Comparative Evaluation of Vanadium Ions in Na2O-CaO-P2O5 and Na2O-CaF2-P2O5 Glasses by Spectroscopic Analysis and Effects of Gamma-Rays Interaction
- 11 Downloads
Ternary soda lime phosphate glasses doped with V2O5 from the two varieties (Na2O-CaO-P2O5, Na2O-CaF2-P2O5) were prepared. The spectral analysis of both optical and FT infrared absorption were conducted for the equipped undoped and two V2O5-doped glasses (0.5 and 1% V2O5) before and after gamma irradiation. ESR technique is used for two chosen samples to confirm the spectral data. Strong UV bands are identified in all the samples but the V2O5-doped samples show additional three broad visible bands. The UV absorption is assumed to be related to the contamination by trace iron impurities, while the visible range bands are attributed to the existence of two species (V3+ and V4+) ions due to the host phosphate glass has reducing effect. FT infrared absorption spectra reveal characteristic vibrational bands due to phosphate groups and the two glass systems show similar IR spectra. Gamma irradiation results in new visible band, while in the irradiated V2O5—doped samples no new band was observed. The induced band in the base glass is related to the formation of (POHC) or (NBOHC) and the presence of vanadium ions causes some shielding behavior toward gamma irradiation. The optical and FTIR results show no distinct variations between the effects of the modifier CaO or CaF2. ESR measurements indicate the presence of unpaired vanadium species in the studied host phosphate glasses.
KeywordsPhosphate glass V2O5 Optical FTIR Gamma irradiation ESR
Unable to display preview. Download preview PDF.
The present work was supported by the National Research Center. We are deeply grateful for the support.
- 1.Martin SW (1991) Review of the structures of phosphate glasses. Eur J Solid State Inorg Chem 28:163–205Google Scholar
- 2.Guo G (1998) Optical and thermal properties of some chemically durable lead phosphate glasses. Glass Technol 39:138–141Google Scholar
- 6.Ehrt D (2015) Rev Phys Chem Glass: Eur J Glass Sci Technol (B) 56(6):217Google Scholar
- 7.Bamford CR (1977) Colour generation and control in glass. Glass Science& Technology 2. Elsevier Publishers, AmsterdamGoogle Scholar
- 8.Wong J, Angell CA (1976) Glass structure by spectroscopy. Marcel Dekker, New YorkGoogle Scholar
- 9.Paul A (1990) Chemistry of glasses, 2nd edn. Elsevier, New YorkGoogle Scholar
- 10.Friebele EJ (1991) In: Uhlmann D R, Kreidl N J (eds) Optical properties of glass. American Ceramic Society, Westerville, pp 205–262Google Scholar
- 13.ElBatal FH, ElBatal HA, Hammad AH (2017) Silicon. https://doi.org/10.1007/s12633-016-95372, in press
- 14.Sigel G H Jr, Ginther RG (1968) The effect of iron on the ultraviolet absorption of high purity soda- silica glass. Glass Technol 9:66Google Scholar
- 15.Sigel G H Jr (1977) Optical absorption of glasses. In: M Tomozawa, RH Doremus (eds) Treatise in materials science and technology, vol 12. Academic Press, San Diego, pp 5–89Google Scholar
- 18.Moncke D, Ehrt D (2007) Photoionization of polyvalent ions. In: Glick HP (ed) Materials science research horizons. Nova Science Publishers, Inc., New York, pp 1–56Google Scholar
- 24.Peng YB, Day DE (1991) High thermal expansion phosphate glasses. Part 1. Glass Technol 5:166–173Google Scholar
- 25.Tarte P (1972) In: Physics of non-crystalline solids. Crystalline Solids. Elsevier, Amsterdam, p 504Google Scholar
- 26.Condrate R (1972) In: Introduction to Glass Science, p 101. Plenum Press, New YorkGoogle Scholar