, Wang L, Ren L, Zhu L, Sun Q, Zhang J, Meng X, Xiao FS (2011) “Solvent-free” synthesis of thermally stable and hierarchically porous aluminophosphates (SF-APOs) and heteroatom-substituted aluminophosphates (SF-MAPOs). J Mater Chem 21:12026–12033CrossRefGoogle Scholar
  22. 22.
    Jin Y, Sun Q, Qi G, Yang C, Xu J, Chen F, Meng X, Deng F, Xiao FS (2013) Solvent-free synthesis of silicoaluminophosphate zeolites. Angew Chem Int Ed Engl 52:9172–9175CrossRefGoogle Scholar
  23. 23.
    Wu Q, Wang X, Qi G, Guo Q, Pan S, Meng X, Xu J, Deng F, Fan F, Feng Z, Li C, Maurer S, Muller U, Xiao FS (2014) Sustainable synthesis of zeolites without addition of both organotemplates and solvents. J Am Chem Soc 136:4019–4025CrossRefGoogle Scholar
  24. 24.
    Wu Q, Liu X, Zhu L, Ding L, Gao P, Wang X, Pan S, Bian C, Meng X, Xu J, Deng F, Maurer S, Muller U, Xiao FS (2015) Solvent-free synthesis of zeolites from anhydrous starting raw solids. J Am Chem Soc 137:1052–1055CrossRefGoogle Scholar
  25. 25.
    Zhang CQ, Li SQ, Bao SC (2018) Sustainable synthesis of ZSM-5 zeolite from rice husk ash without addition of solvents. Waste Biomass Valor.  https://doi.org/10.1007/s12649-018-0356-0
  26. 26.
    Luo W, Yang XY, Wang ZR, Huang WF, Chen JY, Jiang W, Wang LJ, Cheng XW, Deng YH, Zhao DY (2017) Synthesis of ZSM-5 aggregates made of zeolite nanocrystals through a simple solvent-free method. Microporous Mesoporous Mater 243:112–118CrossRefGoogle Scholar
  27. 27.
    Naskar MK, Kundu D, Chatterjee M (2012) A facile hydrothermal conversion of rice husk ash to ZSM-5 zeolite powders. J Am Ceram Soc 95:925–930CrossRefGoogle Scholar
  28. 28.
    Kordatos K, Ntziouni A, Iliadis L, Kasselouri-Rigopoulou V (2013) Utilization of amorphous rice husk ash for the synthesis of ZSM-5 zeolite under low temperature. J Mater Cycles Waste 15:571–580CrossRefGoogle Scholar
  29. 29.
    Yu W, Yuan P, Liu D, Deng L, Yuan W, Tao B, Chen H, Chen F (2015) Facile preparation of hierarchically porous diatomite/MFI-type zeolite composites and their performance of benzene adsorption: the effects of NaOH etching pretreatment. J Hazard Mater 285:173–181CrossRefGoogle Scholar
  30. 30.
    Reyes CAR, Williams C, Alarcón OMC (2013) Nucleation and growth process of sodalite and cancrinite from kaolinite-rich clay under low-temperature hydrothermal conditions. Mater Res 16:424–438CrossRefGoogle Scholar
  31. 31.
    Ríos CA, Williams C, Fullen MA (2009) Nucleation and growth history of zeolite LTA synthesized from kaolinite by two different methods. Appl Clay Sci 42:446–454CrossRefGoogle Scholar
  32. 32.
    Ríos CA, Williams C, Maple MJ (2007) Synthesis of zeolites and zeotypes by hydrothermal transformation of kaolinite and metakaolinite. Bistua 5:15–26Google Scholar
  33. 33.
    Barnes MC, Addai-Mensah J, Gerson AR (1999) The mechanism of the sodalite-to-cancrinite phase transformation in synthetic spent Bayer liquor. Microporous Mesoporous Mater 31:287–302CrossRefGoogle Scholar
  34. 34.
    Kordatos K, Gavela S, Ntziouni A, Pistiolas KN, Kyritsi A, Kasselouri-Rigopoulou V (2008) Synthesis of highly siliceous ZSM-5 zeolite using silica from rice husk ash. Microporous Mesoporous Mater 115:189–196CrossRefGoogle Scholar
  35. 35.
    Hackbarth K, Gesing TM, Fechtelkord M, Stief F, Buhl JC (1999) Synthesis and crystal structure of carbonate cancrinite Na8[AlSiO4]6CO3(H2O)3.4, grown under low-temperature hydrothermal conditions. Microporous Mesoporous Mater 30:347–385CrossRefGoogle Scholar
  36. 36.
    Ocanto F, Figueredo E, Brikgi M, Navarro CU, Linares CF (2009) Oxidation–reduction reactions: a novel method in the synthesis of nitrate cancrinite-type zeolites. Mater Lett 63:11–14CrossRefGoogle Scholar

Copyright information

© Springer-Verlag GmbH Germany, part of Springer Nature 2019

Authors and Affiliations

  1. 1.School of Metallurgical and Ecological EngineeringUniversity of Science and Technology BeijingBeijingChina

Personalised recommendations