The potential use of wood waste ash nanofiller for improvement of laminated veneer lumber production made from Jabon (Anthocephalus cadamba)
- 19 Downloads
The objective of this research was to improve the bonding properties of laminated veneer lumber (LVL) and its strength made from Jabon (Anthocephalus cadamba) wood bonded using phenol formaldehyde (PF) adhesive mixed with nanofiller made from wood waste ash as substitution material of industrial filler produced from wheat flour. Wood waste ash (WWA) produced from boiler installation of plywood mill was converted into nanoparticle using conventional ball milling for 144 h. WWA nanoparticle was characterized to analyze its particle size, morphology, chemical components and thermal properties. The WWA nanoparticle then added to PF adhesive as a nanofiller under various compositions based on weight: (A) PF 100% + hardener 8%; (B) PF 100% + hardener 8% + wheat flour filler 8%; (C) PF 100% + hardener 8% + WWA nanofiller 2.5% and (D) PF 100% + hardener 8% + WWA nanofiller 8%. These compositions of PF adhesive are then used to produce the LVL from Jabon wood and evaluated its bonding and mechanical properties. Compared to wheat flour filler, PF adhesive filled using nanofiller of 2.5% exhibited the improvement in LVL bonding and strength properties, and the increased values of horizontal shear strength on flat and edge direction were 94% and 107%, respectively. Additionally, the increased values of modulus of rupture (MOR) on flat and edge direction were 62% and 32%, respectively, and modulus of elasticity (MOE) on flat and edge direction was 39% and 16%, respectively.
KeywordsPF adhesive Wood waste ash nanofiller Wheat flour filler Bonding properties Jabon wood LVL
The authors wish to thank the Institute of Research and Community Service, Institut Teknologi Bandung for the financial support through the Program of Research, Community Service and Innovation (P3MI program), year 2017. The authors also thank the Dean of School of Life Sciences and Technology, Institut Teknologi Bandung and Head of Division of Research and Development of Wood Composite Industry PT. Sumber Graha Sejahtera, at Tangerang, Banten Province, Indonesia, for the supporting of research facilities.
- Abdul Khalil HPS, Fizree HM, Jawaid M, Alattas OS (2011) Preparation and characterization of nano structured materials from oil palm ash: a bio-agricultural waste from oil palm mill. BioResources 6(4):4537–4546Google Scholar
- Buamscha MG, Altland JE, Sullivan DM, Horneck DA, Cassidy J (2007) Chemical and physical properties of douglas fir bark relevant to the production of container plants. HortScience 42(5):1281–1286Google Scholar
- Fan M, Dai D, Huang B (2012) Fourier transform infrared spectroscopy for natural fibres. In: Salih S (ed.) Fourier transform-materials analysis, ISBN: 978-953-51-0594-7, InTech, Rijeka, Croatia, pp 45–68. (http://www.intechopen.com/books/fourier-transform-materials-analysis/fourier-transform-infraredspectroscopy-for-natural-fibres). Accessed 4 October 2013Google Scholar
- Frihart CR (2004) Adhesive interactions with wood. In: Winandy JE, Kamke FA (eds.) Fundamentals of composite processing, proceedings of a workshop, November 5–6, 2003; Madison, WI. Gen. Tech. Rep. FPL-GTR-149. Madison, WI: U.S. Department of Agriculture, Forest Service, Forest Products LaboratoryGoogle Scholar
- Frihart CR (2005) Wood adhesion and adhesives. In: Rowell RM (ed) Handbook of wood chemistry and wood composites. Fla.: CRC Press, Boca Raton, pp 215–278Google Scholar
- [JAS] Japanese Agricultural Standard (2008) Japanese agricultural standard for laminated veneer lumber. Notification No. 701, Ministry of Agriculture, Forestry and Fisheries, dated May 13, 2008Google Scholar
- T Sellers Jr., Miller GD, Smith W (2005) Tool wear properties of five extender/fillers in adhesive mixes for plywood. For Prod J 55(3):27–31Google Scholar
- Sutrisno, Purwasasmita BS, Alamsyah EM, Syamsudin TS (2015a) Synthesis, characterization and functionalization of bio-based nano filler made from ash resulted from wood waste burning to reduce formaldehyde emission of bio-composite products (text in Indonesian). Res Dev Nanotechnol Indones 2(1):1–19Google Scholar