Friction Welding of Electron Beam Melted γ-TiAl Alloy Ti–48Al–2Cr–2Nb

  • G. S. SankarEmail author
  • G. M. Karthik
  • Ashfaq Mohammad
  • Ravi Kumar
  • G. D. Janaki Ram
Technical Paper
  • 70 Downloads

Abstract

In the current work, rotary friction welding of electron beam melted (EBM) γ-TiAl alloy Ti–48Al–2Cr–2Nb (at%) was investigated. Welding experiments were conducted using cylindrical bars of 12 mm diameter and 70 mm height in as-fabricated and heat treated (1275 °C/2 h/furnace cooling) conditions. No cracking problems were encountered during friction welding of as-fabricated EBM samples. However, in as-welded condition, the joints did not perform well in tensile tests and failures were observed to invariably occur at the weld interface. Friction welded joints produced in heat treated EBM samples were also found to suffer from the same problem. In both the cases, the weld region showed fine, fully lamellar γ + α2 microstructure and relatively high hardness. In order to overcome the problem, a post-weld heat treatment (PWHT) was carried out at 1275 °C/2 h/furnace cooling. After the PWHT, the weld region showed a more desirable duplex microstructure consisting of equiaxed primary γ and relatively coarser lamellar γ + α2. The PWHTed joints showed satisfactory tensile properties, and no failures were observed at the weld interface.

Keywords

Titanium aluminide Ti–48Al–2Cr–2Nb Additive manufacturing Electron beam melting Friction welding 

References

  1. 1.
    Djanarthany S, Viala J C, Bouix J, Mater Chem Phys 72 (2001) 301.CrossRefGoogle Scholar
  2. 2.
    Srivastava D, Chang I T H, Loretto M H, Mater Des 21 (2000) 425.CrossRefGoogle Scholar
  3. 3.
    Liu W, DuPont J N, Metall Mater Trans A 35a (2004) 1133.Google Scholar
  4. 4.
    Qu H P and Wang H M, Mater Sci Eng A 466 (2007) 187.CrossRefGoogle Scholar
  5. 5.
    Sharman A R C, Hughes J I, Ridgway K, Intermetallics, 93 (2018) 89.CrossRefGoogle Scholar
  6. 6.
    Löber L, Schimansky F P, Kühn U, Pyczak F, Eckert J, J Mater Process Techno 214 (2014) 1852.CrossRefGoogle Scholar
  7. 7.
    Gussone J, Hagedorn Y C, Gherekhloo H, Kasperovich G, Merzouk T, Hausmann J, Intermetallics 66 (2015) 133.CrossRefGoogle Scholar
  8. 8.
    Thomas M, Malot T, Aubry P, Colin C, Vilaro T, Bertrand P, Mater High Temp 33 (2016) 571.CrossRefGoogle Scholar
  9. 9.
    Murr L E, Gaytan S M, Ceylan A, Martinez E, Martinez J L, Hernandez D H, Machado B I, Ramirez D A, Medina F, Collins S, Wicker R B Acta Mater 58 (2010) 1887.CrossRefGoogle Scholar
  10. 10.
    Biamino S, Penna A, Ackelid U, Sabbadini S, Tassa O, Fino P, Pavese M, Gennaro P, Badini C, Intermetallics 19 (2011) 776.CrossRefGoogle Scholar
  11. 11.
    Tang H P, Yang G Y, Jia W P, He W W, Lu S L, Qian M, Mater Sci Eng A 636 (2015) 103.CrossRefGoogle Scholar
  12. 12.
    Baudana G, Biamino S, Klöden B, Kirchner A, Weißgärber T, Kieback B, Pavese M, Ugues D, Fino P, Badini C, Intermetallics 73 (2016) 43.CrossRefGoogle Scholar
  13. 13.
    Mohammad A, Alahmari A M, Mohammed M K, Renganayagalu R K, Moiduddin K Materials 10 (2017) 211.CrossRefGoogle Scholar
  14. 14.
    Todai M, Nakano T, Liu T, Yasuda H Y, Hagihara K, Cho K, Ueda M, Takeyama M, Addit Manuf 13 (2017) 61.CrossRefGoogle Scholar
  15. 15.
    Gibson I, Stucker B, Rosen D W, Additive Manufacturing Technologies, Springer, New York (2010) p 136.Google Scholar
  16. 16.
    Hernandez J, Murr L E, Gaytan S M, Martinez E, Medina F, Wicker R B, Metallogr Microstruct Anal. 1 (2012)14.CrossRefGoogle Scholar
  17. 17.
    Baeslack W A, McQuay P A, Lee D S, Fletcher E D, Mater Charact 31 (1993) 197.CrossRefGoogle Scholar
  18. 18.
    Su M, Lang Z, Zheng L, Yan J, Guan K, Zhang H, J Mater Res. 15 (2012) 455.CrossRefGoogle Scholar
  19. 19.
    Cao J, Qi J, Song X, Feng J, Materials, 7 (2014) 4930.CrossRefGoogle Scholar
  20. 20.
    David S A, Horton J A, Goodwin G M, Phillips D H, Reed R W, Weld J Res Suppl (1990) 133s.Google Scholar
  21. 21.
    Baeslack W A, Joining of Gamma Titanium Aluminides (2003) report (# AFRL-ML-WP-TR-2003-4036).Google Scholar
  22. 22.
    Ventzke V, Bohm K H, Kocak M, Riekehr S, Horstmann M, Merhof P, Watzlaw M, J Mater Sci Technol 37 (2006) 649.Google Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  • G. S. Sankar
    • 1
    Email author
  • G. M. Karthik
    • 1
  • Ashfaq Mohammad
    • 2
  • Ravi Kumar
    • 3
  • G. D. Janaki Ram
    • 1
  1. 1.Joining and Additive Manufacturing Laboratory, Department of Metallurgical and Materials EngineeringIndian Institute of Technology Madras, Tamil NaduChennaiIndia
  2. 2.Department of Mechanical EngineeringSheffield UniversitySheffieldUK
  3. 3.Laboratory for High Performance Ceramics, Department of Metallurgical and Materials EngineeringIndian Institute of Technology Madras, Tamil NaduChennaiIndia

Personalised recommendations