, Volume 71, Issue 11, pp 2759–2763 | Cite as

Grain Refinement of B319 Alloy Using Spark Plasma Sintered Al–Ti–C Grain Refiners

  • Anil Prasad
  • Justin Mok
  • Levi Lafortune
  • Lukas Bichler
Technical Paper
  • 22 Downloads

Abstract

The B319 aluminum alloy is a candidate material for automotive applications, where engineers and material designers are seeking to improve vehicle efficiency through vehicle weight reduction. Although the alloy has many desirable properties, such as excellent castability and moderate strength-to-weight ratio, efforts to further enhance the alloy’s strength via the grain refinement approach play a key role to a wider adaptation of the alloy. However, there remain challenges related to the efficient dispersion of inoculating particles in the liquid alloy during casting. The present research has focused on examining the grain refining ability of various novel grain refiners produced via the spark plasma sintering powder metallurgy process. Two novel grain refiners [aluminum–titanium carbide (Al–TiC) and aluminum–titanium–carbon black (Al–Ti–Cb)] were produced at high and low concentrations and then added to the molten B319 alloy. The grain refiners got dispersed within the melt, thus overcoming the need for external melt stirring or treatment. The high concentration formulations for both Al–TiC and Al–Ti–Cb achieved a reduction in the average grain size by 31% and 25%, respectively.

Keywords

Spark plasma sintering B319 Grain refinement Al–TiC 

References

  1. 1.
    Starke E, and Staley J, Prog Aerosp Sci 32 (1996) 131.CrossRefGoogle Scholar
  2. 2.
    Davis J R, Aluminum and Aluminum Alloys, ASM International, Russell Towns (1993) 355.Google Scholar
  3. 3.
    Kalhapure M G, and Dighe P M, Int J Sci Res 6 (2013) 38.Google Scholar
  4. 4.
    Samuel A, Doty H, Valtierra S, and Samuel F, Mater Des 52 (2013) 2457.CrossRefGoogle Scholar
  5. 5.
    -Yan L, Zhang Y, Li X, Li Z, Wang F, Liu H, and Xiong B, Prog Nat Sci Mater Int 24 (2014) 97.CrossRefGoogle Scholar
  6. 6.
    Guan R-G, and Tie D, Acta Metall Sin (Engl Lett) 30 (2017) 409.Google Scholar
  7. 7.
    Malekan M, and Shabestari S, Metall Mater Trans A 40 (2009) 3196.CrossRefGoogle Scholar
  8. 8.
    Kumar V, and Bichler L, Trans Indian Inst Metals 68 (2015) 1173.CrossRefGoogle Scholar
  9. 9.
    Birol Y, Materials 7 (2014) 1749.Google Scholar
  10. 10.
    Toptan F, Kerti I, Dablilar S, Sagin A, Karadeniz O F, and Ambarkutuk A, Light Met 2011, Springer, Cham (2011) 821.Google Scholar
  11. 11.
    Birol Y, J Alloys Compounds 458 (2008) 271.CrossRefGoogle Scholar
  12. 12.
    Murty B S, Kori S A, and Chakraborty M, Int Mater Rev 47 (2002) 3.CrossRefGoogle Scholar
  13. 13.
    Lafortune L, MASc Thesis, University of British Columbia Okanagan, Canada.Google Scholar
  14. 14.
    Vinod Kumar G S, Murty B S, Chakraborty M, J Alloy Compounds 472 (2009) 112.CrossRefGoogle Scholar
  15. 15.
    Vinod Kumar G S, Murty B S, and Chakraborty M, J Alloy Compounds 396 (2005) 143.CrossRefGoogle Scholar
  16. 16.
    Ding W, Zhu J, Zhao W, and Xia T, Adv Metals Res 652 (2013) 1072.Google Scholar
  17. 17.
    Schwertz M, Lemonnier S, Barraud E, Carradò A, Vallat M-F, and Nardin M, Powder Metall 58 (2015) 87.Google Scholar
  18. 18.
    Shen Z, Johnsson M, Zhao Z, and Nygren M, J Am Ceram Soc 85 (2002) 1921.CrossRefGoogle Scholar
  19. 19.
    Anselmi-Tamburini U, Garay J, and Munir Z, Scr Mater 54 (2006) 823.CrossRefGoogle Scholar
  20. 20.
    Mok J, Grain Refinement of B319 Alloy Using Spark Plasma Sintered AlTiC Grain Refiners, MASc Thesis, University of British Columbia, Canada.Google Scholar
  21. 21.
    Davis T, Bichler L, D’Elia F, and Hort N, J Alloy Compounds 759 (2018) 70.CrossRefGoogle Scholar
  22. 22.
    Azad A, Bichler L, Elsayed A, Int J Metalcasting 7 (2013) 49.CrossRefGoogle Scholar
  23. 23.
    Davis T, Bichler L, D’Elia F, and Hort N, Magnesium Technology 2017,  The Minerals, Metals & Materials Series. Springer, Cham (2017) 653.Google Scholar
  24. 24.
    Davis T, Bichler L, Sediako D, and Balogh L, Magnesium Technology 2018, The Minerals, Metals & Materials Series. Springer, Cham (2018) 425Google Scholar
  25. 25.
    Turen Y, Mater Des 49 (2013) 1009.CrossRefGoogle Scholar
  26. 26.
    Behera R, Chatterjee D, and Sutradhar G, Am J Mater Sci 2 (2012) 53.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  • Anil Prasad
    • 1
  • Justin Mok
    • 1
  • Levi Lafortune
    • 1
  • Lukas Bichler
    • 1
  1. 1.School of EngineeringUniversity of British Columbia OkanaganKelownaCanada

Personalised recommendations