Illumination effects on the physical properties of porous silicon prepared by PECE
- 2 Downloads
Laser-assisted etching process was used to prepare porous silicon on n-type silicon substrate of resistivity 10 Ω cm and <100> orientation incubated in hydrofluoric acid of 25% concentration. The porous layers were prepared using laser diode of 645 nm wavelength illumination with different intensities of about 14 and 20 mW/cm2 and current density of 10 mA/cm2 for a fixed etching time (8 min). The morphology and optical characterization of porous silicon were evaluated. Scanning electron microscopy results demonstrated that the power density is a prominent parameter that controls the morphology of pores. The reflectivity decreased with increase in the highest power density to 0.66% and the peak position of PL results increased with increase in power density and moved toward the blue region. These phenomena were due to changing in the characteristics of the surface morphology the change of Si to nanostructures.
KeywordsPS PL SEM PECE Porosity Reflectivity
We wish to thank Professor M. Ahadian for his assistance with the PL measurements, Razi center for SEM measurements and the Solar Energy Department in the Iraq Ministry of Science and Technology for reflectivity measurements.
- Bisi O, Ossicini S, Pavesi L (2000) Porous silicon: a quantum sponge structure for silicon based optoelectronics. Surf Sci Rep 38(1–3):5Google Scholar
- Han PG, Wong H, Andy HP, Chan, Poon MC (1996) Formation mechanism of light-emitting porous silicon prepared by reactive ions etching. 0-7803-3166-4/96/$5.00©1996IEEEGoogle Scholar
- Kadhim RG et al (2015) Structural, morphological, chemical and optical properties of porous silicon prepared by electrochemical etching. Int J Thin Films Sci Technol 4:199–203Google Scholar
- Kolasinski KW (2004) In: Pandalai SG (ed) Recent research advance in applied physics, vol 7. Transworld Research Network, Kerala, pp 267–292Google Scholar
- Narayanan P (2011) Photoelectrochemical etching of isolated, high aspect ratio microstructures in n-type silicon (100). Diss. Faculty of the Louisiana State University and Agriculture and Mechanical College in partial fulfillment of the requirements f or the degree of Master of Science in Chemical Engineering in The Gordon A. and Mary Cain Department of Chemical Engineering by Purnima Narayanan BE, University of Mumbai, 2011Google Scholar
- Nayef UM, Muayad MW (2013) Typical of morphological properties of porous silicon. Int J Basic Appl Sci IJBAS-IJENS 13(02)Google Scholar