Investigations for Surface Hardness of Aluminum Matrix Composites with Hybrid Reinforcement

  • Swarndeep Singh
  • Rupinder Singh
  • Simranpreet Singh Gill
Technical Paper
  • 20 Downloads

Abstract

This work focuses on the investigations of hybrid reinforcement of SiC/Al2O3 as dual particle size and triple particle size (TPS) on the surface hardness of hybrid aluminum matrix composite (AMC) prepared with synergistic combination of fused deposition modeling, vacuum molding (V) process and stir casting. It was observed that TPS-based SiC resulted into highest microhardness of 45HV. Further, ANOVA revealed that the percentage contribution of particle size and type of reinforcement on surface hardness of AMC were 27.30% and 48.72%, respectively. The best parametric setting (of input parameters) for microhardness is: particle size—TPS, type of reinforcement—SiC, vacuum pressure—350 mm of Hg, sand grain size—70 (AFS no.), vibration time—4 s. and composition/proportion of reinforcement in Al matrix—10%, respectively, and overall, 5.1% improvement in microhardness was observed at proposed parametric setting. The presence of Al2O3/SiC responsible for the improvement in microhardness was supported by photomicrographs.

Keywords

Hybrid Al-MMC DPS TPS V-process Microhardness 

Notes

Acknowledgements

The authors are thankful to I. K.G. Punjab Technical University, Kapurthla (Pb.), India, and Guru Nanak Dev Engineering College, Ludhiana (Pb.), India, for providing this opportunity and support.

References

  1. 1.
    Iqbal A A, and Dewan M N, Int J Appl Eng Res 11 (2016) 10408.Google Scholar
  2. 2.
    Sirahbizu Yigezu B, Mahapatra M M, and Jha P K, J Miner Mater Charact Eng 1 (2013) 124.Google Scholar
  3. 3.
    Matsunaga T, Kim J K, Hard Castle S, and Rohatgi P K, Trans AFS 104 (1996) 1097.Google Scholar
  4. 4.
    Hayrettin Ai, Tolga K, Ercan C, and Huseyin Ç, Tribol Int 39 (2006) 213.CrossRefGoogle Scholar
  5. 5.
    Rajmohan T, Palanikumar K, and Ranganathan S, Trans Nonferrous Met Soc China 23 (2013) 2509.CrossRefGoogle Scholar
  6. 6.
    Devaraju A, Kumar A, and Kotiveerachari B, Mater Des 45 (2013) 576.CrossRefGoogle Scholar
  7. 7.
    Ramnath B V, Elanchezhian C, Jaivignesh M, Rajesh S, Parswajinan C, and Ghias A S A, Mater Des 58 (2014) 332.CrossRefGoogle Scholar
  8. 8.
    Suresha S, and Sridhara B K, Compos Sci Technol 70 (2010) 1652.CrossRefGoogle Scholar
  9. 9.
    Uvaraja V C, and Natrajan N, J Miner Mater Charact Eng 11 (2012) 757.Google Scholar
  10. 10.
    Prasad D S, Shoba C, and Ramanaiah N, J Mater Res Technol 3 (2014) 79.CrossRefGoogle Scholar
  11. 11.
    Pugalenthi P, Jayaraman M, and Natarajan A, Appl Mech Mater 766 (2015) 246.CrossRefGoogle Scholar
  12. 12.
    Radhika N, Balaji T V, and Palaniappan S, J Eng Sci Technol 10 (2015) 134.Google Scholar
  13. 13.
    Hashim J, Looney L, and Hashmi M S J, J Mater Proc Technol 92 (1999) 1.CrossRefGoogle Scholar
  14. 14.
    Kubo Y, Nakata K, Akita K K, and Gouwens P R, AFS Trans 81 (1973) 529.Google Scholar
  15. 15.
    Liu Z, Hu J, Wang Q, Ding W, Zhu Y, Lu Y, and Chen W, J Mater Proc Technol 120 (2002) 94.CrossRefGoogle Scholar
  16. 16.
    Kumar P, and Gaindhar J L, Trans Am Foundrym Soc 104 (1997) 635.Google Scholar
  17. 17.
    Singh R, Singh J, and Singh J, J Inst Eng (India) Ser C 93 (2012) 325.Google Scholar
  18. 18.
    Singh R, J Inst Eng India Ser C 94 (2013) 93.CrossRefGoogle Scholar
  19. 19.
    Boparai K S, and Singh R, Appl Mech Mater 330 (2013) 91.CrossRefGoogle Scholar
  20. 20.
    Singh R, and Singh G, J Manuf Process 19 (2015) 142.CrossRefGoogle Scholar
  21. 21.
    Singh R, Podder D, and Singh S, Trans Indian Inst Metals 68 (2015) 791.CrossRefGoogle Scholar
  22. 22.
    Sun Q, and Rizvi G M, Rapid Prototyp J 14 (2008) 72.CrossRefGoogle Scholar
  23. 23.
    Hashim L, Looney L, and Hashmi M S J, J Mater Process Technol 92 (1999) 1.CrossRefGoogle Scholar
  24. 24.
    Kumar G B V, Rao C S P, and Selvaraj N, J. Miner Mater Charac Eng 10 (2011) 59.Google Scholar
  25. 25.
    Sinha A, and Farhat Z, Mater Sci Appl 6 (2015) 549.CrossRefGoogle Scholar
  26. 26.
    Islam M A, and Farhat Z N, Tribol Int 44 (2011) 498.CrossRefGoogle Scholar
  27. 27.
    Kok M, J Mater Process Technol 161 (2005) 381.CrossRefGoogle Scholar
  28. 28.
    Rahimian M, Parvin N, and Ehsani N, Mater Sci Eng A 527 (2010) 1031.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  1. 1.IKG Punjab Technical UniversityKapurthalaIndia
  2. 2.Department of Production EngineeringGuru Nanak Dev Engineering CollegeLudhianaIndia
  3. 3.Department of Mechanical EngineeringBeant College of Engineering and TechnologyGurdaspurIndia

Personalised recommendations