Crystal Structure and XANES Study of Defect Perovskite (Y1−xPrx)1+δBa2−δCu3O7−y Compounds Prepared by Solid State Synthesis Method

  • Poom Prayoonphokkharat
  • Penphitcha Amonpattaratkit
  • Anucha WatcharapasornEmail author
Original Article - Theory, Characterization and Modeling
  • 25 Downloads

Abstract

In this research, the processing and characterization of (Y1−xPrx)1+δBa2−δCu3O7−y cuprate perovskite powder were studied. The experimental powder samples of (Y1−xPrx)1+δBa2−δCu3O7−y (0 ≤ x ≤ 1) were prepared using a conventional solid-state reaction method. The starting powders in appropriate ratios were mixed with 6 mol% excess of A-site ions to reduce the amount of BaCuO2 and PrBaO3 second phases and calcined at 880 °C for 12 h in normal atmosphere. The calcined powders were investigated for phase content using X-ray diffraction technique and detailed structural parameters were obtained by Rietveld refinement. The microstructure of the powders was investigated by scanning electron microscopy (SEM). The chemical composition was carried out by energy dispersive X-ray analysis (EDS). The oxidation state and coordination of Pr and Cu were determined by X-ray absorption near edge structure (XANES) spectroscopy. It was found that high-purity (Y,Pr)BCO powders could be obtained. By the Rietveld refinement, the overall unit cell volume increased with increasing Pr content. SEM–EDS images showed that the particle size was about 1–5 μm and the elemental composition of (Y + Pr):Ba:Cu = 1:2:3. Pr and Cu XANES spectra indicated that the average formal valence was larger than 3 for Pr and 2 for Cu. However, the peak shifted to lower valence state at higher concentration of Pr.

Graphical Abstract

Keywords

YBCO YPrBCO PrBCO XANES Crystal structure 

Notes

Acknowledgements

This research was financially supported by the Thailand Research Fund, the Physics and Astronomy Research Center, and TA/RA (2560–2561) scholarships, Graduate School, Chiang Mai University. Partial supports from the Center of Excellence in Advanced Materials for Printed Electronics and Sensors (CMU-NECTEC), Center of Excellence in Materials Science and Technology, Faculty of Science, the Graduate School, Chiang Mai University, and Takpittayakhom School are also acknowledged. Authors would also like to thank Beamline 8 (BL8) Staff at Synchrotron Light Research Institute (SLRI) for XANES measurement. P. Prayoonphokkharat would also like to thank the financial support from the TRF through the Royal Golden Jubilee Ph.D. Program (PhD 0106/2560).

References

  1. 1.
    Legros, C., Haut, C., Ponsonnet-Mora, L., Ayache, J.: Fabrication of pure YBaCuO powders with controlled microstructure. J. Eur. Ceram. Soc. 19(2), 165–173 (1999)CrossRefGoogle Scholar
  2. 2.
    Singhal, R.K.: A comparative study of Pr substitution at Y and Ba sites in YBa2Cu3O7−δ. Mater. Lett. 65(5), 825–827 (2011)CrossRefGoogle Scholar
  3. 3.
    Khaled, M., Saini, N.L., Garg, K.B., Studer, F.: X-ray adsorption study at Pr L3-edge in (Y, Br)Ba2Cu3O7−δ system. Solid State Commun. 100(11), 773–776 (1996)CrossRefGoogle Scholar
  4. 4.
    Kyoichi, K., Azusa, M., Hiroyuki, S., Takao, I., Takao, W., Tomoaki, Y.: Crystal structure and superconductivity in Ba2Y1- xPr xCu3O7- y. Jpn. J. Appl. Phys. 27(9A), L1642 (1988)Google Scholar
  5. 5.
    Matsuda, A., Kinoshita, K., Ishii, T., Shibata, H., Watanabe, T., Yamada, T.: Electronic and structural properties of Ba2Y1-x PrxCu3O7-δ. In: Proceedings of the 1st international symposium on superconductivity (ISS ’88), advances in superconductivity, pp. 191–196. Springer, JapanGoogle Scholar
  6. 6.
    Zhang, J., Cao, G., Chen, Z., Li, X., Cao, S.: Hole carrier localization and Pr substitution in YBCO systems by positron experiment. Mater. Lett. 54(4), 273–278 (2002)CrossRefGoogle Scholar
  7. 7.
    Bin, O., Michikazu, K., Hiroshi, N., Koh, T., Masatsune, O.: Preparation and physical properties of (PrxY1- x)1+δ Ba2-δCu3Oy. Jpn. J. Appl. Phys. 27(1A), L41 (1988)Google Scholar
  8. 8.
    Lei, S., Yunsong, H., Wenhua, P., Xianming, L., Liangbin, W., Xiao-Guang, L., Guien, Z., Yuheng, Z.: Study on the Pr-doped and Ce-doped YBa2Cu3Oy system by XPS and Raman spectrum. Phys. C Supercond. 282–287, 1021–1022 (1997)CrossRefGoogle Scholar
  9. 9.
    Boyce, J.B., Bridges, F., Claeson, T., Howland, R.S., Geballe, T.H., Nygren, M.: Local structure of YBa2Cu3Oy with varying oxygen content and substitutional dopants on the Cu sites. Phys. C Supercond. 153–155, 852–853 (1988)CrossRefGoogle Scholar
  10. 10.
    Nakaura, M., Ozawa, T., Saiga, K., Kumazawa, S., Katoh, H., Ishida, K., Ozawa, H., Ohsumi, K.: Study of Cu absorption edge of YBCO superconductor by X-ray powder diffraction method. J. Phys. Soc. Jpn. 64(9), 3336–3342 (1995)CrossRefGoogle Scholar
  11. 11.
    Lutterotti, L., Matthies, S., Wenk, H.R.: MAUD: a friendly java program for material analysis using diffraction. IUCr Newslett. CPD 21, 14–15 (1999)Google Scholar
  12. 12.
    Klysubun, W., Sombunchoo, P., Deenan, W., Kongmark, C.: Performance and status of beamline BL8 at SLRI for X-ray absorption spectroscopy. J. Synchrotron Radiat. 19(6), 930–936 (2012)CrossRefGoogle Scholar
  13. 13.
    Ravel, B., Newville, M.: ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12(4), 537–541 (2005)CrossRefGoogle Scholar
  14. 14.
    Prayoonphokkharat, P., Jiansirisomboon, S., Watcharapasorn, A.: Fabrication and properties of YBa2Cu3O7-x ceramics at different sintering temperatures. Electron. Mater. Lett. 9(4), 413–416 (2013)CrossRefGoogle Scholar
  15. 15.
    Wannasut, P., Keawprak, N., Jaiban, P., Watcharapasorn, A.: Preparation and physical properties of segmented thermoelectric YBa2Cu3O7-x-Ca3Co4O9 ceramics. In: IOP Conference Series: Materials Science and Engineering (2018)Google Scholar
  16. 16.
    Andreouli, C., Tsetsekou, A.: Synthesis of HTSC Re(Y)Ba2Cu3Ox powders: the role of ionic radius. Phys. C Supercond. 291(3), 274–286 (1997)CrossRefGoogle Scholar
  17. 17.
    Yu, J., Jin, W.T., Zhao, Y., Zhang, H.: Stable bonds and unstable bonds in Y(Pr)-123 system. Phys. C Supercond. 469(15), 967–969 (2009)CrossRefGoogle Scholar
  18. 18.
    Tan, Z., Heald, S.M., Cheong, S.W., Cooper, A.S., Budnick, J.I.: Rare-earth valence and doping in T-, T’-, and T* -phase R2CuO4 (R = rare earth). Phys. Rev. B 45(5), 2593–2596 (1992)CrossRefGoogle Scholar
  19. 19.
    Booth, C.H., Bridges, F., Boyce, J.B., Claeson, T., Zhao, Z.X., Cervantes, P.: Local disorder in the oxygen environment around Pr in Y1-xPrxBa2Cu3O7 as measured by x-ray-absorption fine structure. Phys. C Supercond. 235–240, 1033–1034 (1994)CrossRefGoogle Scholar
  20. 20.
    Lin, B.N., Lin, Y.X., Hsu, Y.Y., Liao, J.D., Cheng, W.H., Lee, J.F., Jang, L.Y., Ku, H.C.: Anomalous Pr ordering, Pr L3-edge and Cu K-edge XANES studies for the insulating PrBa2Cu3O7-y system. J. Low Temp. Phys. 131(5–6), 803–808 (2003)CrossRefGoogle Scholar
  21. 21.
    Narlikar, A.V., Gupta, A., Samanta, S.B., Chen, C., Hu, Y., Wondre, F., Wanklyn, B.M., Hodby, J.W.: Nanolevel studies of lattice defects and electronic structure of YBa2Cu3O7 single crystals doped with praseodymium: destruction of superconductivity. Philos. Mag. B 79(5), 717–728 (1999)CrossRefGoogle Scholar
  22. 22.
    Huhtinen, H., Awana, V.P.S., Anurag, G., Hari, K., Laiho, R., Narlikar, A.V.: Pinning centres and enhancement of critical current density in YBCO doped with Pr, Ca and Ni. Supercond. Sci. Technol. 20(9), S159 (2007)CrossRefGoogle Scholar

Copyright information

© The Korean Institute of Metals and Materials 2019

Authors and Affiliations

  1. 1.Department of Physics and Materials Science, Faculty of ScienceChiang Mai UniversityChiang MaiThailand
  2. 2.Department of ScienceTakpittayakhom SchoolTakThailand
  3. 3.Graduate SchoolChiang Mai UniversityChiang MaiThailand
  4. 4.Synchrotron Light Research Institute (Public Organization)Nakhon RatchasimaThailand
  5. 5.Center of Excellence in Materials Science and Technology, Materials Science Research Center, Faculty of ScienceChiang Mai UniversityChiang MaiThailand

Personalised recommendations