Effect of Annealing on Mechanical Properties and Metallurgical Factors of Ultrafine-Grained 6082 Al Alloy

  • N. KumarEmail author
  • G. M. Owolabi
  • R. Jayaganthan
  • G. Warner
Technical Paper
  • 41 Downloads

Abstract

In the present work, cryorolling (CR) (rolling temperature is − 196 °C) followed by annealing (AN) (100–400 °C for 1 h) of 6082 Al alloy has been performed. The main objective of this study was to investigate the thermal stability of the ultrafine-grained 6082 Al alloy, for higher temperature applications. The mechanical properties of the CR and the CR + AN 6082 Al alloy were investigated and correlated with the microstructure with the help of a transmission electron microscope (TEM). The hardness and the tensile strength of the CR + AN (150 °C) 6082 Al alloy were significantly improved up to 95% and 40%, respectively, when compared to the solution-treated (ST) 6082 Al alloy. The main reason behind the mechanical strength improvement was dislocation strengthening and precipitation strengthening. Thermal stability of the CR 6082 Al alloy was found up to a high annealing temperature of 300 °C due to the pinning of grain boundaries by precipitates evaluation during annealing by Zener drag effect. The formation of β″-phase, β′-phase and stable β-phase occurred at the annealing temperatures of 175 °C for 1 h, 200 °C for 1 h and 250 °C for 1 h, respectively.

Keywords

Cryorolling Precipitation Thermal stability TEM 6082 Al alloy 

Notes

Acknowledgements

The authors appreciate and specially acknowledge the financial support from the Department of Defense via grant Contract # W911NF-15-1-0457 under the direct supervision of Patricia Huff (HBCU/MI Program Manager, USA Army Research Office).

References

  1. 1.
    Saito Y, Tsuji N, Utsonomis H, and Sakai T, Acta Mater, 47 (1999) 579.CrossRefGoogle Scholar
  2. 2.
    Valiev R Z, Islamgaliev R K, and Alexandrov I V, Prog Mater Sci 45 (2000) 103.CrossRefGoogle Scholar
  3. 3.
    Kim J K, Kim H K, Park J W, and Kim W J, Scripta Mater 53 (2005) 1207.CrossRefGoogle Scholar
  4. 4.
    Loucif A, Figueiredo R B, Baudin T, Brisset F, and Langdon T G, Mater Sci Eng A 527 (2010) 4864.CrossRefGoogle Scholar
  5. 5.
    Shanmugasundaram T, Murty B S, and Sarma V S, Scripta Mater 54 (2006) 2013.Google Scholar
  6. 6.
    Lee Y B, Shin D H, Park K T, and Nam W J, Scripta Mater 51 (2004) 355.CrossRefGoogle Scholar
  7. 7.
    Cheng S, Zao Y H, Zhu Y T, and Ma E, Acta Mater 55 (2007) 5822.CrossRefGoogle Scholar
  8. 8.
    Panigrahi S K, and Jayaganthan R, Mater Sci Forum 584–586 (2008) 734.CrossRefGoogle Scholar
  9. 9.
    Panigrahi S K, and Jayaganthan R, Mater Sci Eng A 492 (2008) 300.CrossRefGoogle Scholar
  10. 10.
    Rao P N, Panigrahi S K, and Jayaganthan R, Mater Sci Tech 26 (2010) 371.CrossRefGoogle Scholar
  11. 11.
    Kang U G, Lee J C, Jeong S W, and Nam W J, J Mater Sci 45 (2010) 4739.CrossRefGoogle Scholar
  12. 12.
    Dobatkin S V, Zakharov V V, and Rokhlin L L, Mater Sci Forum 503–504 (2006) 399.CrossRefGoogle Scholar
  13. 13.
    Nurislamova G, Sauvage X, Murashkin M, Islamgaliev R, and Valiev R, Phil Mag Lett 88 (2008) 459.CrossRefGoogle Scholar
  14. 14.
    Kumar N, Goel S, Jayaganthan R, and Brokmeier H G, Metallography, Microstructure, and Analysis 4 (2015) 411.Google Scholar
  15. 15.
    Morris D G, and Munoz-Morris M A, Acta Mater 50 (2002) 4047.CrossRefGoogle Scholar
  16. 16.
    Yassar R S, Field D P, and Weiland H, Metall Mater Trans A 36A (2005) 2059.CrossRefGoogle Scholar
  17. 17.
    Sushanta Kumar Panigrahi • R. Jayaganthan J Mater Sci (2010) 45:5624.CrossRefGoogle Scholar
  18. 18.
    Urrutia I G, Munoz-Morris M A, and Morris D G, Mater Sci Eng A 394 (2005) 399.CrossRefGoogle Scholar
  19. 19.
    Ou B L, Yang J G, and Wei M Y, Metall Mater Trans A 38A (2007) 1960.Google Scholar
  20. 20.
    Doherty R D, Mater Sci 16 (1982) 1.Google Scholar
  21. 21.
    Esmaeili S, Wang S X, Lloyd D J, and Poole W J, Metall Mater Trans A 34A (2003) 751.Google Scholar
  22. 22.
    Weatherly G C, Perovic A, Mukhopadhyay N K, Llyod D J, and Perovic D D, Metall Mater Trans A 32 (2001) 213.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2019

Authors and Affiliations

  • N. Kumar
    • 1
    Email author
  • G. M. Owolabi
    • 1
  • R. Jayaganthan
    • 2
  • G. Warner
    • 1
  1. 1.Department of Mechanical EngineeringHoward UniversityWashingtonUSA
  2. 2.Department of Engineering DesignIndian Institute of Technology MadrasChennaiIndia

Personalised recommendations