The Effect of Peak Temperature on HAZ Microstructure and Toughness of V- and Nb-Bearing Microalloyed Steels

  • Bin Wang
  • Jing HuEmail author
  • Yiwen Hu
  • L. Pu
Technical Paper
  • 34 Downloads

Abstract

Welding heat cycle processes of V- and Nb-bearing microalloyed steels at different peak temperatures (1350, 1100, 950, 800 and 650 °C) were simulated by Gleeble 3500. The microstructure and toughness of two steels were investigated by optical microscopy (OM), scanning electron microscopy (SEM) and low-temperature impact toughness test (− 40 °C). The results indicated that the microstructure of both V and Nb steels consisted of the lath bainite (LB), granular bainite (GB), polygonal ferrite (PF) and a small amount of martensite austenite (MA) islands at 1350 °C, and acicular ferrite (AF) was also observed in V steel. Ferrite (F) phase became uniform, and hard phase LB decreased with the decrease in peak temperature. Impact tests indicated that both the two steels exhibited the best impact toughness (32.23 and 30.90 J) at the peak temperature of 950 °C. The impact toughness of V steel was better than of Nb steel all the time, which was consistent with the analysis of microfracture.

Keywords

V- and Nb-bearing steels Peak temperature Heat-affected zone Toughness 

Notes

Acknowledgements

The research work was also supported by the National Nature Science Foundation of china (No. 51602269) and The Technology Project of Nanchong and SWPU Cooperation (No. 18SXHZ0013). The research work (TIIM-D-18-00069.1, DOI: 10.1007/s12666-018-1497-3) was also supported by the key Laboratory of Oil and Gas Field Materials in Sichuan Province of China (No. X151518KCL44).

References

  1. 1.
    Hulka K, Kern A, and Schriever U, Mater Sci Forum 500–501 (2005) 519.CrossRefGoogle Scholar
  2. 2.
    Yu S F, and Qian B N, Mater Res Trans 18 (2004) 405.Google Scholar
  3. 3.
    Kim B C, Lee S, Kim N J, and Lee D Y, Metall Trans 22 (1991) 139.CrossRefGoogle Scholar
  4. 4.
    Davis C L, and King J E, Metall Trans 25 (1994) 563.CrossRefGoogle Scholar
  5. 5.
    Matsuda F, Ikeuchi K, Liao J, Effect of weld thermal cycles on the HAZ toughness of SQV-2A pressure vessel steel [M]. 4th International Conference on Trends in welding Research (1995).Google Scholar
  6. 6.
    Fairchild D P, Bangaru N V, Koo J Y, Harrison P L, and Ozekcin A, Weld J 470 (1991) 321s.Google Scholar
  7. 7.
    Tang M Y, Introduction to Welding Physics Metallurgy, Machinery Industry Press, Jing Bei, 1989.Google Scholar
  8. 8.
    Crowther D N, Li Y, Green M J W, Mitchell P S, and Baker T N, ISIJ Int, 41 (2001) 46.CrossRefGoogle Scholar
  9. 9.
    Shi Z R, Wang R Z, and Wang Q F, Kang Tieh Iron Steel, 50 (2015) 70.Google Scholar
  10. 10.
    Ikeuchi K, Matsuda F, and Liao J, Weld Inter 10 (1996) 552.CrossRefGoogle Scholar
  11. 11.
    Chen X W, Liao B, and Qiao G Y, J Iron Steel Res 20 (2013) 53.CrossRefGoogle Scholar
  12. 12.
    Hong Y C, Heat Treat, 17 (2002) 16.Google Scholar
  13. 13.
    Wang L T, Zhao R H, and Mao Y J, J. Iron Steel Res 2 (1984) 97.Google Scholar
  14. 14.
    Han X R, Wide Heavy Plate 12 (2006) 39.Google Scholar
  15. 15.
    Zhang L, and Kannengiesser T, Mater Sci Eng 613 (2014) 326.CrossRefGoogle Scholar
  16. 16.
    Fahlström K, Hutchinson B, and Komenda J, Iron Steel Vanadium Titanium 36 (2015) 104.Google Scholar
  17. 17.
    Wang Y G, li F Y, Heat Treat Met 30 (2005) 27.Google Scholar
  18. 18.
    Wang B, Hu Y W, and Yang X F, Met Sci J 33 (2016) 1004.Google Scholar

Copyright information

© The Indian Institute of Metals - IIM 2019

Authors and Affiliations

  1. 1.School of Materials Science and EngineeringSouthwest Petroleum UniversityChengduChina
  2. 2.Sichuan Provincial Research Center of Welding Engineering TechnologyChengduChina
  3. 3.School of Petroleum and Nature Gas EngineeringSouthwest Petroleum UniversityChengduChina

Personalised recommendations