Microstructure and Mechanical Properties in Warm Forged 27MnSiVS6 Microalloyed Steel

  • Karthick Raghu
  • G. Balachandran
  • D. Ravichandar
Technical Paper
  • 18 Downloads

Abstract

The mechanical properties and microstructure of warm forged 27MnSiVS6 steel was evaluated at temperatures between 850 and 760 °C. The strength values showed enhancement by about 50 MPa, while the impact toughness was almost doubled. The microstructure showed increase in ferrite content with decreasing warm forging temperature, and the ferritic grains showed finer grain structure. While the increased ferrite content resulted in limiting the strength enhancement, the fineness of the grain structure led to a significant enhancement in impact toughness. The ductile-to-brittle transition temperature was pushed to a significantly low temperature in the warm forged steel compared to the hot-rolled steel. The microstructure evolution at various stages of processing was brought out.

Keywords

Micro alloyed steel Warm forging temperature deformation Toughness Fine grains 

Notes

Acknowledgements

The authors wish to thank Ms. V Madhuri for the SEM support and the colleagues in QAD for the support in steel characterization.

References

  1. 1.
    Fisher K, Schweiger H, Hasenberger J, and Dremel H, New Tool Steel for Warm and Hot Forging, 6th International Tooling Conference, Karlstad, Sweden, September (2002) p 10.Google Scholar
  2. 2.
    Jahazi M, and Eghbali B, J Mater Process Technol 113 (2001) 594.CrossRefGoogle Scholar
  3. 3.
    Zhang X, Cai Q, Zhou G, Chen Q, and Xiong Y, J Mater Sci 46 (2011) 1789.CrossRefGoogle Scholar
  4. 4.
    Zajac S, Siwecki T, Hutchinso W B, and Lagnebo R, ISIJ Int 38 (1998) 1130.CrossRefGoogle Scholar
  5. 5.
    Majta J, and Bator A, J Mater Process Technol 125–126 (2002) 77.CrossRefGoogle Scholar
  6. 6.
    Songa R, Ponge D, Raabe D, Speer J G, and Matlock D K, Mater Sci Eng A 441 (2006) 1.CrossRefGoogle Scholar
  7. 7.
    Zhao P, and Boyd J D, Mater Sci Technol 23 (2007) 1186.CrossRefGoogle Scholar
  8. 8.
    Eghbali B, Mater Sci Eng A 527 (2010) 3407.CrossRefGoogle Scholar
  9. 9.
    Spena P R, and Firrao D, Mater Sci Eng A 560 (2013) 208.CrossRefGoogle Scholar
  10. 10.
    Sas J, Kvackaj T, Milkovic O, and Zemko M, Material 9 (2016) 971.CrossRefGoogle Scholar
  11. 11.
    Shena X J, Tanga S, Wua Y J, Yanga X L, Chena J, Liua X Y, Misra R D K, and Wang G D, Mater Sci Eng A 685 (2017) 194.CrossRefGoogle Scholar
  12. 12.
    Caminagaa C, Botta Filhob W J, Silvaa M L N, and Buttona S T, Proc Eng 10 (2011) 512.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  • Karthick Raghu
    • 1
  • G. Balachandran
    • 1
  • D. Ravichandar
    • 1
  1. 1.JSW Steel Limited, Salem WorksSalemIndia

Personalised recommendations