Fatigue Strength and Root-Deck Crack Propagation for U-Rib to Deck Welded Joint in Steel Box Girder
- 110 Downloads
Fatigue tests and numerical analysis were carried out to evaluate the fatigue performance at the U-rib to deck welded joint in steel box girder. Twenty specimens were tested corresponding to different penetration rates (80 and 100%) under fatigue bending load, and the fatigue strength was investigated based on hot spot stress (HSS) method. The detailed stress distribution at U-rib to deck welded joint was analyzed by the finite element method, as well as the stress intensity factor of weld root. The test results show that the specimens with fully penetration rate have longer crack propagation life due to the welding geometry, resulting in higher fatigue failure strength. The classification of FAT-90 is reasonable for evaluating fatigue strength by HSS method. The penetration rate has effect on crack propagation angle near the surface, and the 1-mm stress below weld toe and root approves to be more suitable for fatigue stress assessment, because of its high sensitivity to weld geometry than HSS.
KeywordsFatigue test Weld root crack Hot spot stress Fatigue strength 1-mm stress
The research reported herein has been conducted as part of the research Projects Granted by the National Natural Science Foundation of China (51478163 and 51678216). The assistances are gratefully acknowledged.
- AASHTO. (2012). AASHTO LRFD bridge design specifications. Washington, DC: American Association of State Highway and Transportation Officials.Google Scholar
- Baik, B., Yamada, K., & Ishikawa, T. (2008). Fatigue strength of fillet welded joint subjected to plate bending. International Journal of Steel Structures, 8(3), 163–169.Google Scholar
- Hobbacher, A. (2016). Recommendations for fatigue design of welded joints and components. Springer International Publishing.Google Scholar
- JSSC. (2012). Fatigue design recommendations for steel structures. Tokyo: Japanese Society of Steel Construction.Google Scholar
- JTG-D64. (2015). Specifications for design of highway steel bridge. Chinese National Standard. (in Chinese).Google Scholar
- Kolstein, M. H. (2007). Fatigue classification of welded joints in orthotropic steel bridge decks. TU Delft: Delft University of Technology.Google Scholar
- Miki, C. (2006). Fatigue damage in orthotropic steel bridge decks and retrofit works. International Journal of Steel Structures, 6(4), 255–267.Google Scholar