Microstructural Changes in Hypoeutectic Al–Si Alloys by Low Shear and Vibration Induced Melt Conditioning Setup

  • Shristy Jha
  • G. Sree Lakshmi Aditya
  • A. Mandal
  • B. K. Dhindaw
Technical Paper

Abstract

In the present work, refinement of microstructure in hypoeutectic Al–Si alloys, i.e., A356 and Al–7wt%Si has been reported. One of the mechanical technique, melt conditioning, was used to refine the microstructure. The technique involved subjecting the melt to low shear force by passing it through a slope at a temperature above its liquidus temperature. In addition to the shear force, vibration was induced into the melt during its flow by a simple setup for melt conditioning. Shear force along with vibrations led to enhanced refinement in both the alloys, the most prominent being A356 alloy. It has been suggested that higher fraction of fragmented oxide particles/films into the molten A356 alloy during the flow before solidification in the mould could enhance the nucleation centres. It was concluded that the bi-oxides such as MgAlO4 acted as effective heterogeneous nucleants for α-Al.

Keywords

A356 Melt conditioning Grain refinement Inclined slope 

References

  1. 1.
    Murty B S, Kori S A, Chakraborty M, Murty B S, Kori S A, and Chakraborty M, Grain refinement of aluminium and its alloys by heterogeneous nucleation and alloying Grain refinement of aluminium and its alloys by heterogeneous nucleation and alloying, vol. 6608, no. September (2016).Google Scholar
  2. 2.
    Barekar N S and Dhindaw B K, Mater Manuf Process 29 (2014) 651.CrossRefGoogle Scholar
  3. 3.
    Scamans G, Li H, and Fan Z, in Melt Conditioned Casting of Aluminum Alloys (2012) p. 1395.CrossRefGoogle Scholar
  4. 4.
    Impey S A, Stephenson D J, and Nicholls J R, Mater Sci Technol 4 (1988) 1126.CrossRefGoogle Scholar
  5. 5.
    Li H T, Wang Y, and Fan Z, Acta Mater 60 (2012) 1528.CrossRefGoogle Scholar
  6. 6.
    Wang Y, Li H T, and Fan Z, Trans Indian Inst Met 65 (2012) 653.CrossRefGoogle Scholar
  7. 7.
    Barekar N S, Pradhan R, and Dhindaw B K, J Mater Eng Perform 23 (2014) 439.CrossRefGoogle Scholar
  8. 8.
    KeeHyun Kim, Surf Interface Anal 47 (2015) 429.CrossRefGoogle Scholar

Copyright information

© The Indian Institute of Metals - IIM 2018

Authors and Affiliations

  • Shristy Jha
    • 1
  • G. Sree Lakshmi Aditya
    • 1
  • A. Mandal
    • 1
  • B. K. Dhindaw
    • 1
  1. 1.School of Minerals, Metallurgical and Materials EngineeringIndian Institute of Technology BhubaneswarBhubaneswarIndia

Personalised recommendations